Anion adsorption behavior on Au colloid surface was investigated in virture of depositing monolayers of Au colloid on the self-assembled monolayers of cysteamine on a gold electrode. Po- tential-dependent anion adsor...Anion adsorption behavior on Au colloid surface was investigated in virture of depositing monolayers of Au colloid on the self-assembled monolayers of cysteamine on a gold electrode. Po- tential-dependent anion adsorption-desorption waves via the nonfaradaic current were obtained by means of cyclic voltammetry at Au coltoid-modified gold electrodes in the potential range of -2 00-600 mV. The adsorption sequence in the order of adsorption peak potentials (Epa) is OH- >citrate3 ->H2PO4- >Cl->SO42->ClO4->NO3-. Among them, citrate3- exhibited an en- tirely irreversible adsorption. A rise in temperature can increase the rates of adsorption-desorp- tion and improve the reversibility of the adsorption-desorption of Cl-, SO42-, ClO4-, NO3- and H2PO-4. The adsorption peak potentials shifted more negatively for Ca. 63 mV as the anion con- centrations were increased by a decade factor. The change of pH from 7 to 1 slightly affected the adsorption peak potentials of Cl- and NO3-. Au colloids with a smaller size (16 nm) gave rise to a better reversibility of the adsorption-desorption process and lower adsorption currents. The ex- perimental results of citrate ions adsorption on Au colloid surface show that Au colloids with a smaller size prepared by sodium citrate method exhibited a higher stability in the solution in com- parison to those with larger sizes because of its higher ratio of charge/mass. In other words, the smaller gold nanoparticles are covered with citrate ions monolayer that can also be formed at larg- er gold nanoparticles by means of electrochemical scan.展开更多
基金the National Natural Sciences Foundation of China(No. 29835110).
文摘Anion adsorption behavior on Au colloid surface was investigated in virture of depositing monolayers of Au colloid on the self-assembled monolayers of cysteamine on a gold electrode. Po- tential-dependent anion adsorption-desorption waves via the nonfaradaic current were obtained by means of cyclic voltammetry at Au coltoid-modified gold electrodes in the potential range of -2 00-600 mV. The adsorption sequence in the order of adsorption peak potentials (Epa) is OH- >citrate3 ->H2PO4- >Cl->SO42->ClO4->NO3-. Among them, citrate3- exhibited an en- tirely irreversible adsorption. A rise in temperature can increase the rates of adsorption-desorp- tion and improve the reversibility of the adsorption-desorption of Cl-, SO42-, ClO4-, NO3- and H2PO-4. The adsorption peak potentials shifted more negatively for Ca. 63 mV as the anion con- centrations were increased by a decade factor. The change of pH from 7 to 1 slightly affected the adsorption peak potentials of Cl- and NO3-. Au colloids with a smaller size (16 nm) gave rise to a better reversibility of the adsorption-desorption process and lower adsorption currents. The ex- perimental results of citrate ions adsorption on Au colloid surface show that Au colloids with a smaller size prepared by sodium citrate method exhibited a higher stability in the solution in com- parison to those with larger sizes because of its higher ratio of charge/mass. In other words, the smaller gold nanoparticles are covered with citrate ions monolayer that can also be formed at larg- er gold nanoparticles by means of electrochemical scan.
