This paper investigated on influence of different alloying elements added into duplex stainless steel (DSS) on phase transitions using thermochemical methods in comparison with experiment.The results showed that the m...This paper investigated on influence of different alloying elements added into duplex stainless steel (DSS) on phase transitions using thermochemical methods in comparison with experiment.The results showed that the most possible species in the ferrite phase,austenite phase,σphase,Hcp phase,χphase,and carbide were Cr:Va-type,Fe:Va-type,Ni:Cr:Mo-type,Cr_(2)N-type,Fe_(24)Mo_(10)Cr_(24)-type,and Cr:Mo:C-type,respectively.Furthermore,the Ni,N,Cr,and Mo alloying had significant influences on the transition of each DSS phase.The Ni and N additions obviously raised the temperature at ferrite-1/austenite-1 balance while the Cr and Mo decreased the dual-phase balance temperature.In addition,the Ni addition can promote the precipitating ofσphase at relatively high temperature while the precipitating of Hcp phase at relatively low temperature.The Hcp phase andχphase can be obviously increased by the N addition.The introduction of Cr and Mo notably enhances the precipitation ofσphase.However,the promotion ofχphase precipitation is facilitated by the presence of Mo,while the Cr element acts as an inhibitor forχphase precipitation.Furthermore,the ferrite/austenite ratio tested by experiment was higher than that calculated by thermochemical methods,thus pre-designed solution temperature should be lower about 30-100℃than that calculated by thermochemical methods.展开更多
During aging at a temperature ranging from 650 -950 ℃,the ferric matrix in duplex stainless steels undergoes various decomposition processes which could form the precipitates of the Sigma （σ） and Chi （X） phases,...During aging at a temperature ranging from 650 -950 ℃,the ferric matrix in duplex stainless steels undergoes various decomposition processes which could form the precipitates of the Sigma （σ） and Chi （X） phases, as well as nitrides. It is well known that these precipitates lead to a reduction in creep ductility and adversely affect toughness and corrosion properties of steel. This experiment carded out qualitative and quantitative analyses of intermetallic phases and nitrides and established an analytical procedure, including specimen preparation, the choosing of the electrolyte and electrolytic systems,electrolytic isolation,wet chemical separation, and physical and chemical analysis, etc. The residues were collected by ultrasonic cleaning and filtration after galvanostatic electrolysis. Dynamic laser scattering sizer （DLS- sizer） ,scanning electron microscope （SEM） and transmission electron microscope （TEM） were used to examine their structure,modality and size. Qualitative and quantitative analyses were performed by using X-ray diffraction （XRD）, oxygen-nitrogen analyzer and wet chemical analysis. Furthermore, there is a discussion on the effect of isothermal treatment on precipitation that occurs at different temperatures for different periods of time.展开更多
The precipitation kinetics of secondary phases in two austeno-ferritic lean duplex stainless steels（lean DSS）were examined after aging the materials at 800 ℃.Owing to the instability of ferrite,all DSS are known to...The precipitation kinetics of secondary phases in two austeno-ferritic lean duplex stainless steels（lean DSS）were examined after aging the materials at 800 ℃.Owing to the instability of ferrite,all DSS are known to be sensitive to solid-state phase transformations in the critical temperature range 600-1,000 ℃ and different secondary phases may form,depending on composition and microstructure.The performed thermodynamic simulations revealed the proneness to the precipitation of such phases also have been done in lean DSS,but only information on the equilibrium microstructures were achieved.Therefore,the materials were aged at various times,in order to verify the simulations and determine the precipitation kinetics.The occurred structural modifications were observed and quantified by scanning electron microscope and X-ray diffraction measurements,determining phase type,composition and volumetric fraction.At 800 ℃,grade 2101 was found to be only affected by Cr_2N nitrides precipitation,whereas a significant amount of σ-phase was found to form in LDX 2404 for treatment longer than 1 h,almost totally replacing ferrite after 50 h.Up to now,the intermetallic σ-phase has been observed only in the high alloyed DSS,and the unexpected precipitation in grade 2404 highlighted that the increased content of molybdenum in this steel might be considered as determinant for the formation.展开更多
Vertical section of Fe-18Cr-12Mn-0.04C-N system phase diagram varying with nitrogen content at 1×105 Pa was calculated using Thermo-Calc software and thermodynamic database.The morphology and crystallography info...Vertical section of Fe-18Cr-12Mn-0.04C-N system phase diagram varying with nitrogen content at 1×105 Pa was calculated using Thermo-Calc software and thermodynamic database.The morphology and crystallography information of precipitates in Fe-18Cr-12Mn-0.04C-0.48N high-nitrogen austenitic stainless steel during isothermal aging at 800 ℃ after austenization was investigated using optical microscopy(OM),and transmission electron microscopy(TEM) with energy distribution spectrum(EDS).The experimental results show that three precipitates,(Cr,Fe,Mn)2(N,C),(Cr,Fe,Mn)23(C,N)6 and σ phase exist in this steel,which is consistent with the thermodynamic calculation,indicating that thermodynamic calculation can provide instructions for alloy composition design,heat treatment and prediction of precipitation sequence in Fe-18Cr-12Mn-0.04C-N system.展开更多
A 27.6Cr-3.6Mo-2Ni alloy was solution treated and then aged for a long time to study the effect of grain size on precipitation behaviour by using X-ray diffraction, scanning electron microscopy and transmission electr...A 27.6Cr-3.6Mo-2Ni alloy was solution treated and then aged for a long time to study the effect of grain size on precipitation behaviour by using X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The experimental results demonstrated that the average grain size increased from 46.3 ± 6.2 to 101.8 ± 13.5 μm and the grain boundary length per unit area decreased from 3.3 × 10^(4) to 1.7 × 10^(4) m/m^(2) with an increasing annealing temperature from 1100 to 1200 ℃. After ageing at 800 ℃, the σ-phase,χ-phase and Laves phase were observed. As the ageing time increased, the σ-phase notably increased, while the χ-phase and Laves phase gradually decreased before finally vanishing after ageing for 400 h. The σ-phase precipitation kinetics curves consisted of two parts, and the grain size had a significant effect on the first stage of the precipitation curves due to the abundance of nucleation sites in the specimens with finer grains. The Laves phase was transformed from Nb(C,N) particles by Nb diffusion. As the ageing time increased, the ferrite phase decreased due to the transformation of the ferrite phase to the σ-phase, and then C was expelled into the untransformed ferrite grains. Moreover, new Nb(C,N) particles were formed by Nb diffusion from the Laves phase, resulting in the absence of the Laves phase.展开更多
采用Gleeble 3800热力模拟机对超级双相不锈钢SAF2507焊接热影响区组织进行模拟,研究了不同热输入条件下焊接热影响区显微组织和合金元素含量的变化,通过电化学循环伏安法评价了该组织的耐蚀性。研究结果表明,热输入由0.807 k J/mm增加...采用Gleeble 3800热力模拟机对超级双相不锈钢SAF2507焊接热影响区组织进行模拟,研究了不同热输入条件下焊接热影响区显微组织和合金元素含量的变化,通过电化学循环伏安法评价了该组织的耐蚀性。研究结果表明,热输入由0.807 k J/mm增加至2.552 k J/mm时,模拟热影响区上奥氏体以晶内奥氏体、晶界奥氏体和魏氏奥氏体3种形貌析出,含量由40%增加到52%。各个热输入时奥氏体的PRE值均大于铁素体的PRE值,因此奥氏体含量的增加使热影响区组织的点蚀电位从1030 m V提高至1082 m V。但是继续增加热输入至2.965 k J/mm时,在两相交界处观察到有粒状的χ相析出。虽然该组织上奥氏体含量仍有增加,但是χ相的析出却导致组织的点蚀电位降至1065 m V。展开更多
Multi-wall carbon nanotubes(MWNTs)/SnO core/shell nanosturcture was synthesized by a simple solution-based method,in which SnCl2 was solved in distilled water containing dispersed MWNTs,then stired,filtered and washed...Multi-wall carbon nanotubes(MWNTs)/SnO core/shell nanosturcture was synthesized by a simple solution-based method,in which SnCl2 was solved in distilled water containing dispersed MWNTs,then stired,filtered and washed in ambient atmosphere,finally dryed in air at 90 ℃ for 6 h.The MWNTs/SnO core/shell nanostructure was characterized by X-ray diffraction(XRD),transmission electron microscopy(TEM).It is found that surface defects of MWNTs are necessary for the deposition of SnO.The mechanism of the SnO nanocoating formation through the hydrolysis of SnCl2 in water(4SnCl_2+2H_2O-Sn_4(OH)2Cl_6+2HCl) was presented.展开更多
基金National Natural Science Foundation of China(51905536)Natural Science Foundation of Tianjin(22JCYBJC01280)Key Project of Natural Science of Fundamental Research Funds for the Central Universities of China(3122023039).
文摘This paper investigated on influence of different alloying elements added into duplex stainless steel (DSS) on phase transitions using thermochemical methods in comparison with experiment.The results showed that the most possible species in the ferrite phase,austenite phase,σphase,Hcp phase,χphase,and carbide were Cr:Va-type,Fe:Va-type,Ni:Cr:Mo-type,Cr_(2)N-type,Fe_(24)Mo_(10)Cr_(24)-type,and Cr:Mo:C-type,respectively.Furthermore,the Ni,N,Cr,and Mo alloying had significant influences on the transition of each DSS phase.The Ni and N additions obviously raised the temperature at ferrite-1/austenite-1 balance while the Cr and Mo decreased the dual-phase balance temperature.In addition,the Ni addition can promote the precipitating ofσphase at relatively high temperature while the precipitating of Hcp phase at relatively low temperature.The Hcp phase andχphase can be obviously increased by the N addition.The introduction of Cr and Mo notably enhances the precipitation ofσphase.However,the promotion ofχphase precipitation is facilitated by the presence of Mo,while the Cr element acts as an inhibitor forχphase precipitation.Furthermore,the ferrite/austenite ratio tested by experiment was higher than that calculated by thermochemical methods,thus pre-designed solution temperature should be lower about 30-100℃than that calculated by thermochemical methods.
文摘During aging at a temperature ranging from 650 -950 ℃,the ferric matrix in duplex stainless steels undergoes various decomposition processes which could form the precipitates of the Sigma （σ） and Chi （X） phases, as well as nitrides. It is well known that these precipitates lead to a reduction in creep ductility and adversely affect toughness and corrosion properties of steel. This experiment carded out qualitative and quantitative analyses of intermetallic phases and nitrides and established an analytical procedure, including specimen preparation, the choosing of the electrolyte and electrolytic systems,electrolytic isolation,wet chemical separation, and physical and chemical analysis, etc. The residues were collected by ultrasonic cleaning and filtration after galvanostatic electrolysis. Dynamic laser scattering sizer （DLS- sizer） ,scanning electron microscope （SEM） and transmission electron microscope （TEM） were used to examine their structure,modality and size. Qualitative and quantitative analyses were performed by using X-ray diffraction （XRD）, oxygen-nitrogen analyzer and wet chemical analysis. Furthermore, there is a discussion on the effect of isothermal treatment on precipitation that occurs at different temperatures for different periods of time.
文摘The precipitation kinetics of secondary phases in two austeno-ferritic lean duplex stainless steels（lean DSS）were examined after aging the materials at 800 ℃.Owing to the instability of ferrite,all DSS are known to be sensitive to solid-state phase transformations in the critical temperature range 600-1,000 ℃ and different secondary phases may form,depending on composition and microstructure.The performed thermodynamic simulations revealed the proneness to the precipitation of such phases also have been done in lean DSS,but only information on the equilibrium microstructures were achieved.Therefore,the materials were aged at various times,in order to verify the simulations and determine the precipitation kinetics.The occurred structural modifications were observed and quantified by scanning electron microscope and X-ray diffraction measurements,determining phase type,composition and volumetric fraction.At 800 ℃,grade 2101 was found to be only affected by Cr_2N nitrides precipitation,whereas a significant amount of σ-phase was found to form in LDX 2404 for treatment longer than 1 h,almost totally replacing ferrite after 50 h.Up to now,the intermetallic σ-phase has been observed only in the high alloyed DSS,and the unexpected precipitation in grade 2404 highlighted that the increased content of molybdenum in this steel might be considered as determinant for the formation.
基金This work is financially supported by Key Program of the National Natural Science Foundation of China( No50534010)National Program on Key Basic Research Project ( No2004CB619103)
文摘Vertical section of Fe-18Cr-12Mn-0.04C-N system phase diagram varying with nitrogen content at 1×105 Pa was calculated using Thermo-Calc software and thermodynamic database.The morphology and crystallography information of precipitates in Fe-18Cr-12Mn-0.04C-0.48N high-nitrogen austenitic stainless steel during isothermal aging at 800 ℃ after austenization was investigated using optical microscopy(OM),and transmission electron microscopy(TEM) with energy distribution spectrum(EDS).The experimental results show that three precipitates,(Cr,Fe,Mn)2(N,C),(Cr,Fe,Mn)23(C,N)6 and σ phase exist in this steel,which is consistent with the thermodynamic calculation,indicating that thermodynamic calculation can provide instructions for alloy composition design,heat treatment and prediction of precipitation sequence in Fe-18Cr-12Mn-0.04C-N system.
基金financially supported by the National Natural Science Foundation of China(Grant No.52075503)the Projects of International Cooperation in Shanxi,China(Grant No.201603D421026)。
文摘A 27.6Cr-3.6Mo-2Ni alloy was solution treated and then aged for a long time to study the effect of grain size on precipitation behaviour by using X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The experimental results demonstrated that the average grain size increased from 46.3 ± 6.2 to 101.8 ± 13.5 μm and the grain boundary length per unit area decreased from 3.3 × 10^(4) to 1.7 × 10^(4) m/m^(2) with an increasing annealing temperature from 1100 to 1200 ℃. After ageing at 800 ℃, the σ-phase,χ-phase and Laves phase were observed. As the ageing time increased, the σ-phase notably increased, while the χ-phase and Laves phase gradually decreased before finally vanishing after ageing for 400 h. The σ-phase precipitation kinetics curves consisted of two parts, and the grain size had a significant effect on the first stage of the precipitation curves due to the abundance of nucleation sites in the specimens with finer grains. The Laves phase was transformed from Nb(C,N) particles by Nb diffusion. As the ageing time increased, the ferrite phase decreased due to the transformation of the ferrite phase to the σ-phase, and then C was expelled into the untransformed ferrite grains. Moreover, new Nb(C,N) particles were formed by Nb diffusion from the Laves phase, resulting in the absence of the Laves phase.
文摘采用Gleeble 3800热力模拟机对超级双相不锈钢SAF2507焊接热影响区组织进行模拟,研究了不同热输入条件下焊接热影响区显微组织和合金元素含量的变化,通过电化学循环伏安法评价了该组织的耐蚀性。研究结果表明,热输入由0.807 k J/mm增加至2.552 k J/mm时,模拟热影响区上奥氏体以晶内奥氏体、晶界奥氏体和魏氏奥氏体3种形貌析出,含量由40%增加到52%。各个热输入时奥氏体的PRE值均大于铁素体的PRE值,因此奥氏体含量的增加使热影响区组织的点蚀电位从1030 m V提高至1082 m V。但是继续增加热输入至2.965 k J/mm时,在两相交界处观察到有粒状的χ相析出。虽然该组织上奥氏体含量仍有增加,但是χ相的析出却导致组织的点蚀电位降至1065 m V。
基金This work is financially supported by the National Science Foundation of China ( No 50602011)the Science Foundation of Heilongjiang Province ( No E200517) ]
文摘Multi-wall carbon nanotubes(MWNTs)/SnO core/shell nanosturcture was synthesized by a simple solution-based method,in which SnCl2 was solved in distilled water containing dispersed MWNTs,then stired,filtered and washed in ambient atmosphere,finally dryed in air at 90 ℃ for 6 h.The MWNTs/SnO core/shell nanostructure was characterized by X-ray diffraction(XRD),transmission electron microscopy(TEM).It is found that surface defects of MWNTs are necessary for the deposition of SnO.The mechanism of the SnO nanocoating formation through the hydrolysis of SnCl2 in water(4SnCl_2+2H_2O-Sn_4(OH)2Cl_6+2HCl) was presented.