Microstructures and mechanical properties of C-Mn-Cr-Nb and C-Mn-Si-Nb ultra-high strength dual-phase steels

The microstructures and mechanical properties of C-Mn-Cr-Nb and C-Mn-Si-Nb ultra-high strength dual-phase steels were studied by scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, and tensile test. The results show that Si can promote the transformation of austenite （γ） to ferrite （α）, enlarge the （α＋γ） region, and increase the aging stability of martensite by inhibiting carbide precipitation. Adding Cr leads to the formation of retained austenite and martensite/austenite （M/A） constituents, as well as the decomposi- tion of martensite during the overaging stage. Both of the steels show higher initial strain-hardening rates and two-stage strain-hardening characteristics. The C-Mn-Si-Nb steel shows the higher strain-hardening rate than the C-Mn-Cr-Nb steel in the first stage; however, there is no significant difference in the second stage. Although the tensile strength and elongation of the two steels both exceed 1000 MPa and 15%, respectively, the comprehensive mechanical properties of the C-Mn-Si-Nb steel are superior.

Effect of intercritical annealing on microstructure,mechanical properties,and work-hardening behavior of ultrahigh-strength dual-phase steels with different silicon contents

In this study,three kinds of dual-phase(DP) steels were used to investigate the influence of silicon content and intercritical annealing temperature on their microstructures,mechanical properties,and work-hardening behaviors. By adding silicon and matching the critical annealing temperature,a new DP steel(1.0Si and intercritically annealed at 790 ℃) that exhibits an excellent combination of ultrahigh strength and adequate ductility was obtained. Variations in the strength,elongation,and fracture mechanism of the specimens with respect to different intercritical annealing temperatures were correlated to microstructural features. With an increase in the silicon content,there is no significant change in the martensitic band structure or ferrite morphology. At the same annealing temperature,the yield strength and yield strength ratio of the specimens decreased,but at different annealing temperatures,the tensile strength was reduced. The Hollomon analysis results indicate that the workhardening behavior obeys a two-stage work-hardening mechanism. With an increasing intercritical annealing temperature,the "transition strain"shifts to the left,and with an increasing silicon content,the "transition strain"shifts to the right. The surface exhibits ductile fractures characterized by a high density of microvoid dimples. With an increase in the silicon content,the average dimple size on the fracture surface decreases and the plasticity of the material increases.

CHARACTERISTICS OF MARTENSITIC TRANSFORMATION IN DUAL-PHASE STEELS

A theorectical expression for the driving force and M_(?) point of martensitic transformation has been proposed.The M_(?) values using this expression are in good agreement with that obtained experimentally.It was found that the values of M_(?) and M_(?) are not only related to the carbon content in martensite,but also to the volume fraction of ferrite.

MICROFRACTOGRAPHY OF NEAR-THRESHOLD FATIGUE CRACK PROPAGATION IN DUAL-PHASE STEELS

SEM microfractography of near-threshold fatigue crack propagation were carried out in the dual-phase steels of 3 martensite morphologies and 6 volume fractions of martensite (V_m). All of them are featured by cyclic cleavage characteristics in near-threshold region,i.e.,main- ly controlled by mode Ⅱ stress.In the higher ΔK regions,the fracture surfaces are character- ized by mixed modes including cyclic cleavage facets,two types of secondary cracks and striations,etc..The roughness-induced crack closure of fracture surface is attributed primarily to extreme high fatigue crack growth threshold values.

Improving fatigue strength of bainite/martensite dual-phase steels in very high cycle fatigue regime by refining microstructures

Very high cycle fatigue behaviors of two bainite/martensite dual-phase steels were investigated.One of the steels was cyclic rapid heat treated and its microstructures were refined. Fatigue strength of the steel is 225 MPa higher than that without refining.Observation of fracture surfaces show that the fatigue cracks initiate at bainites for non-refined steel and at non-metallic inclusions for the refined steel.The size of inclusions is much smaller than that of bainites which results in the improvement of fatigue strength.

Experimental study on the forming characteristics of 1.5 GPa ultrahigh-strength dual-phase steel

The DP1500 steel series successfully produced by Baosteel is a marked improvement over the cold-rolled hot-dip galvanized dual-phase steel series.Sufficient parameter data related to forming characteristics are needed for the successful application of dual-phase steel series in engineering structures.Therefore,differences in the mech-anical properties,forming limit,hole expansion ratio,and stretch bend limit of the 1.5 GPa ultrahigh-strength steel,including DP1500,QP1500,and MS1500,have been systematically studied.Results show that the DP1500 exhibits good plastic deformation performance and approximately 5% uniform elongation,and its true major strain minimum on the forming limit curve(FLC_(0)) value is approximately 0.083,which is higher and lower than the FLC_(0) values of MS1500 and QP1500 of the same strength grade,respectively.DP1500 also exhibits good flanging and pore expansion capabilities and superior performance to QP1500 and MS1500.The minimum radius-to-thickness(R/T) ratio(1.4) of DP1500 in the 90° bend tests transverse to the rolling direction is between the R/T ratios of MS1500 and the QP1500.Overall,the formability performance of DP1500 is between that of MS1500 and QP1500.Its excellent crash energy absorption and formability performance render it a suitable structural component,and it has been successfully tested and verified on a typical complex ultrahigh-strength steel skeleton structure.

Characterization of the Trace Phosphorus Segregation and Mechanical Properties of Dual-Phase Steels

The segregation behavior of trace amount of phosphorus(P)and the mechanical properties of dual-phase(DP)steels have been systematically studied.The microstructure of DP steels is mainly composed of martensite,ferrite and nanoscale carbides.For the DP steels with diff erent trace amounts of P(≤0.015 wt%),P has almost no effect on the mechanical properties.Atom probe technology(APT)analyses confirm that P segregation was only found at the precipitate/matrix interface.Moreover,the precipitates of(Ti,Mo)C are widely distributed in the ferrite,martensite and ferrite/martensite interface regions.The special segregation feature of P would not concentrate at specific regions such as ferrite/martensite interface and/or martensite lath interface,which reveals that trace amounts of P(≤0.015 wt%)have almost no effect on the mechanical properties of DP steels.It is proved for the first time that the MC-type carbides of(Ti,Mo)C can reduce or eliminate the damage effect of P on the mechanical properties of steels,which provides a new way for the design of alloys to reduce P damage.This work will promote to increase the P content control standard in DP steels from 0.01 to 0.015 wt%,which will not change the mechanical properties,but greatly reduce the scrap rate and increase the energy e fficiency of the manufacturing process.

Prediction model for corrosion rate of low-alloy steels under atmospheric conditions using machine learning algorithms

This work constructed a machine learning(ML)model to predict the atmospheric corrosion rate of low-alloy steels(LAS).The material properties of LAS,environmental factors,and exposure time were used as the input,while the corrosion rate as the output.6 dif-ferent ML algorithms were used to construct the proposed model.Through optimization and filtering,the eXtreme gradient boosting(XG-Boost)model exhibited good corrosion rate prediction accuracy.The features of material properties were then transformed into atomic and physical features using the proposed property transformation approach,and the dominant descriptors that affected the corrosion rate were filtered using the recursive feature elimination(RFE)as well as XGBoost methods.The established ML models exhibited better predic-tion performance and generalization ability via property transformation descriptors.In addition,the SHapley additive exPlanations(SHAP)method was applied to analyze the relationship between the descriptors and corrosion rate.The results showed that the property transformation model could effectively help with analyzing the corrosion behavior,thereby significantly improving the generalization ability of corrosion rate prediction models.

Formability Investigations of High-Strength Dual-Phase Steels

Car manufacturing is always regarded as the key industry behind sheet metal forming, and thus, the requirements of and developments in car manufacturing play a decisive role in the development of sheet metal forming. The automotive industry is faced with contradictory demands and requirements： better performance with lower consumption and less harmful emissions, more safety and comfort; these are extremely difficult to supply simultaneously with conventional materials and conventional manufacturing processes. The fulfillment of these often contradictory requirements is one of the main driving forces in the automotive industry and thus in the material and process developments in sheet metal forming, as well. In recent years, significant developments can be observed in the application of high-strength steels. In this respect, the application of various dual-phase steels is one of the best examples. However, the application of these highstrength steels often leads to formability and manufacturing problems. One formability problem is the springback occurring after sheet metal forming. In the current research, we have dealt mainly with advanced high-strength steels, primarily with dual-phase steels. When applying them, the springback phenomenon is one of the most critical issues. To reduce the tremendous amount of experimental work needed, we also applied numerical simulation using isotropic–kinematic hardening rules. The isotropic–kinematic hardening behavior of a given material in the applied Auto Form numerical package may be characterized with three independent material parameters c, v and K（a detailed explanation of their meaning will be given in the main part of this paper）. However, we found that the material data included in simulation packages for these new high-strength steels are not fully adequate. For the determination of more reliable material parameters and to achieve better simulation results, a new testing device was developed. Numerical simulations were performed using the material parameters determined by the new device to show the sensitivity of springback behavior to these material parameters.

Effect of temperature and time on the precipitation ofκ-carbides in Fe-28Mn-10Al-0.8C low-density steels:Aging mechanism and its impact on material properties

In low-density steel,κ-carbides primarily precipitate in the form of nanoscale particles within austenite grains.However,their precipitation within ferrite matrix grains has not been comprehensively explored,and the second-phase evolution mechanism during aging remains unclear.In this study,the crystallographic characteristics and morphological evolution ofκ-carbides in Fe-28Mn-10Al-0.8C(wt%)low-density steel at different aging temperatures and times and the impacts of these changes on the steels’microhardness and properties were comprehensively analyzed.Under different heat treatment conditions,intragranularκ-carbides exhibited various morpho-logical and crystallographic characteristics,such as acicular,spherical,and short rod-like shapes.At the initial stage of aging,acicularκ-carbides primarily precipitated,accompanied by a few spherical carbides.κ-Carbides grew and coarsened with aging time,the spherical carbides were considerably reduced,and rod-like carbides coarsened.Vickers hardness testing demonstrated that the material’s hardness was affected by the volume fraction,morphology,and size ofκ-carbides.Extended aging at higher temperatures led to an increase in carbide size and volume fraction,resulting in a gradual rise in hardness.During deformation,the primary mechanisms for strengthening were dislocation strengthening and second-phase strengthening.Based on these findings,potential strategies for improving material strength are proposed.

Critical precipitation behavior of MnTe inclusions in resulfurized steels during solidification

Te treatment is an effective method for modifying sulfide inclusions,and MnTe precipitation has an important effect on thermal brittleness and steel corrosion resistance.In most actual industrial applications of Te treatment,MnTe precipitation is unexpected.The critical precipitation behavior of MnTe inclusions was investigated through scanning electron microscopy,transmission electron microscopy,machine learning,and first-principles calculation.MnTe preferentially precipitated at the container mouth for sphere-like sulfides and at the interface between MnS grain boundaries and steel matrix for rod-like sulfides.The MnS/MnTe interface was semicoherent.A composition transition zone with a rock-salt structure exhibiting periodic changes existed to maintain the semicoherent interface.The critical precipitation behavior of MnTe inclusions in resulfurized steels involved three stages at varying temperatures.First,Mn(S,Te)precipitated during solidification.Second,MnTe with a rock-salt structure precipitated from Mn(S,Te).Third,MnTe with a hexagonal NiAs structure transformed from the rock-salt structure.The solubility of Te in MnS decreased with decreasing temperature.The critical precipitation behavior of MnTe inclusions in resulfurized steels was related to the MnS precipitation temperature.With the increase in MnS precipitation temperature,the critical Te/S weight ratio decreased.In consideration of the cost-effectiveness of Te addition for industrial production,the Te content in resulfurized steels should be controlled in accordance with MnS precipitation temperature and S content.

Electromagnetic responses on microstructures of duplex stainless steels based on 3D cellular and electromagnetic sensor finite element models

Microstructures determine mechanical properties of steels,but in actual steel product process it is difficult to accurately control the microstructure to meet the requirements.General microstructure characterization methods are time consuming and results are not rep-resentative for overall quality level as only a fraction of steel sample was selected to be examined.In this paper,a macro and micro coupled 3D model was developed for nondestructively characterization of steel microstructures.For electromagnetic signals analysis,the relative permeability value computed by the micro cellular model can be used in the macro electromagnetic sensor model.The effects of different microstructure components on the relative permeability of duplex stainless steel(grain size,phase fraction,and phase distribu-tion)were discussed.The output inductance of an electromagnetic sensor was determined by relative permeability values and can be val-idated experimentally.The findings indicate that the inductance value of an electromagnetic sensor at low frequency can distinguish dif-ferent microstructures.This method can be applied to real-time on-line characterize steel microstructures in process of steel rolling.

Review on the plastic instability of medium -Mn steels for identifying the formation mechanisms of Lüders and Portevin -Le Chatelier bands

Plastic instability,including both the discontinuous yielding and stress serrations,has been frequently observed during the tensile deformation of medium-Mn steels(MMnS)and has been intensively studied in recent years.Unfortunately,research results are controversial,and no consensus has been achieved regarding the topic.Here,we first summarize all the possible factors that affect the yielding and flow stress serrations in MMnS,including the morphology and stability of austenite,the feature of the phase interface,and the deformation parameters.Then,we propose a universal mechanism to explain the conflicting experimental results.We conclude that the discontinuous yielding can be attributed to the lack of mobile dislocation before deformation and the rapid dislocation multiplication at the beginning of plastic deformation.Meanwhile,the results show that the stress serrations are formed due to the pinning and depinning between dislocations and interstitial atoms in austenite.Strain-induced martensitic transformation,influenced by the mechanical stability of austenite grain and deformation parameters,should not be the intrinsic cause of plastic instability.However,it can intensify or weaken the discontinuous yielding and the stress serrations by affecting the mobility and density of dislocations,as well as the interaction between the interstitial atoms and dislocations in austenite grains.

Interplay between temperature-dependent strengthening mechanisms and mechanical stability in high-performance austenitic stainless steels

The effects of deformation temperature on the transformation-induced plasticity(TRIP)-aided 304L,twinning-induced plasti-city(TWIP)-assisted 316L,and highly alloyed stable 904L austenitic stainless steels were compared for the first time to tune the mechan-ical properties,strengthening mechanisms,and strength-ductility synergy.For this purpose,the scanning electron microscopy(SEM),electron backscattered diffraction(EBSD),X-ray diffraction(XRD),tensile testing,work-hardening analysis,and thermodynamics calcu-lations were used.The induced plasticity effects led to a high temperature-dependency of work-hardening behavior in the 304L and 316L stainless steels.As the deformation temperature increased,the metastable 304L stainless steel showed the sequence of TRIP,TWIP,and weakening of the induced plasticity mechanism;while the disappearance of the TWIP effect in the 316L stainless steel was also observed.However,the solid-solution strengthening in the 904L superaustenitic stainless steel maintained the tensile properties over a wide temper-ature range,surpassing the performance of 304L and 316L stainless steels.In this regard,the dependency of the total elongation on the de-formation temperature was less pronounced for the 904L alloy due to the absence of additional plasticity mechanisms.These results re-vealed the importance of solid-solution strengthening and the associated high friction stress for superior mechanical behavior over a wide temperature range.

A review on the multi-scaled structures and mechanical/thermal properties of tool steels fabricated by laser powder bed fusion additive manufacturing

The laser powder bed fusion(LPBF) process can integrally form geometrically complex and high-performance metallic parts that have attracted much interest,especially in the molds industry.The appearance of the LPBF makes it possible to design and produce complex conformal cooling channel systems in molds.Thus,LPBF-processed tool steels have attracted more and more attention.The complex thermal history in the LPBF process makes the microstructural characteristics and properties different from those of conventional manufactured tool steels.This paper provides an overview of LPBF-processed tool steels by describing the physical phenomena,the microstructural characteristics,and the mechanical/thermal properties,including tensile properties,wear resistance,and thermal properties.The microstructural characteristics are presented through a multiscale perspective,ranging from densification,meso-structure,microstructure,substructure in grains,to nanoprecipitates.Finally,a summary of tool steels and their challenges and outlooks are introduced.

Progress in weldability research of duplex stainless steels

Duplex stainless steels(DSSs)show better corrosion resistance with higher strength than traditional austenite stainless steels in many aggressive environments,and can be welded properly with almost every welding processes,if proper heat input is provided.Progresses of research works on weldability of DSSs in recent years are reviewed in this paper.Balance control of ferrite/austenite phases is most important for DSSs welding.The phases balance can be controlled with filler materials,nitrogen addition in shielding gas,heat input,post weld heat treatment,and alternating magnetic field.Too high cooling rate results in not only extra ferrite,but also chromium nitride precipitation.While too low cooling rate or heating repeatedly results in precipitation of secondary austenite and intermetallic compounds.In both situations,mechanical properties and corrosion resistance of the DSS joints deteriorate.Recommended upper and lower limits of heat input and maximum interpass temperature should be observed.

Development of a new irradiation-embrittlement prediction model for reactor pressure-vessel steels

Predicting the transition-temperature shift(TTS)induced by neutron irradiation in reactor pressure-vessel(RPV)steels is important for the evaluation and extension of nuclear power-plant lifetimes.Current prediction models may fail to properly describe the embrittlement trend curves of Chinese domestic RPV steels with relatively low Cu content.Based on the screened surveillance data of Chinese domestic and similar international RPV steels,we have developed a new fluencedependent model for predicting the irradiation-embrittlement trend.The fast neutron fluence(E>1 MeV)exhibited the highest correlation coefficient with the measured TTS data;thus,it is a crucial parameter in the prediction model.The chemical composition has little relevance to the TTS residual calculated by the fluence-dependent model.The results show that the newly developed model with a simple power-law functional form of the neutron fluence is suitable for predicting the irradiation-embrittlement trend of Chinese domestic RPVs,regardless of the effect of the chemical composition.

A Physical Core-Loss Model for Laminated Magnetic Sheet Steels

A full-frequency instant core-loss equation built from the induction physical model of magnetic materials, where the iron loss, eddy loss, and hysteresis loss no longer have an integral term, and this new equation provides high simulation accuracy and performs dynamic core loss analysis on non-sinusoidal or pulse magnetic fields. The simulation examples use a high-grade electrical steel sheet 65CS400 by Epstein experimental data covering magnetic field 0.1 - 1.8 T and frequency 50 - 5000 Hz, and the average error of the simulated core loss is less than 4%. Since the simulation is converged by magnetic physical parameters, so the physical relevance of the similar laminated materials can be compared with the coefficient results. .

Effect of Ni content on the weldability of middle-chromium hyperpure ferritic stainless steels 00Cr21Ti

Excellent weldability substantially contributes to the intrinsic quality of steels,while appropriate chemical composition plays a primary role in the essential weldability of steels.The poor weldability of ferritic stainless steels could be improved through modification with minor alloy elements while minimally increasing the cost.Therefore,studying the effect of minor alloy elements on the weldability of steels is of considerable importance.In this study,several steels of middle-chromium hyperpure ferritic stainless 00Cr21Ti with different Ni content(0.3%,0.5%,0.8%,and 1.0%)were developed,and their weldabilities of butt joint samples welded using the metal inert gas welding process,including the influence of welded joints on the microstructure,tensile performance,corrosion resistance,and fatigue property,were investigated.Results show that the steels with w(Ni)≥0.8%exhibit excellent mechanical properties compared with those with low-Ni content steels,further,their impact toughness at normal atmospheric temperature meets the industrial application standard and the fatigue property is similar to that of 304 austenitic stainless steel.Moreover,results show that the corrosion resistance of all the samples is almost at the same level.The results acquired in this study are supposed to be useful for the optimization of the chemical composition of stainless steels aiming to improve weldability.

Precipitation Behavior and Textural Evolution of Cold-Rolled High Strength Deep Drawing Dual-Phase Steels

Low-carbon Cr-Mo micro-alloyed deep drawing dual-phase steels were designed in laboratory. As the mi- crostructure and texture evolution in hot-rolled strips and annealed sheets were investigated using SEM, TEM and XRD technologies, the attribution of solute Mo and MoC particles to DP sheets＇ drawing capacity was investigated. The precipitation thermodynamics were also calculated by Thermo-calc software. Results show that the precipitates in hot-rolled strips mainly are MoC, AIN and MnS, and with the increase of Mo addition, finer and denser MoC par- ticles precipitated in matrix and along grain boundaries of ferrite more easily. Weak textures are shown in the hot- rolled strips, and {112}~110~ and {223}%110~ components tend to be stable in subsequent cold rolling process. During annealing, on one hand, the development of ~lll~//ND texture is suppressed because finer MoC particles prevent the grain boundary migration. On the other hand, unfavorable texture {001 } %110：〉 significantly reduces with Mo increasing, which is attributed to that part of solution C in matrix has been fixed during recrystallization. In addition, the addition of Mo can enhance hardenability strongly and MoC easily re-dissolve at high temperature, which is favor to form martensite in dual-phase steel.