To achieve high microwave permeability in wide-band for the micron-thick magnetic films,[Fe-Fe_(20)Ni_(80)/Cr]_(n) multilayer structure was proposed by co-sputtering Fe and FeNi to form the magnetic layers and Cr to f...To achieve high microwave permeability in wide-band for the micron-thick magnetic films,[Fe-Fe_(20)Ni_(80)/Cr]_(n) multilayer structure was proposed by co-sputtering Fe and FeNi to form the magnetic layers and Cr to form the interlayers.The multilayer structure contributes to the high permeability by reducing the coercivity and diminishing out-of-plane magnetization.The maximum imaginary permeability of[Fe-Fe_(20)Ni_(80)/Cr]_(n) multilayer film reaches a large value of 800 at 0.52 GHz even though its overall thickness exceeds 1μm.Besides,the magnetic resonance frequency of the multilayer film can be modulated from 0.52 to 1.35 GHz by adjusting the sputtering power of Fe from 0 to 86 W,and its bandwidth for μ’’>200(Δf) is as large as 2.0 GHz.The desirable broad Δf of magnetic permeability,which can be well fitted by the Landau-Lifshitz-Gilbert equations,is due to dual magnetic resonances originated from double magnetic phases of Fe and FeNi that are of different saturation magnetization.The micron-thick multilayer films with high permeability in extended waveband are promising candidate for electromagnetic noise suppression application.展开更多
基金Funded by the Young Top-notch Talent Cultivation Program of Hubei Provincethe Fundamental Research Funds for the Central Universities(WUT:2021IVA116 and WUT:2021CG015)。
文摘To achieve high microwave permeability in wide-band for the micron-thick magnetic films,[Fe-Fe_(20)Ni_(80)/Cr]_(n) multilayer structure was proposed by co-sputtering Fe and FeNi to form the magnetic layers and Cr to form the interlayers.The multilayer structure contributes to the high permeability by reducing the coercivity and diminishing out-of-plane magnetization.The maximum imaginary permeability of[Fe-Fe_(20)Ni_(80)/Cr]_(n) multilayer film reaches a large value of 800 at 0.52 GHz even though its overall thickness exceeds 1μm.Besides,the magnetic resonance frequency of the multilayer film can be modulated from 0.52 to 1.35 GHz by adjusting the sputtering power of Fe from 0 to 86 W,and its bandwidth for μ’’>200(Δf) is as large as 2.0 GHz.The desirable broad Δf of magnetic permeability,which can be well fitted by the Landau-Lifshitz-Gilbert equations,is due to dual magnetic resonances originated from double magnetic phases of Fe and FeNi that are of different saturation magnetization.The micron-thick multilayer films with high permeability in extended waveband are promising candidate for electromagnetic noise suppression application.