Corrosion behavior and corrosion products of a low-alloy weathering steel in Qingdao and Wanning

A newly developed low-alloy weathering steel has been exposed in two coastal sites （Qingdao in the north, Wanning in the south） in China for one year. The samples in Wanning corroded far more seriously than those in Qingdao. The rust layer formed on the steel was analyzed by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, N2 adsorption approach, polarization curves, and electrochemical impedance spectroscopy （EIS）. The rust formed in Qingdao contains more X-ray amorphous compounds and is more compact than that formed in Wanning. Cr and Cu are enriched in the rust layer near the steel matrix, and the phenomenon is more obvious in Qingdao than in Wanning. The rust layer formed in Qingdao suppresses the anodic and cathodic reaction more remarkably than that formed in Wanning does. The rust layer formed in Qingdao possesses a higher ability to block the permeation of chloride ions than that formed in Wanning does.

Microstructures and mechanical properties of C-Mn-Cr-Nb and C-Mn-Si-Nb ultra-high strength dual-phase steels

The microstructures and mechanical properties of C-Mn-Cr-Nb and C-Mn-Si-Nb ultra-high strength dual-phase steels were studied by scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, and tensile test. The results show that Si can promote the transformation of austenite （γ） to ferrite （α）, enlarge the （α＋γ） region, and increase the aging stability of martensite by inhibiting carbide precipitation. Adding Cr leads to the formation of retained austenite and martensite/austenite （M/A） constituents, as well as the decomposi- tion of martensite during the overaging stage. Both of the steels show higher initial strain-hardening rates and two-stage strain-hardening characteristics. The C-Mn-Si-Nb steel shows the higher strain-hardening rate than the C-Mn-Cr-Nb steel in the first stage; however, there is no significant difference in the second stage. Although the tensile strength and elongation of the two steels both exceed 1000 MPa and 15%, respectively, the comprehensive mechanical properties of the C-Mn-Si-Nb steel are superior.

Numerical simulation on the microstress and microstrain of low Si-Mn-Nb dual-phase steel

According to the stress-strain curves of single-phase martensite and single-phase ferrite steels,whose compositions are similar to those of martensite and ferrite in low Si-Mn-Nb dual-phase steel,the stress-strain curve of the low Si-Mn-Nb dual-phase steel was simulated using the finite element method（FEM）.The simulated result was compared with the measured one and they fit closely with each other, which proves that the FE model is correct.Based on the FE model,the microstress and microstrain of the dual-phase steel were analyzed. Meanwhile,the effective factors such as the volume fraction of martensite and the yield stress ratio between martensite and ferrite phases on the stress-strain curves of the dual-phase steel were simulated,too.The simulated results indicate that for the low Si-Mn-Nb dual-phase steel, the maximum stress occurs in the martensite region,while the maximum strain occurs in the ferrite one.The effect of the volume fraction of martensite（fm） and the yield stress ratio on the stress-strain curve of the dual-phase steel is small in the elastic part,while it is obvious in the plastic part.In the plastic part of this curve,the strain decreases with the increase of f_M,while it decreases with the decrease of the yield stress ratio.

Effect of hot-dip galvanizing processes on the microstructure and mechanical properties of 600-MPa hot-dip galvanized dual-phase steel

A C–Mn dual-phase steel was soaked at 800°C for 90 s and then either rapidly cooled to 450°C and held for 30 s(process A) or rapidly cooled to 350°C and then reheated to 450°C(process B) to simulate the hot-dip galvanizing process. The influence of the hot-dip galvanizing process on the microstructure and mechanical properties of 600-MPa hot-dip galvanized dual-phase steel(DP600) was investigated using optical microscopy, scanning electron microscopy(SEM), transmission electron microscopy(TEM), and tensile tests. The results showed that, in the case of process A, the microstructure of DP600 was composed of ferrite, martensite, and a small amount of bainite. The granular bainite was formed in the hot-dip galvanizing stage, and martensite islands were formed in the final cooling stage after hot-dip galvanizing. By contrast, in the case of process B, the microstructure of the DP600 was composed of ferrite, martensite, bainite, and cementite. In addition, compared with the yield strength(YS) of the DP600 annealed by process A, that for the DP600 annealed by process B increased by approximately 50 MPa because of the tempering of the martensite formed during rapid cooling. The work-hardening coefficient(n value) of the DP600 steel annealed by process B clearly decreased because the increase of the YS affected the computation result for the n value. However, the ultimate tensile strength(UTS) and elongation(A80) of the DP600 annealed by process B exhibited less variation compared with those of the DP600 annealed by process A. Therefore, DP600 with excellent comprehensive mechanical properties(YS = 362 MPa, UTS = 638 MPa, A_(80) = 24.3%, n = 0.17) was obtained via process A.

Effects of pre-strain and baking parameters on the microstructure and bake-hardening behavior of dual-phase steel

In a typical process, C-Mn steel was annealed at 800℃ for 180 s, and then cooled rapidly to obtain the ferrite-martensite microstructure. After pre-straining, the specimens were baked and the corresponding bake-hardening （BH） values were determined as a function of pre-strain, baking temperature, and baking time. The influences ofpre-strain, baking temperature and baking time on the microstructure evolution and bake-hardening behavior of the dual-phase steel were investigated systematically. It was found that the BH value apparently increased with an increase in pre-strain in the range from 0 to 1%; however, increasing pre-strain from 1% to 8% led to a decrease in the BH value. Furthermore, an increase in baking temperature favored a gradual improvement in the BH value because of the formation of Cottrell atmosphere and the precipitation of carbides in both the ferrite and martensite phases. The BH value reached a maximum of 110 MPa at a baking temperature of 300℃. Moreover, the BH value enhanced significantly with increasing baking time from 10 to 100 min.

Stress-assisted corrosion mechanism of 3Ni steel by using gradient boosting decision tree machining learning method

Traditional 3Ni weathering steel cannot completely meet the requirements for offshore engineering development,resulting in the design of novel 3Ni steel with the addition of microalloy elements such as Mn or Nb for strength enhancement becoming a trend.The stress-assisted corrosion behavior of a novel designed high-strength 3Ni steel was investigated in the current study using the corrosion big data method.The information on the corrosion process was recorded using the galvanic corrosion current monitoring method.The gradi-ent boosting decision tree(GBDT)machine learning method was used to mine the corrosion mechanism,and the importance of the struc-ture factor was investigated.Field exposure tests were conducted to verify the calculated results using the GBDT method.Results indic-ated that the GBDT method can be effectively used to study the influence of structural factors on the corrosion process of 3Ni steel.Dif-ferent mechanisms for the addition of Mn and Cu to the stress-assisted corrosion of 3Ni steel suggested that Mn and Cu have no obvious effect on the corrosion rate of non-stressed 3Ni steel during the early stage of corrosion.When the corrosion reached a stable state,the in-crease in Mn element content increased the corrosion rate of 3Ni steel,while Cu reduced this rate.In the presence of stress,the increase in Mn element content and Cu addition can inhibit the corrosion process.The corrosion law of outdoor-exposed 3Ni steel is consistent with the law based on corrosion big data technology,verifying the reliability of the big data evaluation method and data prediction model selection.

Effect of Holding Time on the Microstructure and Mechanical Properties of Dual-Phase Steel during Intercritical Annealing

Continuous annealing simulation tests were conducted by using a continuous annealing thermomechanical simulator. Holding times of 5, 60, 180, and 480 seconds for an intercritical annealing temperature of 820℃ were adopted to investigate the evolution of the mierostructure and mechanical properties of ferrite-bainite dual-phase steel. The ferrite-bainite dual-phase steel was characterized by high strength and low yield ratio due to the presence of the constituents （polygonal ferrite, bainite, martensite and retained austenite） of the steel microstructure. Specimen 3 exhibits the highest value of A50 （7.67%） and a product of Rm × A50 （10453MPa%） after a 180s holding. This is likely attributed to the presence of a C-enriched retained anstenite in the microstructure. And the effect of martensite islands and carbide precipitate is thought to be able to contribute in strengthening the present steel. It is expected that equilibrium of anstenite fraction would be reached for reasonable intercritical holding period, regardless of the heating temperature. The results suggest that long increasing holding times may not be needed because the major phase of the microstructure does not change very significantly. It is favorable for industrial production of DP steels to shorten holding times. Key words： ferrite-bainite dual-phase steel; holding time; martensite islands; mechanical properties

Corrosion behavior of tempered dual-phase steel embedded in concrete

Dual-phase （DP） steels with different martensite contents were obtained by appropriate heat treatment of an SAE1010 structural carbon steel, which was cheap and widely used in the construction industry. The corrosion behavior of DP steels in concrete was investigated under various tempering conditions. Intercritical annealing heat treatment was applied to the reinforcing steel to obtain DP steels with different contents of martensite. These DP steels were tempered at 200, 300, and 400℃ for 45 min and then cooled to room temperature. Corrosion experiments were conducted in two stages. In the first stage, the corrosion potential of DP steels embedded in concrete was measured every day for a period of 30 d based on the ASTM C 876 standard. In the second stage, the anodic and cathodic polarization values of these steels were obtained and subsequently the corrosion currents were determined with the aid of cathodic polarization curves. It was observed that the amount of second phase had a definite effect on the corrosion behavior of the DP steel embedded in concrete. As a result of this study, it is found that the corrosion rate of the DP steel increases with an increase in the amount of martensite.

Effect of intercritical annealing on microstructure,mechanical properties,and work-hardening behavior of ultrahigh-strength dual-phase steels with different silicon contents

In this study,three kinds of dual-phase(DP) steels were used to investigate the influence of silicon content and intercritical annealing temperature on their microstructures,mechanical properties,and work-hardening behaviors. By adding silicon and matching the critical annealing temperature,a new DP steel(1.0Si and intercritically annealed at 790 ℃) that exhibits an excellent combination of ultrahigh strength and adequate ductility was obtained. Variations in the strength,elongation,and fracture mechanism of the specimens with respect to different intercritical annealing temperatures were correlated to microstructural features. With an increase in the silicon content,there is no significant change in the martensitic band structure or ferrite morphology. At the same annealing temperature,the yield strength and yield strength ratio of the specimens decreased,but at different annealing temperatures,the tensile strength was reduced. The Hollomon analysis results indicate that the workhardening behavior obeys a two-stage work-hardening mechanism. With an increasing intercritical annealing temperature,the "transition strain"shifts to the left,and with an increasing silicon content,the "transition strain"shifts to the right. The surface exhibits ductile fractures characterized by a high density of microvoid dimples. With an increase in the silicon content,the average dimple size on the fracture surface decreases and the plasticity of the material increases.

Some Advances in the Application of Weathering and Cold-Formed Steel in Transmission Tower

Application of weathering and cold-formed steel in transmission lines can reduce steel consumption and environmental pollution. Some advances in the studies on the weathering and cold-formed steel in transmission tower are introduced. Firstly, corrosion-resistant tests of weathering steel samples under different simulating technical atmospheres were carried out separately for 240 hours. It shows that the corrosion degree of joint samples is higher than that of single chip samples, and the corrosion-resistant performance of weathering steel is superior to common carbon steel. The corrosion-resistance of weathering steel meets with the requirement of transmission tower. Secondly, experiments and finite element analysis for cold-formed angles and a 220kV prototype tower were completed, and the stability coeffi-cient fitting curves as well as the modification formulas of slenderness ratio for cold-formed members were determined. According to the structural characteristics of transmission towers, four sections of cold-formed angles with different sections and slenderness ratios were selected in this study. The finite element model well predicted the buckling behav-iour of the cold-formed members. Ultimate loads calculating by the fitting curve were well agreed to the experimental values, especially for the members with small slenderness ratios. Weight of the cold-formed steel tower can be reduced by more than 5 percent after considering the strength enhancement. Cost of the weathering and cold-formed steel transmission tower is nearly equivalent to that of hot-rolled steel tower with hot galvanizing.

CORROSION BEHAVIORS OF THE EXPOSED SIDE AND UNDERSIDE OF LOW ALLOY WEATHERING STEEL IN QINGDAO AND WANNING FOR 18 MONTHS

For 18 months, a newly developed low alloy weathering steel has been exposed in two coastal sites （Qingdao in the north China, Wanning in the south China）. The different corrosion behaviors of the exposed side and the underside of the samples were characterized by X-ray diffraetion （XRD）, polarization curve, electrochemical impedance spectroscopy （EIS）, scanning electron microscopy （SEM）, and N2 adsorption approach. It was found that the samples exhibited higher corrosion rate in Wanning than that in Qingdao. The underside of the samples corrodes more seriously than the exposed side in Qingdao, whereas the result in Wanning is just the reverse. The protection performance of rust layers mainly depends on its compactness and the enrichment of Cu and Cr is a secondary causation. The different compactness of rust layers in the exposed side and the underside originates from different corrosion conditions of the two sides.

Industrial trial of strip-casting weathering steel

Baostrip has chosen a steel-grade weathering steel for industrial trial. By carefully designing the composition and manufacturing process,qualified weathering-steel products have been successfully produced on the Ningbosteel-Baosteel strip casting industrialization demo project( NBS) production line. The industrialized practice of Baostrip shows the following: The surface microstructure of weathering-steel products is polygonal ferrite +pearlite,and that of the center is acicular ferrite. After single-stand on-line hot rolling at a 26% low pressure rate,the thickness tolerance ratio controlled within ± 25 μm reaches 99. 6%. The surface convexity and the wedge can be controlled to | C40 |< 50 μm and | W40 |< 30 μm,respectively. The mechanical properties of the strip are superior,exhibiting a yield strength range of( 430 ± 50) MPa,a tensile strength range of( 550 ± 50) MPa,and an elongation range of( 27 ± 5)%. The corrosion resistance is equivalent to that of current commercial atmospheric corrosion-resistant steels,with a relative corrosion rate of 43%. When used,the weathering steel produced by the strip-casting process meets the strict quality and usage requirements of container steel sheets.

Characteristics of Corrosion Product Layer Formed on Weathering Steel Exposed to the Tropical Climate of Vietnam

The weathering steel (Corten B) was exposed to out-door atmosphere of Hanoi (urban site) and Donghoi (marine site). The results showed the protective ability of corrosion product layer formed on weathering steel in the initial stage. The SEM-EDX analysis detected the presence of chromium and copper in the inner layers of corrosion product formed on weathering steel. These elements improved corrosion resistance of corrosion product layers. In addition, the dense α-FeOOH phase were appeared early in corrosion product which is detected by X-ray diffraction and Micro Raman investigations. The results of polarization and EIS measurements also demonstrated the protectiveness of the corrosion product of weathering steel.

Effects of overaging temperature on the microstructure and properties of 600MPa cold-rolled dual-phase steel

C–Mn steels prepared by annealing at 800°C for 120 s and overaging at 250–400°C were subjected to pre-straining（2%） and baking treatments（170°C for 20 min） to measure their bake-hardening（BH_2） values. The effects of overaging temperature on the microstructure, mechanical properties, and BH_2 behavior of 600 MPa cold-rolled dual-phase（DP） steel were investigated by optical microscopy, scanning electron microscopy, and tensile tests. The results indicated that the martensite morphology exhibited less variation when the DP steel was overaged at 250–350°C. However, when the DP steel was overaged at 400°C, numerous non-martensite and carbide particles formed and yield-point elongation was observed in the tensile curve. When the overaging temperature was increased from 250 to 400°C, the yield strength increased from 272 to 317 MPa, the tensile strength decreased from 643 to 574 MPa, and the elongation increased from 27.8% to 30.6%. Furthermore, with an increase in overaging temperature from 250 to 400°C, the BH_2 value initially increases and then decreases. The maximum BH_2 value of 83 MPa was observed for the specimen overaged at 350°C.

Plastic Deformation Mechanism of Dual-phase Steel at Different Strain Rates

The mechanical properties of dual-phase steel (DP1000) over the strain rate range of 10^-3-10^3 s^-1 were studied using an electronic universal testing machine and a high-speed tensile testing machine.The plastic deformation mechanism was investigated from the perspectives of the strain rate sensitivity index,activation volume and dynamic factors.The results show that the tensile strength and yield strength of DP1000 increase as the strain rate increases.The elongation increases without any change after fracture,and then decreased rapidly when the strain rate reaches 103 s^-1.The true strain curves of DP1000 show three stages:the point of instability decreases in the strain range of 10^-3-10^-1 s^-1;the instability point increases between 100-5×10^2 s^-1;above 5×10^2 s^-1,and the instability strain becomes smaller again.The plastic deformation mechanism of the DP was determined by the competitive contributions of work hardening (strain hardening,strain rate hardening) and softening effects due to the adiabatic temperature rise.

Microstructure evolution and mechanical properties of 1000 MPa cold rolled dual-phase steel

The microstructure evolution of 1 000 MPa cold rolled dual-phase (DP) steel at the initial heating stages of the continuous annealing process was analyzed. The effects of different overaging temperatures on the microstructures and mechanical properties of 1 000 MPa cold rolled DP steel were investigated using a Gleeble-3500 thermal/mechanical simulator. The experimental results show that ferrite recovery and recrystallization, pearlite dissolution and austenite nucleation and growth take place in the annealing process of ultra-high strength cold rolled DP steel. When being annealed at 800 ℃ for 80 s, the tensile strength and total elongation of DP steel can reach 1 150 MPa and 13%, respectively. The microstructure of DP steel mainly consists of a mixture of ferrite and martensite. The steel exhibits low yield strength and continuous yielding which is commonly attributed to mobile dislocations introduced during cooling process from the intercritical annealing temperature.

Atmospheric corrosion of carbon steel in acid rain by accelerated weathering test

In this work, the accelerated weathering test of immersion-wet-dry combined cycles was carried ont. The artificial acid rain of NaHSO3-(NH4)2SO4-H2SO4 solution system was selected as immersion solution. Acidity of artificial acid rain affected corrossion weight loss of carbon steel, and pH 4.1 was found to be a critical point. Anodic reaction resistance of the samples during accelerated weathering test increased with exposed time by electrochemical measurement.

Electrochemical Performance Study of Rust Layer on Cu-P-RE Weathering Steel

Corrosion rates of 10PCuRE steels with different rate earth contents and plain carbon steel were studied by dry-wet cycle immersion test. The corrosion resistance of rust layer on rare earths weathering steel and carbon steel was studied through the electrochemical means of polarization test and electrochemical impedance spectra. The difference of corrosion resistance of testing steels was analyzed through electrochemical means. The 10PCuRE steels whose rare earths content is smaller than 0.016% have good performance of corrosion resistance because corrosion potential of the steel is positive and resistance of rust layer is large. The results showed that rare earths of proper content could diminish corrosion tendency and promote the formation of the steady and compact rust layer.

CHARACTERISTICS OF MARTENSITIC TRANSFORMATION IN DUAL-PHASE STEELS

A theorectical expression for the driving force and M_(?) point of martensitic transformation has been proposed.The M_(?) values using this expression are in good agreement with that obtained experimentally.It was found that the values of M_(?) and M_(?) are not only related to the carbon content in martensite,but also to the volume fraction of ferrite.

The Study of Dual-phase Steel after Cyclic Deformation at Various Strain Amplitudes

Low cycle fatigue tests under plastic strain control were carried out with a dual-phase steel containing 23 Vol.-％ martensite. Specimens hardened rapidly at first few cycles followed by a slight softening to saturation stages when cycled at higher strain amplitudes, whereas at lower strain amplitudes the specimens presented continually hardening for a long time until saturation. TEM examination of the saturation dislocation structures show that clusters, parallel walls and cells were found at low, medium and high strain amplitude, respectively. It also has been found that the martensite/ferrite interfaces did not affect the dislocation structures signi- ficantly when a specimen was fatigued at lower strain amplitude. However, the dislocation struc- ture adjacent to the two-phase boundary is dif- ferent to some extent from that in the remote regions in the ferrite when a higher strain amplitude is applied.