Niobium was electrodeposited on 316 stainless steel bipolar plates of a fuel cell in water and air-stable choline chloride based ionic liquids. The electrochemical corruption property of bipolar plates in simulated PE...Niobium was electrodeposited on 316 stainless steel bipolar plates of a fuel cell in water and air-stable choline chloride based ionic liquids. The electrochemical corruption property of bipolar plates in simulated PEMFC environment was investigated. It was showed that the plating film was distributed on the surface of 316 stainless steel like isolated islands with height less than 50 nm. The XPS, XRD results showed that a smooth and strong chemical inert film of Nb O and Nb2O5 was formed on the surface of 316 stainless steel. In simulated cathodic condition, the corrosion potential of Nb coated stainless steel was improved by 244 m V, whilst in an anodic condition, it was improved by 105 m V. The current densities for the coated 316 stainless steel were decreased to 2.479 4 μA·cm-2 from 14.810 μA·cm-2 at-0.1 V and to 0.576 μA·cm-2 from 13.417 μA/·cm-2 at 0.6 V, respectively. It was implied that the niobium coating effectively decreased the corrosion rate. The results of the electrochemical tests indicated that the corrosion resistance of stainless steel was greatly improved after coated with niobium.展开更多
A new conception, which combines the advantages of both twist drill and diamond grit, is proposed to develop a new tool for drilling hard brittle materials. The manufacturing process of the drill is introduced, and d...A new conception, which combines the advantages of both twist drill and diamond grit, is proposed to develop a new tool for drilling hard brittle materials. The manufacturing process of the drill is introduced, and drilling experiments are carried out by using of the drill developed. As a result, not only it can drill holes with a high efficiency, but also a good quality of hole inlet and outlet can be obtained for such materials as glasses, marble, granite, Al 2O 3, etc. The prospect in practical application of the technique developed is also discussed.展开更多
基金Funded by the National Natural Science Foundation of China(No.21276036)the Fundamental Research Funds for the Central Universities(No.3132014323)
文摘Niobium was electrodeposited on 316 stainless steel bipolar plates of a fuel cell in water and air-stable choline chloride based ionic liquids. The electrochemical corruption property of bipolar plates in simulated PEMFC environment was investigated. It was showed that the plating film was distributed on the surface of 316 stainless steel like isolated islands with height less than 50 nm. The XPS, XRD results showed that a smooth and strong chemical inert film of Nb O and Nb2O5 was formed on the surface of 316 stainless steel. In simulated cathodic condition, the corrosion potential of Nb coated stainless steel was improved by 244 m V, whilst in an anodic condition, it was improved by 105 m V. The current densities for the coated 316 stainless steel were decreased to 2.479 4 μA·cm-2 from 14.810 μA·cm-2 at-0.1 V and to 0.576 μA·cm-2 from 13.417 μA/·cm-2 at 0.6 V, respectively. It was implied that the niobium coating effectively decreased the corrosion rate. The results of the electrochemical tests indicated that the corrosion resistance of stainless steel was greatly improved after coated with niobium.
文摘A new conception, which combines the advantages of both twist drill and diamond grit, is proposed to develop a new tool for drilling hard brittle materials. The manufacturing process of the drill is introduced, and drilling experiments are carried out by using of the drill developed. As a result, not only it can drill holes with a high efficiency, but also a good quality of hole inlet and outlet can be obtained for such materials as glasses, marble, granite, Al 2O 3, etc. The prospect in practical application of the technique developed is also discussed.