Effects of current density on preparation of grainy electrolytic manganese dioxide 被引量:1
1
作者 郭华军 朱炳权 +4 位作者 李新海 张新明 王志兴 彭文杰 刘鲁平 《Journal of Central South University of Technology》 EI 2005年第6期667-670,共4页
Grainy electrolytic manganese dioxide was prepared by electrodeposition in a 0.9 mol/L MnSO4 and 2.5 mol/LH2SO4 solution. The structure, particle size and appearance of the grainy electrolytic manganese dioxide were d... Grainy electrolytic manganese dioxide was prepared by electrodeposition in a 0.9 mol/L MnSO4 and 2.5 mol/LH2SO4 solution. The structure, particle size and appearance of the grainy electrolytic manganese dioxide were determined by powder X-ray diffraction, laser particle size analysis and scanning electron micrographs measurements. Current density has important effects on cell voltage, anodic current efficiency and particle size of the grainy electrolytic manganese dioxide, and the optimum current density is 30 A/dm2. The grainy electrolytic manganese dioxide electrodeposited under the optimum conditions consists of γ-MnO2 with an orthorhombic lattice structure; the grainy electrolytic manganese dioxide has a spherical or sphere-like appearance and a narrow particle size distribution with an average particle diameter of 7.237 μm. 展开更多
关键词 alkaline batteries electrolytic manganese dioxide current density ELECTRODEPOSITION
下载PDF
Effects of temperature and concentration of sulfuric acid on the electrodeposition of grainy electrolytic manganese dioxide
2
作者 Huajun Guo Xinhai Li Luping Liu Xinming Zhang Zhixing Wang Wenjie Peng Bingquan Zhu 《Journal of University of Science and Technology Beijing》 CSCD 2005年第6期553-557,共5页
The effects of temperature and the concentration of sulfuric acid on the cell voltage, the anode current efficiency of electrodeposition and the particle size of grainy electrolytic manganese dioxide (EMD) were inve... The effects of temperature and the concentration of sulfuric acid on the cell voltage, the anode current efficiency of electrodeposition and the particle size of grainy electrolytic manganese dioxide (EMD) were investigated. The structure, particle size and appearance of grainy EMD were determined by powder X-ray diffraction, laser particle size analysis and scanning electron micrograph measurements. As the concentration of sulfuric acid increases, both the cell voltage and the average anode current efficiency decrease. With the increase of electrolysis temperature in the range of 30-60℃, the cell voltage, average anode current efficiency and particle size decrease. The optimum temperature of 30℃ and concentration of sulfuric acid of 2.5 mol/L for electrodeposition of the grainy EMD were obtained. XRD patterns show that the grainy EMD electrodeposited under the optimum conditions consists of γ-MnO2 and has an orthorhombic lattice structure. According to the results of SEM, the grainy EMD has a spherical or sphere-like appearance and a narrow particle size distribution with an average size of about 7μm. The grainy EMD is a promising cathode of rechargeable alkaline batteries for high energy density and a prospective precursor for production of the LiMn2O4 cathode of lithium ion batteries. 展开更多
关键词 alkaline batteries electrolytic manganese dioxide TEMPERATURE sulfuric acid ELECTRODEPOSITION
下载PDF
Preparation of MnO_2 and calcium silicate hydrate from electrolytic manganese residue and evaluation of adsorption properties 被引量:7
3
作者 李昌新 钟宏 +3 位作者 王帅 薛建荣 武芳芳 张振宇 《Journal of Central South University》 SCIE EI CAS CSCD 2015年第7期2493-2502,共10页
Electrolytic manganese residue(EMR), a high volume byproduct resulting from the electrolytic manganese industry, was used as a cheap and abundant chemical source for preparing MnO2 and EMR-made calcium silicate hydrat... Electrolytic manganese residue(EMR), a high volume byproduct resulting from the electrolytic manganese industry, was used as a cheap and abundant chemical source for preparing MnO2 and EMR-made calcium silicate hydrate(EMR-CSH). The MnO2 is successfully synthesized from the metal cations extracted from EMR, which can effectively recycle the manganese in the EMR. By the combination of XRD, SEM and EDX analysis, the as-prepared MnO2 is found to exhibit a single-phase with the purity of 90.3%. Furthermore, EMR-CSH is synthesized from EMR via hydrothermal method. Based on the detailed analyses using XRD, FT-IR, FE-SEM, EDX and BET surface area measurement, the product synthesized under the optimum conditions(p H 12.0 and 100 °C) is identified to be a calcium silicate hydrate with a specific surface area of 205 m2/g incorporating the slag-derived metals(Al and Mg) in its structure. The as-synthesized material shows good adsorption properties for removal of Mn2+ and phosphate ions diluted in water, making it a promising candidate for efficient bulk wastewater treatment. This conversion process, which enables us to fabricate two different kinds of valuable materials from EMR at low cost and through convenient preparation steps, is surely beneficial from the viewpoint of the chemical and economical use of EMR. 展开更多
关键词 electrolytic manganese residue manganese dioxide calcium silicate hydrate adsorption
下载PDF
Flexible Zinc-Manganese Dioxide Alkaline Batteries Based on Kelp Electrolytes 被引量:2
4
作者 Shuyang Wang Xiayue Fan 《Journal of Materials Science and Chemical Engineering》 2019年第12期19-28,共10页
Flexible energy-storage devices play a critical role in the development of portable, flexible and wearable electronics. In addition, biological materials including plants or plant-based materials are known for their s... Flexible energy-storage devices play a critical role in the development of portable, flexible and wearable electronics. In addition, biological materials including plants or plant-based materials are known for their safety, biodegradability, biocompatibility, environmental benignancy, and low cost. With respect to these advances, a flexible alkaline zinc-manganese dioxide (Zn-MnO2) battery is fabricated with a kelp-based electrolyte in this study. To the best of our knowledge, pure kelp is utilized as a semi-solid electrolyte for flexible Zn-MnO2 alkaline batteries for the first time, with which the as-assembled battery exhibited a specific capacity of 60 mA&#183;h and could discharge for 120 h. Furthermore, the as-assembled Zn-MnO2 battery can be bent into a ring-shape and power a light-emitting diode screen, showing promising potential for the practical application in the future flexible, portable and biodegradable electronic devices. 展开更多
关键词 Zinc-manganese dioxide BATTERY FLEXIBLE BATTERY Kelp-Based ELECTROLYTE
下载PDF
Reductive recovery of manganese from low-grade manganese dioxide ore using toxic nitrocellulose acid wastewater as reductant
5
作者 Yong-tao Zhang Zhi-gang Dan +1 位作者 Ning Duan Bao-ping Xin 《International Journal of Minerals,Metallurgy and Materials》 SCIE EI CAS CSCD 2018年第9期990-999,共10页
The hydrometallurgical strategy of extracting Mn from low-grade Mn ores has attracted attention for the production of electrolytic manganese metal(EMM). In this work, the reductive dissolution of low-grade Mn O2 ores ... The hydrometallurgical strategy of extracting Mn from low-grade Mn ores has attracted attention for the production of electrolytic manganese metal(EMM). In this work, the reductive dissolution of low-grade Mn O2 ores using toxic nitrocellulose acidic wastewater(NAW) as a reductant was investigated for the first time. Under the optimized conditions of an Mn O2 ore dosage of 100 g·L-1, an ore particle size of-200 mesh, concentrated H2 SO4-to-NAW volume ratio of 0.12, reaction temperature of 90°C, stirring speed at 160 r·min-1, and a contact time of 120 min, the reductive leaching efficiency of Mn and the total organic carbon(TOC) removal efficiency of NAW reached 97.4% and 98.5%, respectively. The residual TOC of 31.6 mg·L-1 did not adversely affect the preparation of EMM. The current process offers a feasible route for the concurrent realization of the reductive leaching of Mn and the treatment of toxic wastewater via a simple one-step process. 展开更多
关键词 LOW-GRADE manganese dioxide ORE NITROCELLULOSE ACID wastewater sulfuric ACID leaching Mn REDUCTIVE dissolution electrolytic manganese metal
下载PDF
锰氧化物正极材料的低温焙烧制备及电化学性能
6
作者 刘宝成 陈思含 +2 位作者 黄燕 熊利芝 向延鸿 《精细化工》 EI CAS CSCD 北大核心 2024年第9期1919-1924,1948,共7页
以电解锰阳极泥(EMAM)为原料,利用焙烧活化法制备了水系锌离子电池(AZIBs)锰氧化物正极材料,通过XRD、TGA、SEM及电化学性能测试考察了氮气氛围下,不同焙烧温度(300、425、575℃)对锰氧化物正极材料的结构、形貌及电化学性能的影响。结... 以电解锰阳极泥(EMAM)为原料,利用焙烧活化法制备了水系锌离子电池(AZIBs)锰氧化物正极材料,通过XRD、TGA、SEM及电化学性能测试考察了氮气氛围下,不同焙烧温度(300、425、575℃)对锰氧化物正极材料的结构、形貌及电化学性能的影响。结果表明,氮气氛围下焙烧提高了锰氧化物正极材料的衍射峰强度和结晶度,材料呈现出片状和颗粒状形态,团聚现象减少,空隙增加;随着焙烧温度的提高,锰氧化物正极材料物相逐渐从α-MnO_(2)转变为Mn_(2)O_(3)与Mn_(3)O_(4);焙烧使锰氧化物正极材料的首次放电比容量、倍率性能和循环性能得到提升,材料具有较小的瓦尔堡系数和更快的Zn^(2+)扩散速度。其中,焙烧温度300℃制备的锰氧化物正极材料(300-EMAM)表现出更好的电化学性能,在5 C倍率下,300-EMAM的初始放电比容量为232 mA·h/g,循环100圈后仍能保持190 mA·h/g的放电比容量;300-EMAM电极具有较低的接触电阻(33.6Ω)和电荷转移电阻(816.3Ω)。 展开更多
关键词 水系锌离子电池 正极材料 二氧化锰 电解锰阳极泥 功能材料
下载PDF
基于响应面法优化同槽电积锰和二氧化锰工艺研究
7
作者 张悦 宋小三 《有色金属工程》 CAS 北大核心 2024年第2期41-48,共8页
针对目前生产锰和电解二氧化锰行业能耗大、污染严重的问题,设计了一种同槽电沉积锰和二氧化锰工艺,在提高阴阳极电流效率的同时使得能耗最低,达到节能降耗的目的。结合响应面法对阴极硫酸铵浓度、阳极硫酸浓度、中隔室硫酸浓度、温度... 针对目前生产锰和电解二氧化锰行业能耗大、污染严重的问题,设计了一种同槽电沉积锰和二氧化锰工艺,在提高阴阳极电流效率的同时使得能耗最低,达到节能降耗的目的。结合响应面法对阴极硫酸铵浓度、阳极硫酸浓度、中隔室硫酸浓度、温度四个因素与阴阳极电沉积效率之间的交互作用进行分析,得到二次回归拟合模型,确定同槽电积的最佳条件为:阴极硫酸铵浓度为107.11 g/L,阳极硫酸浓度投加量为2.8 mol/L,中隔室硫酸浓度为0.516%,温度为40.2℃。阴极电流效率可达到84.79%、阳极电流效率可达到68.43%。分析表明,硫酸铵和温度对阴极电流效率交互影响最大、硫酸浓度和温度对阳极电流效率交互影响最大。电沉积得到的金属锰沉积紧密。电解二氧化锰粒径均一,形貌良好。 展开更多
关键词 同槽电积 电解二氧化锰 响应面法
下载PDF
两种不同锰源制备锰酸锂实验研究
8
作者 詹海青 李海亮 +1 位作者 潘妮东 李华成 《中国锰业》 2024年第1期1-5,共5页
电解二氧化锰和四氧化三锰是当前制备锰酸锂的两大锰源,分别以电解二氧化锰和球形四氧化三锰为原料,采用高温固相法来制备锰酸锂,并对锰酸锂的理化性能及电性能进行了对比分析。结果表明,烧结温度为760℃时,以球形四氧化三锰为原料制备... 电解二氧化锰和四氧化三锰是当前制备锰酸锂的两大锰源,分别以电解二氧化锰和球形四氧化三锰为原料,采用高温固相法来制备锰酸锂,并对锰酸锂的理化性能及电性能进行了对比分析。结果表明,烧结温度为760℃时,以球形四氧化三锰为原料制备的锰酸锂的性能较好,粒度D 50为15.182μm,振实密度为2.39 g/cm^(3),比表面积为0.289 cm^(2)/g,放电容量为111.65 mAh/g,50次循环容量保持率为95.71%。 展开更多
关键词 四氧化三锰 电解二氧化锰 锰酸锂 理化性能 电性能
下载PDF
电感耦合等离子体发射光谱法(ICP-OES)检测电解二氧化锰痕量杂质时基体效应影响的研究
9
作者 张修华 苏广源 +3 位作者 李坚 韦秋宋 黄小波 陈奇志 《中国锰业》 2024年第1期31-39,43,共10页
电解二氧化锰有去极化作用,作为正极活性物质可有效提高放电容量,其质量的优劣对电池性能至关重要。随着电池生产销售在2006年实现无汞化,电池中不再含有能屏蔽重金属的腐蚀、减少自放电的汞齐,多数电池用电解二氧化锰要求铁、钴、镍、... 电解二氧化锰有去极化作用,作为正极活性物质可有效提高放电容量,其质量的优劣对电池性能至关重要。随着电池生产销售在2006年实现无汞化,电池中不再含有能屏蔽重金属的腐蚀、减少自放电的汞齐,多数电池用电解二氧化锰要求铁、钴、镍、钒、铅、铜、钼、砷、锑含量低于一定限值,以防止这些有害金属杂质引起电池内部自放电、气涨、枝晶穿刺隔膜和漏液等不良反应。这些有害金属杂质常使用电感耦合等离子体发射光谱法(ICP-OES)同时进行分析,方法精确度高、分析速度快,但操作过程中受到基体效应干扰严重,尤其当杂质元素含量低至痕量范围内时,干扰信号可能会增强、削弱或覆盖待测元素信号,造成检测结果不准确。研究以SPECTRO ARCOS型号ICP-OES光谱仪为例,结合仪器特性和实际工作经验,对检测过程中出现的干扰特点进行分析,探讨基体效应消除或扣除的方法,以保障检测结果的准确性。 展开更多
关键词 电解二氧化锰 电感耦合等离子体发射光谱仪 基体效应 痕量
下载PDF
蔗渣白泥在电解二氧化锰生产中资源化利用研究进展
10
作者 朱甜甜 陆宾 叶有明 《广州化工》 CAS 2024年第1期4-6,共3页
蔗渣白泥是甘蔗渣制浆造纸产生的固体废弃物,主要成分是碳酸钙和少量的无机盐、有机杂质等,对蔗渣白泥的综合利用是广西蔗渣造纸行业面临的难题。从蔗渣白泥的主要来源、成分及当前主要用途进行分析,并对蔗渣白泥在电解二氧化锰行业中... 蔗渣白泥是甘蔗渣制浆造纸产生的固体废弃物,主要成分是碳酸钙和少量的无机盐、有机杂质等,对蔗渣白泥的综合利用是广西蔗渣造纸行业面临的难题。从蔗渣白泥的主要来源、成分及当前主要用途进行分析,并对蔗渣白泥在电解二氧化锰行业中应用的可能性及需要解决的关键问题进行综述,为蔗渣白泥在电解二氧化锰行业实现资源化利用提出了有效途径。 展开更多
关键词 蔗渣白泥 电解二氧化锰 碳酸钙 资源化利用 硫酸锰溶液
下载PDF
单膜双室电沉积金属锰联产EMD的影响因素
11
作者 宋小三 申庆超 +1 位作者 王三反 郑洋洋 《兰州交通大学学报》 CAS 2023年第6期81-90,共10页
针对传统膜电解法单独电解金属锰或电解二氧化锰(EMD)工艺存在资源利用率低、污染环境的问题,采用单膜双室电解法将金属锰与EMD进行同槽电解,且在阳极回收硫酸,并考察了阴极液硫酸铵浓度、电解液Mn^(2+)浓度、阳极液初始硫酸浓度、电流... 针对传统膜电解法单独电解金属锰或电解二氧化锰(EMD)工艺存在资源利用率低、污染环境的问题,采用单膜双室电解法将金属锰与EMD进行同槽电解,且在阳极回收硫酸,并考察了阴极液硫酸铵浓度、电解液Mn^(2+)浓度、阳极液初始硫酸浓度、电流密度4个因素对电沉积效果的影响。结果表明:在阴极液硫酸铵浓度为120 g/L、电解液Mn^(2+)浓度为40 g/L、阳极液初始硫酸浓度为0.6 mol/L、阴阳两极的电流密度分别为400 A/m^(2)和800 A/m^(2)的条件下,进行6 h电解,得到阴极锰产率可达78.22%,酸回收率为62.41%,EMD产率为23.7%,电能消耗仅为5675 kW·h/t,槽电压为5.86 V。同时发现对锰产率影响最显著的因素是电流密度,对EMD产率及酸回收率影响最显著的因素是阳极液初始硫酸浓度和电流密度。在最佳实验条件下的阴极产品金属锰板表面光洁密实、具明显银白色金属光泽、晶粒分层聚集、颗粒粒度均一、并呈现蜂窝状组织,整体形态良好。 展开更多
关键词 金属锰 单膜双室 同槽电解 电解二氧化锰 含锰废水
下载PDF
电解二氧化锰行业“前消后用”固废资源化应用发展策略 被引量:2
12
作者 全军 蓝晗兮 +5 位作者 黄先碧 吴勇 喻林萍 陈奇志 王智青 黄中伟 《中国锰业》 2023年第2期7-12,共6页
基于电解二氧化锰(EMD)生产工艺特征,提出从前端消纳蔗渣造纸白泥到末端锰渣进一步资源化利用的“前消后用”固废高值化应用策略。在EMD生产制液工序中以蔗渣造纸白泥替代石灰,并对蔗渣造纸白泥引入的杂质进行针对性地去除,从而避免影... 基于电解二氧化锰(EMD)生产工艺特征,提出从前端消纳蔗渣造纸白泥到末端锰渣进一步资源化利用的“前消后用”固废高值化应用策略。在EMD生产制液工序中以蔗渣造纸白泥替代石灰,并对蔗渣造纸白泥引入的杂质进行针对性地去除,从而避免影响硫酸锰溶液的净化流程以及EMD产品的品质,在消纳了固废蔗渣造纸白泥的同时也较显著地节约了EMD生产成本。对EMD工业中产生的锰渣固废进行资源化利用,获得水泥混合材添加剂和磷酸锰铁锂基正极材料等新产品,有效地解决蔗渣造纸企业和电解二氧化锰企业固废大量堆积的困扰,同时对其他行业推进固废资源的规模化、高值化利用具有参考意义。 展开更多
关键词 蔗渣白泥 电解二氧化锰 锰渣 固废 资源化利用
下载PDF
电解二氧化锰(EMD)粉体流动性试验研究
13
作者 张学英 马靖威 +2 位作者 马春玉 王红伟 阎安澜 《中国锰业》 2023年第2期35-41,共7页
以EMD粉体为研究对象,借助HORIBA粒度分布测试仪、BT-1001粉体流动性能测试仪,进行粉体流动性表征评价。通过表征得到粉体物性参数与流动性参数之间的函数关系,发现粉体物性对压缩性、流动性的影响规律不同,构建了不同流动性参数间的关... 以EMD粉体为研究对象,借助HORIBA粒度分布测试仪、BT-1001粉体流动性能测试仪,进行粉体流动性表征评价。通过表征得到粉体物性参数与流动性参数之间的函数关系,发现粉体物性对压缩性、流动性的影响规律不同,构建了不同流动性参数间的关联式,获得了休止角、流动性指数和喷流性指数的线性关系式,以期为EMD流动性和产品加工性能提供一种表征评价手段,对生产实践具有一定的指导作用。 展开更多
关键词 电解二氧化锰 粉体流动性 粉体物性 体止角
下载PDF
电解二氧化锰(EMD)铜阴极结晶发黑的机理分析和改善方法
14
作者 陈钊铭 吴云阳 +2 位作者 罗昌璃 李艳红 黄小广 《中国锰业》 2023年第3期95-97,共3页
电解二氧化锰(EDM)广泛应用于一次电池和二次电池,作为二次电池固相法工艺的锰源,EMD不仅对纯度与杂质有要求,同时还对颗粒形状、比表面积等有要求,整体工艺技术门槛较高,生产中出现的问题也较多。研究发现在EMD生产过程中,铜阴极易结... 电解二氧化锰(EDM)广泛应用于一次电池和二次电池,作为二次电池固相法工艺的锰源,EMD不仅对纯度与杂质有要求,同时还对颗粒形状、比表面积等有要求,整体工艺技术门槛较高,生产中出现的问题也较多。研究发现在EMD生产过程中,铜阴极易结晶发黑,结合EMD的电解生产工艺,分析铜阴极结晶发黑的原因,提出并实施相应的处理措施,改善铜阴极结晶发黑的现象。 展开更多
关键词 电解二氧化锰 铜阴极结晶发黑 改善研究
下载PDF
回收电解锰渣中的可溶性锰 被引量:23
15
作者 杜兵 周长波 +3 位作者 曾鸣 彭晓成 孟俊利 裴倩倩 《化工环保》 CAS CSCD 北大核心 2010年第6期526-529,共4页
以电解锰渣滤液为实验原料,研究了利用二氧化碳和氨水回收锰渣滤液中可溶性锰的工艺,实验结果表明:当n(氨水):n(可溶性锰)为2.50、二氧化碳曝气流量为50 L/h、曝气时间为5 min、振荡时间为60 min时,可溶性锰回收率达75%以上;对沉淀物进... 以电解锰渣滤液为实验原料,研究了利用二氧化碳和氨水回收锰渣滤液中可溶性锰的工艺,实验结果表明:当n(氨水):n(可溶性锰)为2.50、二氧化碳曝气流量为50 L/h、曝气时间为5 min、振荡时间为60 min时,可溶性锰回收率达75%以上;对沉淀物进行X射线衍射分析,碳酸锰纯度接近100%。1kg电解锰渣可回收27 mg碳酸锰。 展开更多
关键词 电解锰渣 可溶性锰 二氧化碳 曝气 氨水 碳酸锰 综合利用
下载PDF
电解液对水系可充电池MnO_2正极电化学性能的影响 被引量:7
16
作者 白守礼 李欣 +4 位作者 文越华 程杰 曹高萍 杨裕生 李殿卿 《物理化学学报》 SCIE CAS CSCD 北大核心 2016年第8期2007-2017,共11页
研究了水系电解液中Li^+、Zn^(2+)和Mn^(2+)阳离子对具有不同晶型结构和形貌的MnO_2正极电化学性能的影响,探讨其储能机理。结果表明,在不含Mn(Ⅱ)离子的水溶液中,MnO_2电极所表现的电化学性能趋同,容量低,衰减快。含有Zn^(2+)离子的水... 研究了水系电解液中Li^+、Zn^(2+)和Mn^(2+)阳离子对具有不同晶型结构和形貌的MnO_2正极电化学性能的影响,探讨其储能机理。结果表明,在不含Mn(Ⅱ)离子的水溶液中,MnO_2电极所表现的电化学性能趋同,容量低,衰减快。含有Zn^(2+)离子的水溶液中,MnO_2电极因二价锌离子的嵌入-脱出,容量明显提升,但衰减严重。当溶液中同时含有Zn^(2+)、Mn^(2+)离子时,基于Mn^(2+)和Zn^(2+)离子之间的协同作用和Mn^(2+)离子氧化/还原反应过程的作用,有效抑制MnO_2颗粒的聚集和结构塌陷,削弱碱式硫酸锌杂质不利的影响,保持了锌离子在MnO_2电极中嵌入-脱出的高容量特性(200 m Ah?g^(-1),电流密度:100m A?g^(-1)),及良好的循环稳定性。 展开更多
关键词 水系可充电池 MNO2 电解液 锌锰离子存储
下载PDF
掺铋电解二氧化锰可充性研究 被引量:10
17
作者 童庆松 甘晖 +1 位作者 连锦明 张其昕 《电池》 CAS CSCD 北大核心 1997年第1期14-17,共4页
利用日本TOYO SODA有限公司的粉状电解二氧化锰与含铋离子的溶液混合的物理方法制备掺铋的电解二氧化锰。掺铋样品的化学分析、循环伏安扫描及模拟电池的充放电实验表明:在浅度和深度放电时,掺杂样的充放电性能均有一定的改善,掺入的铋... 利用日本TOYO SODA有限公司的粉状电解二氧化锰与含铋离子的溶液混合的物理方法制备掺铋的电解二氧化锰。掺铋样品的化学分析、循环伏安扫描及模拟电池的充放电实验表明:在浅度和深度放电时,掺杂样的充放电性能均有一定的改善,掺入的铋对放电在—0.33V至—0.62V(vs.Hg/HgO)范围的二氧化锰可充性改善更加明显,充放电反应机理也有一定的改变。 展开更多
关键词 二氧化锰 电解二氧化锰 金属导电材料
下载PDF
电解二氧化锰对亚甲基蓝和甲基橙染料吸附性能的研究 被引量:11
18
作者 郝晓丹 魏杰 +1 位作者 张钱丽 王东田 《水处理技术》 CAS CSCD 北大核心 2013年第3期23-27,31,共6页
以电解二氧化锰(EMD)为吸附剂,分析了吸附剂投加量、pH和吸附时间等因素对EMD吸附亚甲基蓝(MB)和甲基橙(MO)的影响;亚甲基蓝是一种典型的阳离子型染料,性质很稳定;甲基橙是一种酸碱指示剂,分子中带有磺酸基-SO3-。结果表明,最佳吸附条... 以电解二氧化锰(EMD)为吸附剂,分析了吸附剂投加量、pH和吸附时间等因素对EMD吸附亚甲基蓝(MB)和甲基橙(MO)的影响;亚甲基蓝是一种典型的阳离子型染料,性质很稳定;甲基橙是一种酸碱指示剂,分子中带有磺酸基-SO3-。结果表明,最佳吸附条件为吸附MB和MO时EMD的最佳用量分别为33.33 g/g和55.56g/g,pH为2、吸附时间为300 min时吸附效果最好。EMD对MB和MO的吸附过程较符合Langmuir等温式和拟二级动力学方程,吸附速率常数分别为0.002 3和0.006 4 g/(mg.min)。EMD对染料的去除机理为吸附和氧化综合作用的结果。 展开更多
关键词 吸附 电解二氧化锰 亚甲基蓝 甲基橙
下载PDF
电解锰阳极泥的除杂活化及应用 被引量:13
19
作者 陶长元 李东海 +1 位作者 刘作华 邹开云 《电池》 CAS CSCD 北大核心 2011年第3期121-124,共4页
采用稀H2SO4[w(NaCl)=5%]酸浸处理后,电解锰阳极泥中的MnO2含量由42%-59%提高到87%-93%,MnO2的晶体结构得到改善、电化学性能提高。用所得MnO2制成的R20电池,3.9Ω、0.9 V连放时间超过290 min。
关键词 电解锰阳极泥 除杂 二氧化锰(MnO2) 锌锰干电池
下载PDF
改性电解二氧化锰研究 被引量:9
20
作者 袁国辉 褚德威 +2 位作者 申日辉 潘宏伟 张翠芬 《电化学》 CAS CSCD 1995年第4期446-450,共5页
用电解法制备一种掺杂铋的改性二氧化锰材料(Bi-EMD).通过x射线衍射及光电子能谱分析,Bi-EMD属于γ-MnO_2,Bi以Bi_2O_3形式存在于改性材料中,且材料中Bi含量随电解时Bi ̄(3+)浓度增加而增加... 用电解法制备一种掺杂铋的改性二氧化锰材料(Bi-EMD).通过x射线衍射及光电子能谱分析,Bi-EMD属于γ-MnO_2,Bi以Bi_2O_3形式存在于改性材料中,且材料中Bi含量随电解时Bi ̄(3+)浓度增加而增加.当电解液中Bi ̄(3+)浓度为0.008mol·L ̄(-1)时,材料中Bi含量高达14.3%(重量百分比).用Bi-EMD装配成AA型Zn/MnO_2试验电池.通过循环寿命实验,Bi-EMD表现出良好的可逆性. 展开更多
关键词 电解 二氧化锰 改性电极 碱锰电池
下载PDF