A double-layer aluminum consisting of an aluminum core and a shellof SiO2 and polyacrylic acid was synthesized.This modified aluminum was used to improve the corrosion resistance and dispersive property of aluminum in...A double-layer aluminum consisting of an aluminum core and a shellof SiO2 and polyacrylic acid was synthesized.This modified aluminum was used to improve the corrosion resistance and dispersive property of aluminum in waterborne media.TEM,FTIR,XPS,and EDX determination showed that PAA and SiO2 were coated on the surface of aluminum.Evolved hydrogen detection showed that the corrosion resistance of composite particle had been markedly improved.Maximum corrosion inhibition efficiency of SiO2 coated aluminum（SiO2@Al）was 95.1% while that of double-layer coated aluminum（PAA/SiO2@Al）was 98.8%.Meanwhile,polyacrylic acid layer improved the agglomeration of aluminum significantly.According to the dispersibility test,the particle size of 50% volume fraction [d（0.5）] of aluminum,SiO2@Aland PAA/SiO2@Alwere 42,53,and 34 μm,respectively.展开更多
Novel phosphate pigments imitated with Scorzalite,FeAl2(PO4)2(OH)2,were prepared from iron and aluminum nitrate solutions,ascorbic acid,and phosphoric acid with pH adjustments(pH 5,7,9).The obtained precipitates were ...Novel phosphate pigments imitated with Scorzalite,FeAl2(PO4)2(OH)2,were prepared from iron and aluminum nitrate solutions,ascorbic acid,and phosphoric acid with pH adjustments(pH 5,7,9).The obtained precipitates were heated at 300,500,and 700°C for 1 h.The precipitates and their thermal products were estimated with X-ray diffraction(XRD),Infrared(IR)spectra,ultraviolet-visible(UV-Vis)reflectance spectra,and L*a*b*color space.The precipitated sample was not clearly colored,but it turned orange to red when heated.Samples prepared at low pH showed higher whiteness than samples prepared at high pH.The theoretical amount of ascorbic acid was sufficient to completely reduce iron during the adjustment.This study showed the possibility of novel inorganic phosphate red pigment.展开更多
基金Funded by the National Natural Science Foundation of China(31170558)the Fundamental Research Funds for the Central Universities(410500006)
文摘A double-layer aluminum consisting of an aluminum core and a shellof SiO2 and polyacrylic acid was synthesized.This modified aluminum was used to improve the corrosion resistance and dispersive property of aluminum in waterborne media.TEM,FTIR,XPS,and EDX determination showed that PAA and SiO2 were coated on the surface of aluminum.Evolved hydrogen detection showed that the corrosion resistance of composite particle had been markedly improved.Maximum corrosion inhibition efficiency of SiO2 coated aluminum（SiO2@Al）was 95.1% while that of double-layer coated aluminum（PAA/SiO2@Al）was 98.8%.Meanwhile,polyacrylic acid layer improved the agglomeration of aluminum significantly.According to the dispersibility test,the particle size of 50% volume fraction [d（0.5）] of aluminum,SiO2@Aland PAA/SiO2@Alwere 42,53,and 34 μm,respectively.
文摘Novel phosphate pigments imitated with Scorzalite,FeAl2(PO4)2(OH)2,were prepared from iron and aluminum nitrate solutions,ascorbic acid,and phosphoric acid with pH adjustments(pH 5,7,9).The obtained precipitates were heated at 300,500,and 700°C for 1 h.The precipitates and their thermal products were estimated with X-ray diffraction(XRD),Infrared(IR)spectra,ultraviolet-visible(UV-Vis)reflectance spectra,and L*a*b*color space.The precipitated sample was not clearly colored,but it turned orange to red when heated.Samples prepared at low pH showed higher whiteness than samples prepared at high pH.The theoretical amount of ascorbic acid was sufficient to completely reduce iron during the adjustment.This study showed the possibility of novel inorganic phosphate red pigment.