Technology and properties of electroless composite RE-Ni-B-SiC coatings have been investigated.Results show that stabilizer plys a decisive role in electroless composite Ni-B-SiC,the addition of appropriate quantity o...Technology and properties of electroless composite RE-Ni-B-SiC coatings have been investigated.Results show that stabilizer plys a decisive role in electroless composite Ni-B-SiC,the addition of appropriate quantity of RE(rare earth) into the Ni-B-SiC bath not only increases SiC content in composite coatings,their hardness and wear resistance but also improves crystalline fineness,Wear resistance increases with the increase of SiC.Hardness and wear resistance of composite coatings reach peak values a fter heat treatment at 4OO and 500℃ for 1h respectively.展开更多
A NiP/TiO2 composite film on carbon steel was prepared by electroless plating and sol-gel composite process. An artificial neural network was applied to optimize the prepared condition of the composite film. Corrosion...A NiP/TiO2 composite film on carbon steel was prepared by electroless plating and sol-gel composite process. An artificial neural network was applied to optimize the prepared condition of the composite film. Corrosion behavior of the NiP/TiO2 composite film was investigated by polarization resistance measurement, anode polarization, ESEM （environmental scanning electron microscopy） and EIS （electrochemical impedance spectroscopy） measurements. Results showed that the NiP/ TiO2 composite film has a good corrosion resistance in 0.5mol/L H2SO4 solution. The element valence of the composite film was characterized by XPS （X-ray photoelectron spectroscopy） spectrum, and an anticorrosion mechanism of the composite film was discussed.展开更多
The effect of nanodiamond content in electrolyte and rotational speed of the stirrer on the deposition rate of coatings, the nanodiamond content in coatings, the micro- structure and the micro-hardness of coatings wer...The effect of nanodiamond content in electrolyte and rotational speed of the stirrer on the deposition rate of coatings, the nanodiamond content in coatings, the micro- structure and the micro-hardness of coatings were studicd. A self-made pin-on-disk tribo-meter was employed to evaluate the wear resistance of prepared coatings. Re- sults show that the thickness of composite coating decreases with the rotational speed, while the micro hardness of coating and the content of nanodiamond in coating increase with increasing its content in electrolyte. The wear resistance of the composite coating deposited in an electrolye with 6 g/L nanodiamond increases by 50% in contrast with the pure Ni-P coating.展开更多
文摘Technology and properties of electroless composite RE-Ni-B-SiC coatings have been investigated.Results show that stabilizer plys a decisive role in electroless composite Ni-B-SiC,the addition of appropriate quantity of RE(rare earth) into the Ni-B-SiC bath not only increases SiC content in composite coatings,their hardness and wear resistance but also improves crystalline fineness,Wear resistance increases with the increase of SiC.Hardness and wear resistance of composite coatings reach peak values a fter heat treatment at 4OO and 500℃ for 1h respectively.
文摘A NiP/TiO2 composite film on carbon steel was prepared by electroless plating and sol-gel composite process. An artificial neural network was applied to optimize the prepared condition of the composite film. Corrosion behavior of the NiP/TiO2 composite film was investigated by polarization resistance measurement, anode polarization, ESEM （environmental scanning electron microscopy） and EIS （electrochemical impedance spectroscopy） measurements. Results showed that the NiP/ TiO2 composite film has a good corrosion resistance in 0.5mol/L H2SO4 solution. The element valence of the composite film was characterized by XPS （X-ray photoelectron spectroscopy） spectrum, and an anticorrosion mechanism of the composite film was discussed.
基金supported by the Jiangsu Key Laboratory for Materials Tribology (No.kjsmcx0901)
文摘The effect of nanodiamond content in electrolyte and rotational speed of the stirrer on the deposition rate of coatings, the nanodiamond content in coatings, the micro- structure and the micro-hardness of coatings were studicd. A self-made pin-on-disk tribo-meter was employed to evaluate the wear resistance of prepared coatings. Re- sults show that the thickness of composite coating decreases with the rotational speed, while the micro hardness of coating and the content of nanodiamond in coating increase with increasing its content in electrolyte. The wear resistance of the composite coating deposited in an electrolye with 6 g/L nanodiamond increases by 50% in contrast with the pure Ni-P coating.