The effects of the partial substitution of element M(M=Cr,V,Mn,x=0.05;Zr,Ga,x=0.017; Si,x=0.15;Co,x=0.10)for Fe in samarium-iron-nitride Sm_2(Fe_(1-x)M_x)_(17)N_y compounds on their stabilities and Curie temperatures ...The effects of the partial substitution of element M(M=Cr,V,Mn,x=0.05;Zr,Ga,x=0.017; Si,x=0.15;Co,x=0.10)for Fe in samarium-iron-nitride Sm_2(Fe_(1-x)M_x)_(17)N_y compounds on their stabilities and Curie temperatures have been studied.It is found that Co,Ga can raise the Curie temperature of the compounds.The initial decomposition temperatures cannot be raised significantly by all the studied elements except Co.The result contradicts the formation enthalpy consideration.The final decomposition tempera- tures can be raised by all of the substitution elements.The effects of atmospheres on their decomposition be- havior were also studied.The results show that oxidation is the major reason for magnetic deterioration of the powder heated in air.Compared with nitrogen atmosphere,argon or vacuum helps to delay the decompo- sition of the compounds.展开更多
文摘The effects of the partial substitution of element M(M=Cr,V,Mn,x=0.05;Zr,Ga,x=0.017; Si,x=0.15;Co,x=0.10)for Fe in samarium-iron-nitride Sm_2(Fe_(1-x)M_x)_(17)N_y compounds on their stabilities and Curie temperatures have been studied.It is found that Co,Ga can raise the Curie temperature of the compounds.The initial decomposition temperatures cannot be raised significantly by all the studied elements except Co.The result contradicts the formation enthalpy consideration.The final decomposition tempera- tures can be raised by all of the substitution elements.The effects of atmospheres on their decomposition be- havior were also studied.The results show that oxidation is the major reason for magnetic deterioration of the powder heated in air.Compared with nitrogen atmosphere,argon or vacuum helps to delay the decompo- sition of the compounds.