X2CrNiMoN25-7-3 duplex stainless steel is suitable for chloride-containing environments such as seawater because it has excellent pitting corrosion resistance. Duplex stainless cast steel is often used to accommodate ...X2CrNiMoN25-7-3 duplex stainless steel is suitable for chloride-containing environments such as seawater because it has excellent pitting corrosion resistance. Duplex stainless cast steel is often used to accommodate the complexity of part geometry at joints. However, machining after casting is indispensable. This study evaluated the cutting characteristics of stainless cast steel. Adhesion of the cutting edge was weak at high cutting speeds, but tool wear was large. Diffusion and reactions between the work-pieces and the tool edge were investigated. Slight inter-diffusion and a reaction phase were observed, but the bond-ability was low.展开更多
Hot tearing is one of the major defects in continuous casting of steels, which severely limits the productivity of steelmaking processes. To further understand the defect, the problem of hot tearing in duplex stainles...Hot tearing is one of the major defects in continuous casting of steels, which severely limits the productivity of steelmaking processes. To further understand the defect, the problem of hot tearing in duplex stainless steel produced by a vertical continuous caster was investigated. A three-dimensional heat transfer and elastic-plastic model was developed based on the realistic roller layout in continuous slab casting, using ProCAST software. According to the hot tearing indicator criterion, the influence of operating parameters on the hot tearing susceptibility was evaluated. The results show that the surface temperature distribution is not sensitive to the superheat. The center of wide surface shell at the mold exit is the thinnest, and the thickness is about 10.52 mm at the superheat temperature of 40 -C. The hot tearing mainly concentrates on the slab solidification front and near the narrow face. However, corner cracks are prone to appear near the corner. With the increase in casting speed and the decrease in the cooling intensity in the secondary cooling zone, the solidification end point is rushed, which leads to the position of hot tearing lowering accordingly.展开更多
文摘X2CrNiMoN25-7-3 duplex stainless steel is suitable for chloride-containing environments such as seawater because it has excellent pitting corrosion resistance. Duplex stainless cast steel is often used to accommodate the complexity of part geometry at joints. However, machining after casting is indispensable. This study evaluated the cutting characteristics of stainless cast steel. Adhesion of the cutting edge was weak at high cutting speeds, but tool wear was large. Diffusion and reactions between the work-pieces and the tool edge were investigated. Slight inter-diffusion and a reaction phase were observed, but the bond-ability was low.
基金The authors gratefully express their appreciation to the National Natural Science Foundation of China(No.51474143)for the financial support.
文摘Hot tearing is one of the major defects in continuous casting of steels, which severely limits the productivity of steelmaking processes. To further understand the defect, the problem of hot tearing in duplex stainless steel produced by a vertical continuous caster was investigated. A three-dimensional heat transfer and elastic-plastic model was developed based on the realistic roller layout in continuous slab casting, using ProCAST software. According to the hot tearing indicator criterion, the influence of operating parameters on the hot tearing susceptibility was evaluated. The results show that the surface temperature distribution is not sensitive to the superheat. The center of wide surface shell at the mold exit is the thinnest, and the thickness is about 10.52 mm at the superheat temperature of 40 -C. The hot tearing mainly concentrates on the slab solidification front and near the narrow face. However, corner cracks are prone to appear near the corner. With the increase in casting speed and the decrease in the cooling intensity in the secondary cooling zone, the solidification end point is rushed, which leads to the position of hot tearing lowering accordingly.