Combined with DTG analysis, X-Ray diffraction analysis （XRD） and field emission scanning electron microscopy analysis （FSEM） affiliated with energy dispersive spectrometer analysis （EDS）, the early hydration and...Combined with DTG analysis, X-Ray diffraction analysis （XRD） and field emission scanning electron microscopy analysis （FSEM） affiliated with energy dispersive spectrometer analysis （EDS）, the early hydration and carbonation behavior of cement paste compacts incorporated with 30% of dolomite powder at low water to cement ratio （0.15） was investigated. The results showed that early carbonation curing was capable of developing rapid early strength. It is noted that the carbonation duration should be strictly controlled otherwise subsequent hydration might be hindered. Dolomite powder acted as nuclei of crystallization, resulting in acceleration of products formation and refinement of products crystal size. Therefore, as for cement-based material, it was found that early carbonation could reduce cement dosages to a large extent and promote rapid strength gain resulting from rapid formation of products, supplemental enhancement due to water release in the reaction of carbonation, and formation ofnanometer CaCO3 skeleton network at early age.展开更多
In this paper,C50 ultra-high-early-strength concrete was prepared with rapid-harden sulphoaluminate cement,alkali carbonate early strength agent,inorganic tribasic acid retarder and polycarboxylate water reducing agen...In this paper,C50 ultra-high-early-strength concrete was prepared with rapid-harden sulphoaluminate cement,alkali carbonate early strength agent,inorganic tribasic acid retarder and polycarboxylate water reducing agent. The properties testing results of C50 ultra-high-early-strength concrete indicated that the compressive strength at 12 h exceeded 37 MPa and at 3 d exceeded 59 MPa. Compared to the C50 ordinary reference concrete,the durability of C50 ultra-high-early strength concrete was investigated. The results indicated that C50 ultra-high-early-strength concrete had the same chloride ion permeability resistance,carbonization resistance and abrasion resistance to the C50 ordinary concrete. As to the sulfate resistance,the ultra-high-early-strength concrete was much better than the ordinary concrete.展开更多
基金Funded by the National Key Research Program(973 Program)(No.2013CB035901)the National Natural Science Foundation of China(No.51379163)
文摘Combined with DTG analysis, X-Ray diffraction analysis （XRD） and field emission scanning electron microscopy analysis （FSEM） affiliated with energy dispersive spectrometer analysis （EDS）, the early hydration and carbonation behavior of cement paste compacts incorporated with 30% of dolomite powder at low water to cement ratio （0.15） was investigated. The results showed that early carbonation curing was capable of developing rapid early strength. It is noted that the carbonation duration should be strictly controlled otherwise subsequent hydration might be hindered. Dolomite powder acted as nuclei of crystallization, resulting in acceleration of products formation and refinement of products crystal size. Therefore, as for cement-based material, it was found that early carbonation could reduce cement dosages to a large extent and promote rapid strength gain resulting from rapid formation of products, supplemental enhancement due to water release in the reaction of carbonation, and formation ofnanometer CaCO3 skeleton network at early age.
基金the financial support from China Communications Construction Company Limited.
文摘In this paper,C50 ultra-high-early-strength concrete was prepared with rapid-harden sulphoaluminate cement,alkali carbonate early strength agent,inorganic tribasic acid retarder and polycarboxylate water reducing agent. The properties testing results of C50 ultra-high-early-strength concrete indicated that the compressive strength at 12 h exceeded 37 MPa and at 3 d exceeded 59 MPa. Compared to the C50 ordinary reference concrete,the durability of C50 ultra-high-early strength concrete was investigated. The results indicated that C50 ultra-high-early-strength concrete had the same chloride ion permeability resistance,carbonization resistance and abrasion resistance to the C50 ordinary concrete. As to the sulfate resistance,the ultra-high-early-strength concrete was much better than the ordinary concrete.