Study on Particle Size and Electrochemical Properties of Rare Earth Based Hydrogen Storage Alloys

The rare earth based hydrogen storage alloys Ml_ 0.7Mm_ 0.3(Ni_ 3.55Co_ 0.75Mn_ 0.4Al_ 0.3) were chosen as objects of investigation in this paper. The effects of particle size on electrochemical properties of the alloy were investigated. The results indicate that the alloy with particle size of 100 and 150 mesh shows good activation behavior and high discharge capacity (the first discharge capacity and the maximum discharge capacity), but poor cycling stability, low capacity retention and high discharge capacity rate. The Ml_ 0.7Mm_ 0.3(Ni_ 3.55Co_ 0.75Mn_ 0.4Al_ 0.3) alloy with particle size of 150 mesh shows excellent electrochemical properties.

Study on Phase Structure and PCT Characteristics of Rare Earth Based Hydrogen Storage Alloys

The rare earth based hydrogen storage alloys Mm_xMl_ 1-xNi_ 3.55Co_ 0.75Mn_ 0.4Al_ 0.3(x=0～0.50) were investigated in this work. The influences of phase structure on the PCT characteristics were analyzed by means of electrochemical measurements. The results indicate that there is a strict relationship between crystal volume and PCT characteristics.

基于Google Earth Engine的洱海流域建成区范围及生态质量变化分析

以洱海流域为研究区,借助Google Earth Engine云平台,利用Landsat 8 OLI系列影像,合成研究区域的增强的指数型建筑指数(EIBI)并对洱海流域建成区进行提取,再对研究区域遥感生态指数进行合成,通过对建成区范围与流域范围内遥感生态指数进行空间相关分析,从而对2014—2021年洱海流域及其建成区进行生态评估。结果表明,EIBI可有效增强建筑信息,使用EIBI可有效、准确地提取研究区域建成区,经过EIBI提取,洱海流域2014—2021年建成区扩张面积共14.712 km2;2014—2021年洱海流域生态明显改善,遥感生态指数增加0.008,其上升速率为0.001/年,流域内超过65%的区域生态得到改善;洱海流域建成区与生态未得到改善区域大致匹配,建成区经过生态修复后生态质量未见显著提升,且建成区生态质量呈逐年下降趋势,说明建成区对环境改善具有阻力。

Magnetocaloric effect and slow magnetic relaxation behavior in binuclear rare earth based RE_(2)(L)_(2)(DMF)4(RE=Gd,Tb,and Dy) complexes

Three binuclear rare earth based complexes combining RE ions with semirigid tricarboxylic ligand(H_(3)L).namely,[RE_(2)(L)_(2)(DMF)_(4)][RE=Gd,Tb,and Dy;H_(3)L=5-((4-Carboxybenzyl)oxy)isophthalic acid;DMF=N,N-dimethylformamide]complexes,were fabricated success fully.The RE_(2)(L)_(2)(DMF)_(4) co mplexe s consist of two central RE ions with the same coordination environment which were connected by two tridentate bridging carboxylic groups and two syn-syn bidentate bridging carboxylic groups originating from the L^(3-)ligands to form the{RE_(2)}dimeric unit,and thus provides the basis for further constructing a dense three-dimensional(3 D)network structure.Moreover,the present RE_(2)(L)_(2)(DMF)_(4) complexes can be described by a topology diagram with the topology point symbol of{4^(2)·6}_(2){4^(4)·6^(2)·8^(7)·10^(2)}.Weak antiferromagnetic(AFM)coupling between the adjacent RE ions for all the present complexes was found according to the magnetic calculations.The observed significant cryogenic magnetocaloric effect(MCE)with the maximum magnetic entropy change-ΔS_(M)^(max) to be 26.3 J/(kg·K)withΔH=7 T in Gd_(2)(L)_(2)(DMF)_(4) complex makes it competitive for the cryogenic magnetic refrigerant.Moreover,the slow magnetic relaxation behavior at 0.2 T dc field with an obvious large U_(eff)/k=45(4)K and τ_(0)=6.5(2)×10^(-10)s was confirmed in Dy_(2)(L)_(2)(DMF)_(4)complex.This work not only provides an effective strategy for obtaining molecular materials with high MCE,but also confirms that tricarboxylate ligands are the ideal choice for constructing stable high dimensional geometric structures.

Simulation of nucleation and coalescence of second phase droplets during earth-based solidification process of immiscible alloys

The solidified microstructure of immiscible alloys strongly depends on the nucleation, diffusional growth, especially the coalescence of the second phase droplets in the miscibility gap. A numerical model based on the discrete multi-particle approach was developed to simulate the nucleation and coalescence mode of the second phase droplets during the earth-based processing of immiscible alloys (in this case, the effect of gravity cannot be neglected). The cooling rate is the major factor influencing the coalescence mode. Under the super-rapid or rapid solidification condition (>104K/s), Brownian collision is the dominant coalescence mode. Marangoni collision becomes the dominant mode under the sub-rapid solidification condition (>102K/s). In the conventional slow cooling scope(101K/s), Stokes collision becomes the dominant coalescence mode, correspondingly, leading to a serious phase segregation.

Effect of Heat-Treatment Process on Properties of Rare Earth Mg-Based System Hydrogen Storage Alloys with AB_3-Type

The effect of heat-treatment process on the properties of Mm0.8Mg0.2(NiCoAlMn)3.5 hydrogen storage alloy was discussed . The electrochemical properties such as cycling stability, activation property, and the plateau voltage of the alloy which was heat-treated in various temperatures and times had different changes during the cycle process, the optimum heat-treatment conditions of this alloy were determined by this work.

Study on Nanocrystalline Rare Earth Mg-Based System Hydrogen Storage Alloys with AB_3-Type

A sort of rare earth Mg-based system hydrogen storage alloys with AB3-type was prepared by double-roller rapid quenching method. The alloys were nanocrystalline multi-phase structures composed of LaNi3 phase and LaNi5 phase by X-ray diffraction and scanning electron microscopy analyses, and the suitable absorption/desorption plateau was revealed by the measurement of P-C-I curve. Electrochemical studies indicate that the alloys exhibit good electrochemical properties such as high capacity and stable cycle life, and the discharge capacity is 369 mAh·g-1 at 0.2 C (72 mA·g-1). after 460 cycles, the capacity decay was only 19.4% at 2 C (720 mA·g-1).

Synthesis, Characterization and Bioactivity of Complexes of Rare Earth with Bis-Schiff Base from Furoylpyrazolone

Eleven new complexes of rare earths with bis-Schiff base derived from N,N'-bis[(1-phenyl-3-methyl-5-oxo-4-pyrazolinyl) alpha-furylmethylidyne] ethylenediimine ((HPM alpha FP)(2)en) were synthesized. On the basis of elemental analysis and molar conductance, a general formula of the complexes, [RE(HPM alpha FP)(2)en(NO3)(2)]NO3(RE = La, Pr, Nd, Sm, Eu, Th, Dy, Ho, Er, Yb,Y), was given. The complexes were characterized by IR, UV-visible, H-1 NMR, C-13 NMR and fluorescence. The results show that the bis-Schiff base is a quadridentate ligand and the rare earth ions exhibit coordination of eight in the complexes. The antibacterial experiments indicate that they have high antibacterial activities against S. aureus, B. subtillis, E. coli, E. carotovora, C. flaccumfaciens.

Synthesis, characterization, and anticancer properties of rare earth complexes with Schiff base and o-phenanthroline

Five novel ternary complexes of the rare earth ions with o-phenanthroline（Phen） and Schiff base salicylaldehyde L-phenyla- lanine（KHL） were synthesized in ethanol. Their compositions were characterized by elemental analysis, molar conductance, ^1H NMR, FT-IR, and Raman spectra. The formulas of the complexes were verified to be RE（L）（Phen）Cl（H2O） （RE=La^3＋, Ce^3＋, Nd^3＋, Er^3＋, and Gd^3＋; L=Schiff base salicylaldehyde L-phenylalanine; phen=o-phenanthroline）. Methyl thiazolyl tetrazolium （MTT） colorimetry and flow cytometry were used to test the anticancer effect of the complexes with K562 tumor cell. The research showed that the complexes could inhibit K562 tumor cell＇s growth, generation, and induce apoptosis. The inhibition ratio was accelerated by increasing the dosage, and it had significant positive correlation with the medication dosage.

FORMATION OF GRADIENT COATING OF Fe-BASED ALLOY WITH RARE EARTHS BY PLASMA SURFACING

A gradient coating of Fe-based alloy was manufactured with rare earths (RE) by plasma surfacing on Q235 steel substrate. The coatings were studied by using X-ray diffraction(XRD), scanning electron microscope(SEM), differential thermal analyzer(DTA), and electron probe micro-analyzer (EPMA). The results show that the phases of the two kinds of coatings(with and without RE) both include α-Fe, Fe7C3, Fe3C, Cr2B, Fe2B and FeB. The microstructure of F314 coating is mainly hypereutectic, the pro-phases Cr7C3 and Cr2B are loose, crassi, spiculate and contain microcracks. The brittleness of the coating is high, and the average hardness is 787 HV. When 0.8wt% RE was added into the F314 alloy, the microstructure varied from hypoeutectic to hypereutectic continuously, The hardness appears as gradient distribution with the highest value of 773 HV, meanwhile, the brittleness decreases significantly. The formation of gradient structure depends on the fallowing factors: (i) the conversion of RE. The addition of RE lowers the elements point and Fe-C eutectic temperature, thus the base metal melting acutely. (ii) the heating of plasma arc. Graded temperature results in directional solidification, thus the gradient structure forms easily. The main reasons for the hardness decrease with RE addition in the alloy are the ratio of hard phase lowering and the hardness of the hard phase decreasing.

Effect of Roasting Conditions of Rich Cerium Rare Earth Carbonate on Crystallite Morphology and Polishing Ability of Ceria-Based Rare Earth Oxide

The granule shape and crystal structure of the the ceria-based rare earth oxide which were roasted at 600～1050 ℃ for 2～6 h and then cooled in furnace, cooled out of furnace or cooled in water were studied by means of XRD and SEM. The results revealed that the rich cerium rare earth carbonate could be changed into the rare earth oxide which was a kind of sandwich made of globose granule whose diameter was between 0.5～3.0 μm after being roasted in 900 ℃ for 2 h. This kind of crystal lattice in rare earth oxide belonged to face-centered cubic lattice and its space between crystal surface {111} and {200} (viz. L111 and L200) would enlarge as the roasting temperature increasing. With increasing roasting temperature, L111 would rise straightly upward, and L200 would rise straightly upward when roasting time was 2～4 h but changed little when roasting time was 4～6 h. The glass-polishing experiments found that the polishing ability of the ceria-based rare earth oxide was the best as L111 was 43～53 nm and the L200 was 43～56 nm.

Effect of Rare Earth on the Corrosion-Resisting Performance of Zinc-Based Alloy Coatings

The corrosion behavior of coatings of pure zinc and Zn-Al,Zn-Al-RE alloys in NaCl solu- tions was studied by salt-spray experiments,even corrosion experiments and electrochemical measurements of bi-directional polarization curves and a.c.impedance in weak polarization region consistent regularities were obtained by these different methods,viz.,the corrosion resistance of Zn could be enhanced by alloying it with Al,and particularly with Al-RE.The causes of enhancement of corrosion resistance by RE were also discussed.

Study on Rare Earth-Containing Phases in TiAl Based Alloys Prepared by Non-Equilibrium Solidification Processing

Microstructure evolution of rare earth rich phase of rapidly-solidified (RS) TiAl based alloys was investigated. The two rapid-solidification techniques employed are melt-spinning technique (MS) and Hammer-and-Anvil technique (HB). MS ribbons and HA foils were obtained in the experiment. The results demonstrate that with the increasing of cooling rates of TiAl based alloys great changes are taken place in the microstructures of rare earth rich phase, from scattering mainly on grain boundaries of as-cast ingot to distributing homogeneously as very fine fibers or powders (nanometer grade) on the matrix. The fine paralleling second phase fibers in the HA foils are considered to be connected with gamma/alpha (2) lamellar colonies. Selected area electronic diffraction (SAED) patterns of the rare earth rich phase is in accordance with that of intermetallic AlCe.

Mechanism of interaction relation between the rare-earth element Ce and impurity elements Pb and Bi in Ag-based filler metal

The mechanism of interaction relation between the rare-earth element Ce and elements Pb and Bi in Ag-based filler metal has been studied. The results show that the compounds CePb and CeBi with high melting point can be easily produced between these three elements in the filler metal, which greatly limited the formation of the isolated phase Pb or Bi and also eliminated the bad effect of impurity elements Pb and Bi on the spreading property of Ag-based filler metal. The metallurgical and quantum-mechanical bond formation analysis show that a strong chemical affinity was existed between the rare-earth element Ce and impurity elements Pb and Bi, which was proved by the XRD analysis results.

Improving Wear Resistance of the Ni-base Thermal Spray-Welding Coating Using Rare Earths

By adding rare earth alloy and cerium oxide, the effect of rare earths on tribological properties of nickel base alloy layer was studied to approach the possibility of applying rare earths to Ni base thermal spray welding coating. Wear test results showed that the wear rates of the nickel base coating without rare earths were quite high, and the load bearing capacity of coating was low, in contrast, the wear rates of the coating with rare earths were low and the coating had higher load bearing capacity. The results show that rare earths can refine the structure of nickel base alloy, improve the interface of the coating and substrate.

Effect of Rare Earth on Microstructure of Vacuum Melting Ni-Based Self-Fluxing Alloy Coatings

The Ni-based self-fluxing alloy coating containing RE was acquired by the technique of vacuum melting on the hypoeutectoid steel (Fe-0.45%C) matrix. By X-ray diffraction, SEM and EDX, the microstructure and phase structure of section of coating and the microstructure near the interface between coating and matrix were investigated, and the effect of RE on microstructure of coating was also discussed. The results show that the microstructure of the NiCrBSi alloy coating is composed of Ni-based solid solution and a lot of massive, globular and needle secondary phases CrB, Ni_3B, Cr_7C_3, Cr_(23)C_6 among the solid solution. The metallurgical binding between steel matrix and coating is realized. RE makes needle phase of alloy coating vanish. New phases of NiB and Cr_(6.5)Ni_(2.5)Si are precipitated from alloy coating, and secondary phases of alloy coating are sphericized. Consequently, RE also hinders the diffusion of Ni, Cr and Si atoms from coating to matrix and Fe atoms from matrix to coating, holds back the dilution of Fe for NiCrBSi alloy coating, and assures the chemical composition of the alloy coating.

COMPLEXES OF RARE EARTH NITRATE WITH SCHIFF BASE DERIVED FROM VANILLIN AND P-TOLUIDINE

In this paper,complexes of rare earth nitrate with Schiff base derived from vanillin(3-methoxy-4-hydroxy-benzaldehyde)and p-toluidine[LnL_2(NO_3)_2]NO_3(Ln=La-Eu except Pm,L=Schiff base ligand) have been prepared and characterized.

EFFECT OF RARE EARTH ELEMENT Er ON STRENGTHENING OF INTERFACE OF Ti（C，N） BASED CERMETS

ＥＦＦＥＣＴＯＦＲＡＲＥＥＡＲＴＨＥＬＥＭＥＮＴＥｒＯＮＳＴＲＥＮＧＴＨＥＮＩＮＧＯＦＩＮＴＥＲＦＡＣＥＯＦＴｉ（Ｃ，Ｎ）ＢＡＳＥＤＣＥＲＭＥＴＳ￥ＬｉｕＮｉｎｇ（ＤｅｐａｒｔｍｅｎｔｏｆＭａｔｅｒｉａｌｓＳｃｉｅｎｃｅａｎｄＥｎｇｉｎｅｅｒｉｎｇ，...

Study of Bi_2O_3-based Rare Earth Solid Electrolyte Used in Fuel Cell

Solid ceramic electrolyte materials (Bi_2O_3)_(0.75)(Y_2O_3)_(0.25) and(Bi_2O_3)_(0.65)(Gd_2O_3 )_(0.35)were synthesized.Their crystal structure, XPS spectra and the change of ionic conductivity versus temperature were measured.A Bi_2O_3-based rare earth solid electrolyte fuel cell with ZrO_2-Y_2O_3 protection film was made.