Dual-phase Mg-Li alloys sheets were rolled at four different temperatures ranging from liquid nitrogen to 300℃to explore effect of rolling temperature on texture and mechanical properties of the material.Crystal plas...Dual-phase Mg-Li alloys sheets were rolled at four different temperatures ranging from liquid nitrogen to 300℃to explore effect of rolling temperature on texture and mechanical properties of the material.Crystal plasticity simulation was utilized to illustrate the influence of slip activity on rolling texture development.The results show that the rolling texture is largely depended on deformation temperature.Unlike commercial Mg alloys,the critical resolved shear stress of basal slip inα-Mg phase of Mg-Li alloy decreased more significantly by increasing temperature compared to that of pyramidal<c+a>slip.Enhancement of basal slip by increasing temperature triggered a decrease of split angle of basal poles for the double-peak texture.Prismaticslip largely enhanced by increasing temperature upon 200℃,which induced a wider orientation spread along the transverse direction.For theβ-Li phase,the promotion of{110}<111>slip system at elevated temperature triggered the enhancement of{211}<110>and{111}<211>texture components.The cryo-rolled sample exhibited the highest strength compared to the others due to a strong hardening behavior at this temperature.A two-stage hardening behavior was observed in these as-rolled dual-phase alloys.Strain transition at phase boundaries could be the reason for appearance of this two-stage hardening.展开更多
Crystalline/amorphous nanolaminate is an effective strategy to improve the mechanical properties of metallic materials,but the underlying deformation mechanism is still under the way of exploring.Here,the mechanical p...Crystalline/amorphous nanolaminate is an effective strategy to improve the mechanical properties of metallic materials,but the underlying deformation mechanism is still under the way of exploring.Here,the mechanical properties and plastic deformation mechanism of Ti/TiCu dual-phase nanolaminates(DPNLs)with different layer thicknesses are investigated using molecular dynamics simulations.The results indicate that the influence of the layer thickness on the plastic deformation mechanism in crystalline layer is negligible,while it affects the plastic deformation mechanism of amorphous layers distinctly.The crystallization of amorphous TiCu is exhibited in amorphous parts of the Ti/TiCu DPNLs,which is inversely proportional to the layer thickness.It is observed that the crystallization of the amorphous TiCu is a process driven by stress and heat.Young's moduli for the Ti/TiCu DPNLs are higher than those of composite material due to the amorphous/crystalline interfaces.Furthermore,the main plastic deformation mechanism in crystalline part:grain reorientation,transformation from hexagonal-close-packed-Ti to face-centered cubic-Ti and body-centered cubic-Ti,has also been displayed in the present work.The results may provide a guideline for design of high-performance Ti and its alloy.展开更多
基金F.Guo thanks for the support of Chongqing Research Program of Basic Research and Frontier Technology Scientific Research(cstc2019jcyj-msxmX0111)University Innovation Research Group of Chongqing(CXQT20023)+1 种基金Scientific Research Foundation of Chongqing University of Technology(2017ZD35)L.Y.Jiang is sponsored by Science and Technology Research Program of Chongqing Municipal Education Commission(Grant No.KJQN201901127).
文摘Dual-phase Mg-Li alloys sheets were rolled at four different temperatures ranging from liquid nitrogen to 300℃to explore effect of rolling temperature on texture and mechanical properties of the material.Crystal plasticity simulation was utilized to illustrate the influence of slip activity on rolling texture development.The results show that the rolling texture is largely depended on deformation temperature.Unlike commercial Mg alloys,the critical resolved shear stress of basal slip inα-Mg phase of Mg-Li alloy decreased more significantly by increasing temperature compared to that of pyramidal<c+a>slip.Enhancement of basal slip by increasing temperature triggered a decrease of split angle of basal poles for the double-peak texture.Prismaticslip largely enhanced by increasing temperature upon 200℃,which induced a wider orientation spread along the transverse direction.For theβ-Li phase,the promotion of{110}<111>slip system at elevated temperature triggered the enhancement of{211}<110>and{111}<211>texture components.The cryo-rolled sample exhibited the highest strength compared to the others due to a strong hardening behavior at this temperature.A two-stage hardening behavior was observed in these as-rolled dual-phase alloys.Strain transition at phase boundaries could be the reason for appearance of this two-stage hardening.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.51902254 and 12072286)the Natural Science Foundation of Shaanxi Province,China(Grant Nos.2021JZ-53 and 2018JQ5108)the Scientific Research Program Funded by Shaanxi Provincial Education Department,China(Grant No.20JK0845)。
文摘Crystalline/amorphous nanolaminate is an effective strategy to improve the mechanical properties of metallic materials,but the underlying deformation mechanism is still under the way of exploring.Here,the mechanical properties and plastic deformation mechanism of Ti/TiCu dual-phase nanolaminates(DPNLs)with different layer thicknesses are investigated using molecular dynamics simulations.The results indicate that the influence of the layer thickness on the plastic deformation mechanism in crystalline layer is negligible,while it affects the plastic deformation mechanism of amorphous layers distinctly.The crystallization of amorphous TiCu is exhibited in amorphous parts of the Ti/TiCu DPNLs,which is inversely proportional to the layer thickness.It is observed that the crystallization of the amorphous TiCu is a process driven by stress and heat.Young's moduli for the Ti/TiCu DPNLs are higher than those of composite material due to the amorphous/crystalline interfaces.Furthermore,the main plastic deformation mechanism in crystalline part:grain reorientation,transformation from hexagonal-close-packed-Ti to face-centered cubic-Ti and body-centered cubic-Ti,has also been displayed in the present work.The results may provide a guideline for design of high-performance Ti and its alloy.