Synthesis and Characterization of Novel Schiff Base for Enhanced Dye-Sensitized Solar Cell Photo-Response Mechanism

The efficient photo-response mechanism is one of the key factors in the commercialization of dye-sensitized solar cells in a bid to satisfy renewable energy demands. Progress in green technology has put solar energy on the front burner as a provider of clean and affordable energy for a sustainable society. We report the synthesis of a novel Schiff base with optical transparency in the visible and near IR region of the solar spectrum that can find application in the DSSCs photo-response mechanism. The synthesized crystal exhibited features that could handle some of the shortcomings of dye-sensitized solar cells which include wide band solar spectrum absorption and capability for swift charge transfer within the photoelectrodes. The synthesized Schiff base was characterized using x-ray diffractometer, UV/Visible spectrometer, Frontier transmission infrared spectrometer and conductometer. XRD data revealed the grown crystal to have an average crystallite size of 2.08 nm with average microstrain value of about 269.43. The FT-IR recorded transmission wave ѵ (CO) at 1207.7 cm−1 while dominant wave occurred at ѵ1654.9 and ѵ1592.3 cm−1 relating to ѵ (CN) stretching and ѵ (NH) bending respectively were observed. The IR spectrum revealed the bonding species and a probable molecular structure of 2,6-bis(benzyloxy)pyridine. The UV/Visible spectra convoluted to maximum peak within the near IR region suggesting that 2,6-bis(benzyloxy)pyridine can absorb both the visible and near IR region while its electrical conductivity was determined to be 4.58 µS/cm. The obtained result of the present study revealed promising characteristics of a photosensitizer that can find application in the photo-response mechanism of DSSCs.

Preparation of Multi-Wall Carbon Nanotubes/Graphene Composites with Cadmium Sulfide in Dye-Sensitized Solar Cells (DSSCs)

In the present work, Dye Sensitized Solar Cells (DSSCs) have been fabricated by utilizing a dense layer of photoelctrode cadmium sulfide thin film (CdS) as n-type, which prepared by spray coating, while p-type electrode was multi-wall carbon nanotubes/graphene (MWNT-G) composites. The experimental results showed the higher energy conversion efficiency for CdS/MWNT-G was 0.056% in comparison with the others, which were CdS/MWNT with 0.044% and CdS/G with 0.037% respectively, which referred to improvement in the conductivity by using MWNT-G. The microstructure and nanostructure of CdS, MWNT, G, and MWNT-G nanocomposite were carried out by employing Scanning Electron Microscopy (SEM). X-Ray Diffraction (XRD) has been used to get crystal size of CdS, Raman scattering, and optical absorption also used for characterizations the samples. This study promised to increase and enhance the conversion efficiency of photovoltaic devices.

Guanidinium Iodides-based Ionic Liquids: Synthesis and Application for Dye-sensitized Solar Cells(DSSCs)

A series of guanidinium ionic liquids（GILs） was designed, synthesized, and used as electrolytes for dye-sensitized solar cells（DSSCs）. The effect of electrolytes containing GILs on the photovoltaic performance of DSSCs was investigated. It is demonstrated that these GILs are promising for being used as electrolytes for DSSCs and a conversion efficiency of 4.1% can be obtained under AM 1.5 sun light irradiation.

Performance of Rhodamine-Sensitized Solar Cells Fabricated with Silver Nanoparticles

A plasmonic effect of silver nanoparticles (AgNPs) in dye-sensitized solar cells (DSSCs) is studied. In this investigation, the efficiency of dye-sensitized solar cells has been remarkably increased by infusion of synthesized silver nanoparticles into the TiO2 photoanode. Rhodaminederivative RdS1 was synthesized by microwave-assisted condensation of hydrazide and 3-for-mylchromone. The synthesized silver nanoparticles were characterized with UV/Vis absorption spectroscopy and transmission electron microscopy. The interfacial charge transport phenomena of the dye-sensitized solar cell (DSSCs) are determined by electrochemical impedance spectroscopy and the corresponding efficiencies are calculated using current-voltage (I-V) curve. The solar cell photoanode with silver nanoparticles infused with RdS1 in titanium dioxide had the highest solar-to-electric power efficiency at 0.17%.

Titania Nanostructures for Dye-sensitized Solar Cells

Titania is one kind of important materials, which has been extensively investigated because of its unique electronic and optical properties. Research efforts have largely focused on the optimization of the dye,but recently the titania nanostructures electrode itself has attracted more attention. It has been shown that particle size, shape, crystallinity, surface morphology, and chemistry of the TiO_2 material are key parameters which should be controlled for optimized performance of the solar cell. Titania can be found in different shape of nanostructures including mesoporous, nanotube, nanowire, and nanorod structures. The present article reviews the structural, synthesis, electronic, and optical properties of TiO_2 nanostructures for dye sensitized solar cells.

Dye-sensitized Solar Cells with Higher J_(sc) by Using Polyvinylidene Fluoride Membrane Counter Electrodes

A flexible counter electrode(CE) for dye-sensitized solar cells(DSCs) has been fabricated using a micro-porous polyvinylidene fluoride membrane as support media and sputtered Pt as the catalytic material.Non-conventional structure DSCs have been developed by the fabricated CEs. The Pt metal was sputtered onto one surface of the membrane as the catalytic material. DSCs were assembled by attaching the Ti O2 electrode to the membrane surface without Pt coating. The membrane was with cylindrical pore geometry. It served not only as a substrate for the CE but also as a spacer for the DSC. The fabricated DSC with the flexible membrane CE showed higher photocurrent density than the conventional sandwich devices based on chemically deposited Pt/FTO glass, achieving a photovoltaic conversion efficiency of 4.43%. The results provides useful information in investigation and development of stable, low-cost, simple-design, flexible and lightweight DSCs.

Novel micro-ring structured ZnO photoelectrode for dye-sensitized solar cell

The micro-ring like structured zinc oxide(ZnO) film was deposited on SnO_2: F coated glass substrate by sol-gel dip-coating technique with 1.0 g polyethylene glycol(PEG) content. The surface morphology of micro-ring structured ZnO film has been confirmed by the scanning electron microscope. This ZnO film is used to fabricate the solar cell with the help of ruthenium based dye and carbon counter electrode. The photoelectric and incident photon-to-current conversion efficiency was 1.17% and 48.4%, respectively. The DSC results have been compared with ZnO films prepared without PEG contents.

Recent Progress of Counter Electrodes in Nanocrystalline Dye-sensitized Solar Cells

Dye-sensitized solar cell （DSC） consists a combination of several different materials： photoanodes with nanoparticulated semiconductors, sensitizers, electrolytes and counter electrodes （CEs）. Each materials performs specific task for the conversion of solar energy into electricity. The main function of CE is to transfer electrons to the redox electrolyte and regenerate iodide ion. The work of CE is mainly focused on the studies of the kinetic performance and stability of the traditional CEs to improve the overall efficiency of DSC, seeking novel design concepts or new materials. In this review, the development and research progress of different CE materials and their electrochemical performance, and the problems are discussed.

Preparation and performance of dye-sensitized solar cells based on ZnO-modified TiO_2 electrodes

The ZnO-modified TiO2 electrode was prepared by adding Zn（CH3COO）2·2H2O to the TiO2 colloid during the sol-gel production process, and was used in dye-sensitized solar cells （DSCs）. The open circuit voltage （Voc） and fill factor （if） of the cells were improved sig- nificantly. The performances of the ZnO-modified TiO2 electrode such as dark current, transient photocurrent, impedance, absorption spectra, and fiat band potential （Vfb） were investigated. It is found that the interface charge recombination impedance increases and Vfb shifts about 200 mV toward the cathodic potential. The effect mechanism of ZnO modification on the performance of DSCs may be that ZnO occupies the surface states of the TiO2 film.

Influence of TiCl_4 treatment on performance of dye-sensitized solar cell assembled with nano-TiO_2 coating deposited by vacuum cold spraying

Titanium tetrachloride (TiCl4) treatment was employed to TiO2 coating deposited on fluoride-doped tin oxide (FTO) conducting glass and indium oxide doped tin oxide (ITO) conducting glass, respectively. The nano-crystalline TiO2 coating was deposited using a composite powder composed of polyethylene glycol (PEG) and 25 nm TiO2 particles by vacuum cold spraying (VCS) process. A commercial N-719 dye was used to adsorb on the surface of TiO2 coating to prepare TiO2 electrode, which was applied to assemble dye-sensitized solar cell (DSC). The cell performance was measured under simulated solar light at an intensity of 100 mW·cm-2. Results show that with an FTO substrate the DSC composed of a VCS TiO2 electrode untreated by TiCl4 gives a short-circuit current density of 13.1 mA·cm-2 and an open circuit voltage of 0.60 V corresponding to an overall conversion efficiency of 4.4%. It is found that after TiCl4 treatment to the VCS TiO2 electrode with an FTO substrate, the short circuit current density of the cell increases by 31%, the open-circuit voltage increases by 60 mV and a higher conversion yield of 6.5% was obtained. However, when an ITO substrate is used to deposit TiO2 coating by VCS, after TiCl4 treatment, the conversion efficiency of the assembled cell reduces slightly due to corrosion of the conducting layer on the ITO glass by TiCl4.

Well-aligned Ni Pt alloy counter electrodes for high-efficiency dye-sensitized solar cell applications

Development of cost-effective and robust counter electrodes(CEs) is a persistent objective for highefficiency dye-sensitized solar cells(DSSCs). To achieve this goal, we present here the hydrothermal synthesis of well-aligned Ni Pt alloy CEs, which is templated by ZnO nanowires and nanosheets. The preliminary results demonstrate that Ni Pt alloy electrodes are featured by increased charge-transfer processes and electrocatalytic activity in comparison with expensive Pt CE, yielding power conversion efficiencies of 8.29% and 7.41% in corresponding DSSCs with Ni Pt nanowire and nanosheet alloy CEs, respectively. Additionally, the Ni Pt alloy CEs also display extraordinary dissolution-resistant ability when suffering longterm utilization in liquid-junction DSSCs.

A Bi-layer Composite Film Based on TiO_2 Hollow Spheres, P25,and Multi-walled Carbon Nanotubes for Efficient Photoanode of Dye-sensitized Solar Cell

A bi-layer photoanode for dye-sensitized solar cell(DSSC) was fabricated, in which TiO_2 hollow spheres(THSs) were designed as a scattering layer and P25/multi-walled carbon nanotubes(MWNTs) as an under-layer. The THSs were synthesized by a sacrifice template method and showed good light scattering ability as an over-layer of the photoanode. MWNTs were mixed with P25 to form an under-layer of the photoanode to improve the electron transmission ability of the photoanode. The power conversion efficiency of this kind of DSSC with bi-layer was enhanced to 5.13 %,which is 14.25 % higher than that of pure P25 DSSC.Graphical Abstract A bi-layer composite photoanode based on P25/MWNTs-THSs with improved light scattering and electron transmission, which will provide a new insight into fabrication and structure design of highly efficient dyesensitized solar cells.

Dye-Sensitized Solar Cells Based on ZnO Films

In order to improve the performance of the dye-sensitized solar cells based on ZnO films, ZnO nanoparticles of different sizes were prepared by two methods. Some surfactants were added into the particles to form three types of ZnO pastes. Electrodes of various thickness applied to dye-sensitized solar cell were prepared starting from each of those pastes by the screen-printing method. The performance of dye-sensitized solar cells was optimized via both the selected particle size and film thickness. The reason of the inefficiency was explained by the infrared and ultraviolet- visible absorption spectra.

Effect of imidazole based polymer blend electrolytes for dye-sensitized solar cells in energy harvesting window glass applications

The exploration of polymer electrolyte in the field of dye sensitized solar cell(DSSC) can contribute to increase the invention of renewable energy applications. In the present work, the influence of imidazole on the poly(vinylidene fluoride)(PVDF)–poly(methyl methacrylate)(PMMA)–Ethylene carbonate(EC)–KI–I2 polymer blend electrolytes has been evaluated. The different weight percentages of imidazole added into polymer blend electrolytes have been prepared by solution casting. The prepared films were characterized by Fourier transform infrared spectroscopy(FTIR), X-ray diffraction(XRD), thermogravimetric analysis(TGA), UV–visible spectra, photoluminescence spectra and impedance spectroscopy. The surface roughness texture of the film was analyzed by atomic force microscopy(AFM). The ionic conductivity of the optimized polymer blend electrolyte was determined by impedance measurement, which is 1.95 × 10-3 S·cm-1 at room temperature. The polymer electrolyte containing 40 wt% of imidazole content exhibits the highest photo-conversion efficiency of 3.04%under the illumination of 100 m W·cm-2. Moreover, a considerable enhancement in the stability of the DSSC device was demonstrated.

Towards Improvement of Photovoltaic Performance of Aqueous Dye-sensitized Solar Cells by Tungsten-doped Mesoporous Nanobeads TiO_2 Working Electrode

Tungsten doped(W-doped) TiO_2 mesoporous nanobeads, possessing high surface area and superior scattering effect, were used for photoanode preparation. The W-doping would induce a positive shift of the TiO_2 conduction band, and enhance the driving force for electron injection and collection efficiencies. The electrochemical impedance spectra indicated a retarded charge recombination and increased electron diffusion length after W-doping. By fine-tuning the W-doping concentration to 0.25%, aqueous DSCs produced a significant improved the open circuit voltage of 712 mV and a short circuit current of 7.05 mA·cm^(-2), leading to an overall increased power conversion efficiency of 3.40% at 1 000 W·m^(-2) simulated irradiation, which is roughly 25% enhancement compared to that without W-doping photoanode.

A new D–D–π–A dye for efficient dye-sensitized solar cells

New metal-free organic dye sensitizers containing mono-triphenylamine or bis-triphenylamine as the electron donor, a thiophene as the π-conjugated system, and a cyanoacrylic acid moiety as the electron acceptor were synthesized. The optical and electrochemical properties of the dyes were investigated,and their performance as sensitizers in solar cells was evaluated. Dye-sensitized solar cells based on dye containing bis-triphenylamine as the electron donor produced a photon-to-current conversion efficiency of 6.06%（Jsc = 14.21 m A/cm;, Voc = 0.62 V, ff = 0.69） under 100 m W/cm;simulated AM 1.5 G solar irradiation（100 m W/cm;）.

Low platinum loading PtNPs/graphene composite catalyst with high electrocatalytic activity for dye-sensitized solar cells

Platinum nanoparticles （PtNPs）/graphene composite materials are synthesized by a controlled chemical reduction of H2PtC16 on graphene sheets. The electrocatalytic activity of a PtNPs/graphene composite counter electrode for a dye-sensitized solar cell （DSSC） is investigated. The results demonstrate that the PtNPs/graphene composite has high electrocatalytic activity for the dye-sensitized solar cell. The cell employing PtNPs （1.6 wt%）/graphene counter electrode reaches an conversion efficiency （η） of 3.89% upon the excitation of 100 mW/cm2 AM 1.5 white light, which is comparable to that of the cell with a Pt-film counter electrode （7 = 3.76%）. It suggests that one can use only 14% Pt content of the conventional Pt-film counter electrode to obtain a comparable conversion efficiency. It may be possible to obtain a high performance DSSC using the PtNPs/graphene composite with a very low Pt content as a counter electrode due to its simplicity, low cost, and large scalability.

Unique ZnS nanobuns decorated with reduced graphene oxide as an efficient and low-cost counter electrode for dye-sensitized solar cells

Unique ZnS nanobuns decorated with reduced graphene oxide （ROO） was synthesized and found to exhibit a synergetic effect as a highly efficient and low-cost counter electrode （CE） in dye-sensitized solar cells （DSCs）. Using this ZnS-ROO CE, a power conversion efficiency （PCE） of 7.03% was achieved. This value was 53% and 41 % higher than those of pure ZnS and ROO CEs, respectively. The ZnS-ROO nanocomposite is indeed an efficient and cost-effective Pt-like alternative for iodine reduction reaction.

Low temperature fabrication of flexible carbon counter electrode on ITO-PEN for dye-sensitized solar cells

A novel low temperature method was used to prepare the mesoporous carbon（MC） counter electrode（CE） on indium-doped tin oxide coated polyethylene naphthalate（ITO-PEN） for flexible dye-sensitized solar cells（DSSCs）.The obtained flexible MC CEs with carbon loading of 280μg cm^（-2） were characterized by SEM,XRD and electrochemical impedance.The light-to-electricity conversion efficiency of the DSSC fabricated with the prepared flexible MC CE was 86%of that of DSSC based on the decomposited Pt CE.

Enhanced Electrocatalytic Activity by RGO/MWCNTs/NiO Counter Electrode for Dye-sensitized Solar Cells

We applied the reduced graphene oxide/multi-walled carbon nanotubes/nickel oxide(RGO/MWCNTs/Ni O)nanocomposite as the counter electrode(CE) in dye-sensitized solar cells(DSSCs) on fluorine-doped tin oxide substrates by blade doctor method. Power conversion efficiency(PCE) of 8.13 % was achieved for this DSSCs device, which is higher than that of DSSCs devices using Ni O, RGO, and RGO/Ni O-CE(PCE = 2.71 %, PCE = 6.77 % and PCE = 7.63 %). Also, the fill factor of the DSSCs devices using the RGO/MWCNTs/Ni O-CE was better than that of other CEs. The electron transfer measurement of cyclic voltammetry and electrochemical impedance spectroscopy showed that RGO/MWCNTs/Ni O film could provide fast electron transfer between the CE and the electrolyte, and high electrocatalytic activity for the reduction of triiodide in a CE based on RGO/MWCNTs/Ni O in a DSSC.