The effect of water content on the electrorheological effect (ERE) behaviour of silica dispersions has been investigated. The types of silica powders were fumed silica, precipitated and acid washed silica and colloida...The effect of water content on the electrorheological effect (ERE) behaviour of silica dispersions has been investigated. The types of silica powders were fumed silica, precipitated and acid washed silica and colloidal silica. Silica dispersions with a water content varying in the range 10% - 30%, and with conducting ions deliberately added, were redispersed in chlorinated hydrocarbon oil and then the ER behaviour studied. Samples were tested on a static yield rig (SYR), an instrument which can measure both the yield stress and the conductivity. The effects of electric field strength and water content on the ERE were studied. The yield stress initially increased with increase in electric field strength and then decreased at high electric fields suggesting a breakdown in structure of the electrorheological fluid samples tested. It was also found that the ERE increased and electric saturation or electric breakdown shifted to lower electric fields as the water content increased. Higher electric fields caused a drop in the ERE.展开更多
Exposing waxy oils to an electric field may significantly improve their cold flowability.Our previous study has shown that interfacial polarization,i.e.,charged particle accumulation on the wax particle surface,is the...Exposing waxy oils to an electric field may significantly improve their cold flowability.Our previous study has shown that interfacial polarization,i.e.,charged particle accumulation on the wax particle surface,is the primary mechanism of the electrorheological behavior of waxy oils.However,the way that charged particles interact with wax particles under an electric field remains unknown.In this study,we found no viscosity and impedance change for two waxy crude oils after their exposure to a high-voltage electric field.However,the yield stresses were reduced obviously.We thus proposed that the collision of colloidal particles such as resins and asphaltenes with the wax particles could be an essential mechanism that the wax particle structure was weakened.To verify this hypothesis,a series of ad hoc experiments were carried out,i.e.,by performing electrorheological tests on model waxy oils containing additives removable under an electric field,including electrically-neutral colloidal particles(Fe3O4),charged colloidal particles(resins),and oil-soluble electrolyte(C22H14CoO4),respectively,and demonstrated that upon application of a high-voltage electric field,charged particles in a waxy oil may move and thus collide with wax particles,and consequently adhere to the wax particle surface.The particle collision results in damage to the wax particle network,and the electrostatic repulsion arising from the adhesion of the charged particle on the wax particle diminishes attraction between wax particles.This study clarifies the process of interfacial polarization.展开更多
Traditional dielectric electrorheological fluid(ER)is based on the interaction of dielectric particle polarization,and the yield stress is low,which cannot meet the application requirements.The giant ER(GER)effect is ...Traditional dielectric electrorheological fluid(ER)is based on the interaction of dielectric particle polarization,and the yield stress is low,which cannot meet the application requirements.The giant ER(GER)effect is caused by orientations and interactions of polar molecules adsorbed on the particle surfaces.Despite the high yield stress,these polar molecules are prone to wear and fall off,resulting in a continuous reduction in shear stress of GER liquid,which is also not suitable for application.Here we introduce a new type of ER fluid called induced dipole dominant ER fluid(ID-ER),of which the particles contain oxygen vacancies or conductor microclusters both prepared by high energy ball milling(HEBM)technique.In the electric field E,oxygen vacancies or conductor microclusters form induced dipoles.Because the local electric field E_(loc) in the gaps between particles can be two to three orders of magnitude larger than E,the induced dipole moments must be large.The strong interactions of these induced dipoles make the yield stress of the ID-ER fluid reaching more than 100 kPa.Since there are oxygen vacancies or conductor microclusters everywhere in the particles,the particles will not lose the function due to surface wear during use.The experimental results show that the ID-ER fluid possesses the advantages of high shear stress,low current density,short response time,good temperature stability,long service life,and anti-settlement,etc.The comprehensive performance is much better than the existing ER materials,and also the preparation method is simple and easy to repeat,thus it should be a new generation of ER fluid suitable for practical applications.展开更多
Electrorheological (ER) properties of polyaniline (PAni), pumice and polyaniline/pumice composites (PAPC) were investigated. Polyaniline and PAni/pumice composite were prepared by oxidative polymerization. PAni/...Electrorheological (ER) properties of polyaniline (PAni), pumice and polyaniline/pumice composites (PAPC) were investigated. Polyaniline and PAni/pumice composite were prepared by oxidative polymerization. PAni/pumice particlesbased ER suspensions were prepared in silicone oil (SO), and their ER behavior was investigated as a function of shear rate, electric field strength, concentration and temperature. Sedimentation stabilities of suspensions were determined. It has been found that ER activity of all the suspensions increases with increasing electric field strength, concentration and decreasing shear rate. It has shown that the suspensions have a typical shear thinning non-Newtonian viscoelastic behavior. Yield stress of composite suspensions increased linearly with increasing applied electric field strength and with concentrations of the particles. The effect of high temperature on ER activity of purrfice/silicone oil systems was also investigated.展开更多
The problem of electrorheological(ER) technology’s application in the vibration isolation system is emphatically studied. Based on the particular characteristics of the electrorheological fluid (ERF) tunable damping,...The problem of electrorheological(ER) technology’s application in the vibration isolation system is emphatically studied. Based on the particular characteristics of the electrorheological fluid (ERF) tunable damping, a metal-spring ER isolator is designed and its working principle is mainly discussed. By theoretical analysis of its simplified physical model, the dynamic response of an ER isolator is sensitive to the system equivalent spring stiffness K and ERF damping coefficient C. According to the dynamic performance tests, the result confirms that applying different electric field strength can change the dynamic peculiarity of the metal-spring ER isolator. The configuration design parameters of the ER equipment, such as the stiffness ratio of two fluid chambers and the size of the electric field, are important factors for the tunable range of ER isolator.展开更多
The electrorheological properties of CaO–SiO2–Al2O3–MgO–TiO2–Ti C slags were investigated to enhance understanding of the effect of TiC addition on the viscosity, yield stress, and fluid pattern of Ti-bearing sla...The electrorheological properties of CaO–SiO2–Al2O3–MgO–TiO2–Ti C slags were investigated to enhance understanding of the effect of TiC addition on the viscosity, yield stress, and fluid pattern of Ti-bearing slags in a direct-current electric field. The viscosities and shear stresses of 4wt% and 8wt% Ti C slags were found to increase substantially with increasing electric field intensity, whereas virtually no rheological changes were observed in the 0wt% TiC slag. The Herschel–Bulkley model was applied to demonstrate that the fluid pattern of the 4wt% TiC slag was converted from that of a Newtonian fluid to that of a Bingham fluid in response to the applied electric field; and the static yield stress increased linearly with the square of the electric field intensity.展开更多
The yield stress of our newly developed electrorheological (ER) fluids consisting of dielectric nano-particles suspended in silicone oil reaches hundreds of kPa, which is orders of magnitude higher than that of conv...The yield stress of our newly developed electrorheological (ER) fluids consisting of dielectric nano-particles suspended in silicone oil reaches hundreds of kPa, which is orders of magnitude higher than that of conventional ones. We found that the polar molecules adsorbed on the particles play a decisive role in such new ER fluids. To explain this polar molecule dominated ER (PM-ER) effect a model is proposed based on the interaction of polar molecule-charge between the particles, where the local electric field is significantly enhanced and results in the polar molecules aligning in the direction of the electric field. The model can well explain the giant ER effect and a near-linear dependence of the yield stress on the electric field. The main effective factors for achieving high-performance PM-ER fluids are discussed. The PM-ER fluids with the yield stress higher than one MPa can be expected.展开更多
We have prepared novel coated particles, with a conductor graphite core and a dielectric TiO2 coating, as the dispersed phase of electrorheological fluids. One order of magnitude enhancement in the shear stress is obt...We have prepared novel coated particles, with a conductor graphite core and a dielectric TiO2 coating, as the dispersed phase of electrorheological fluids. One order of magnitude enhancement in the shear stress is obtained by using such composite particles, when it is compared with that of TiO2 particles. The experimental results show a way to get excellent ER system.展开更多
A new class of electrorheological (ER) material using rare earth (RE = Y) oxide as the substrate, NaNO3- doped Y2O3 materials, were synthesized using Na2CO3 and Y(NO3)3 as starting materials. Their ER performanc...A new class of electrorheological (ER) material using rare earth (RE = Y) oxide as the substrate, NaNO3- doped Y2O3 materials, were synthesized using Na2CO3 and Y(NO3)3 as starting materials. Their ER performance, dielectric property, and crystal structure were studied. The results show that doping NaNO3 can markedly enhance the ER activity of the Y2O3 material. For the suspensions of these materials in dimethyl silicone oil, a clear dependence of the shear stress on the doping degree of NANO3 was observed, and the optimal value of Na/Y molar ratio of 0.6 in doping degree was discovered, the relative viscosity ηr( ηE/η0, E = 4.2 kV·mm^-1) of the suspensions is nine times higher than that of pure Y2O3 material. The new results of the relationship between ER effect and the microstructure were obtained, which are helpful for further understanding the mechanism of ER effect and synthesizing a good ER material.展开更多
Nano-SiOdoped with rare earth carboxylate grafting continuous component of functional poly-silicone liquid, a kind of subsidence high-resistance. Electrorheological fluid (ERF) was synthesized. And its viscoelastic pr...Nano-SiOdoped with rare earth carboxylate grafting continuous component of functional poly-silicone liquid, a kind of subsidence high-resistance. Electrorheological fluid (ERF) was synthesized. And its viscoelastic properties were investigated experimentally. The special polarization effect of rare earth in the ERF was also discussed. The forced oscillating behavior was obtained using a rheometer. The variation of the shear modulus of ERF subjected to various stress amplitude and frequency were investigated. The complex shear modulus and storage modulus of ERF were also given at different electric field intensities. Meanwhile, the creep and recovery characteristics of ERF were also measured. The equilibrium compliance Jc and the steady state recoverable compliance JR were investigated as a function of electric field strength and ratio of reactant, and the effect of ERF′s structure was analyzed. With increasing in electric field strength at fixed ratio of reactant, the plastic response diminishes, and the elastic behavior rose.展开更多
According to the results of experiments and theoretical analysis, a phenomenon called "capture effect" is put forward, which could be used to describe the particles dynamic behavior of electrorheological (ER) susp...According to the results of experiments and theoretical analysis, a phenomenon called "capture effect" is put forward, which could be used to describe the particles dynamic behavior of electrorheological (ER) suspensions. Then a "structure-force" mathematical model is established to explain this effect based on electrostatic energy density equation. The analysis results show that the dynamic coupling process of ER suspensions under an external electric filed is the function not only of the electric intensity, but also of the dielectric properties and the structure form.展开更多
The structure transitions in cluster-cluster aggregation (CCA) and diffusion-limited aggregation (DLA) under external electric fields have been investigated by computer simulations. With the increase of external elect...The structure transitions in cluster-cluster aggregation (CCA) and diffusion-limited aggregation (DLA) under external electric fields have been investigated by computer simulations. With the increase of external electric field, there exists a structure transition from disorder to order, i. e., the aggregates change from fractals of diffusion-limited CCA and DLA to the electrorheological chains parallel to electric field. Pair distribution shows, the system changes from local order to long-range order gradually with the external field rising.展开更多
The new electrorheologicai (ER) material, a particle material composed of Y4O(OH)9(NO3) and NH4NO3, was obtained. They display better ER performance. The shear stress of the suspension of Y4O (OH)9 (NO3) ( ...The new electrorheologicai (ER) material, a particle material composed of Y4O(OH)9(NO3) and NH4NO3, was obtained. They display better ER performance. The shear stress of the suspension of Y4O (OH)9 (NO3) ( NH4NO3 )2.8 material in dimethyl silicone oil reaches 1469 Pa at an electric field strength (E) of 4.2 kV·mm^-1 and the shear rate (7) of 150 s^-1 The relative shear stress, τ E/τ0( τE and τ0 are the shear stresses at E = 4.2 and 0 kV·mm^-1 respectively), is up to 29, which is 19 times that of pure Y2O3 material. The dielectric and conductive property of the materials play important roles in the modification of the ER effect of the particle materials. The researches on these new ER materials are very useful for obtaining a better understanding on the mechanism of the ER effect and finding an ideal ER material.展开更多
By using oxalate group-modified TiO2 nanoparticles as the dispersing phase, different kinds of silicone oil with various viscosities and terminal groups(hydroxyl, hydrogen, and methyl) were used as the dispersing me...By using oxalate group-modified TiO2 nanoparticles as the dispersing phase, different kinds of silicone oil with various viscosities and terminal groups(hydroxyl, hydrogen, and methyl) were used as the dispersing media to prepare different electrorheological(ER) fluids. Their zero-field viscosity, yield stress under direct current electric fields, ER efficiency, shear stability, leakage current density, and sedimentation stability were tested to study the effect of carrier liquid on the properties of ER fluids. The results indicate that the zerofield viscosity, the yield stress, and the leakage current density increase with increasing viscosity of the silicone oils. The effects of the viscosity on the ER efficiency, the shear stability, and the sedimentation ratio depend on the competition between the viscous resistance and the aggregation of the particles. Among the three ER fluids prepared with silicone oil with different terminal groups, hydroxyl-terminated oil based sample has the highest zero-field viscosity, the highest field-induced yield stress and ER efficiency, the largest current density, and the best sedimentation stability.展开更多
Ethylene propylene diene elastomers (EPDM) of various side chains and molecular weights were prepared as thin discs and the effects of electric field strength and temperature on the electromechanical properties were i...Ethylene propylene diene elastomers (EPDM) of various side chains and molecular weights were prepared as thin discs and the effects of electric field strength and temperature on the electromechanical properties were investigated. The electrical conductivity, the dielectric constant, the storage and loss moduli (G' and G'), the storage modulus response (ΔG’1000 V/mm), and the storage modulus sensitivity (ΔG’1000 V/mm/G’0) of the elastomers of different ethylene norbornene (ENB) contents and molecular weights were measured under electric field strengths varying from 0 V/mm to 1000 V/mm and at temperatures between 300 K and 380 K. The storage modulus response and sensitivity increase with increasing molecular weight and dielectric constant, consistent with the existing theory. However, for the case of EPDMs with different ENB contents, the storage modulus response and sensitivity vary inversely with the dielectric constant. EDPM is potentially a new type of electroactive materials.展开更多
Based on a modified Maxwell-Wagner model,molecular dynamics is carried out to simulate the structural changes of ER(electrorheological) suspensions in a poiseuille flow field.The simulation results show that the flow ...Based on a modified Maxwell-Wagner model,molecular dynamics is carried out to simulate the structural changes of ER(electrorheological) suspensions in a poiseuille flow field.The simulation results show that the flow assists in the collection of particles at the electrodes under a low pressure gradient,and the negative ER effect will show under a high pressure gradient.By analyzing the relationship curves of the shear stress and the pressure gradient in different relaxation time,it is found that for the same kind of ER suspensions materials,there is an optimal dielectric relaxation frequency.展开更多
Zinc borate(ZB)particles dispersed in silicone oil(SO)at concentrations of φ=5vol%-20vol% were subjected to dielectric analysis to elucidate their polarization strength,time,and mechanism.Results revealed that all vi...Zinc borate(ZB)particles dispersed in silicone oil(SO)at concentrations of φ=5vol%-20vol% were subjected to dielectric analysis to elucidate their polarization strength,time,and mechanism.Results revealed that all virgin dispersions lacked polarization.Triton X-100,a non-ionic surfactant,was added to ZB/SO dispersions to enhance the polarizability of ZB particles.The addition of 1vol% Triton X-100 enhanced the polarizability of ZB/SO dispersions,and the 15vol% ZB/SO system provided the highest dielectric difference Δε′(the difference in ε′values at zero and infinite frequency,Δε′=ε0–ε∝)of 3.64.The electrorheological(ER)activities of the ZB/SO/Triton-X dispersion system were determined through the ER response test,and viscoelastic behaviors were investigated via oscillation tests.A recoverable deformation of 36% under an applied electrical field strength of 1.5 kV/mm was detected through creep and creep recovery tests.展开更多
Graphite/TiO2 composite particles were obtained by sol-gel technique in this paper. The structure and characteristic of the composite particles are analyzed by XRD, SEM and TG-DTA. The electrorheological properties of...Graphite/TiO2 composite particles were obtained by sol-gel technique in this paper. The structure and characteristic of the composite particles are analyzed by XRD, SEM and TG-DTA. The electrorheological properties of the ER fluid containing the particles were measured by a Couette-type rheometer under shear rates of 1-136 s-1 and AC electric fields of 0-3 kV/mm. The experimental results show that the leaking current density of the ER fluid is higher than that of pure titanium dioxide particles dispersed in damping oil. The shear yield stress of the ER fluid increases with increasing electric field and exhibits a typical Bingham flow behavior. The suspension demonstrates an excellent ER performance (τ/τo=1200) compared with conventional ER fluids (τ/τ0 ≤500). The sedimentation of the ER fluid is improved obviously due to the coating effect of the particles.展开更多
文摘The effect of water content on the electrorheological effect (ERE) behaviour of silica dispersions has been investigated. The types of silica powders were fumed silica, precipitated and acid washed silica and colloidal silica. Silica dispersions with a water content varying in the range 10% - 30%, and with conducting ions deliberately added, were redispersed in chlorinated hydrocarbon oil and then the ER behaviour studied. Samples were tested on a static yield rig (SYR), an instrument which can measure both the yield stress and the conductivity. The effects of electric field strength and water content on the ERE were studied. The yield stress initially increased with increase in electric field strength and then decreased at high electric fields suggesting a breakdown in structure of the electrorheological fluid samples tested. It was also found that the ERE increased and electric saturation or electric breakdown shifted to lower electric fields as the water content increased. Higher electric fields caused a drop in the ERE.
基金financial support from the National Natural Science Foundation of China(No.52174066,No.51534007).
文摘Exposing waxy oils to an electric field may significantly improve their cold flowability.Our previous study has shown that interfacial polarization,i.e.,charged particle accumulation on the wax particle surface,is the primary mechanism of the electrorheological behavior of waxy oils.However,the way that charged particles interact with wax particles under an electric field remains unknown.In this study,we found no viscosity and impedance change for two waxy crude oils after their exposure to a high-voltage electric field.However,the yield stresses were reduced obviously.We thus proposed that the collision of colloidal particles such as resins and asphaltenes with the wax particles could be an essential mechanism that the wax particle structure was weakened.To verify this hypothesis,a series of ad hoc experiments were carried out,i.e.,by performing electrorheological tests on model waxy oils containing additives removable under an electric field,including electrically-neutral colloidal particles(Fe3O4),charged colloidal particles(resins),and oil-soluble electrolyte(C22H14CoO4),respectively,and demonstrated that upon application of a high-voltage electric field,charged particles in a waxy oil may move and thus collide with wax particles,and consequently adhere to the wax particle surface.The particle collision results in damage to the wax particle network,and the electrostatic repulsion arising from the adhesion of the charged particle on the wax particle diminishes attraction between wax particles.This study clarifies the process of interfacial polarization.
基金Project supported by the National Key Research and Development Program of China(Grant No.2017YFA0403000)the National Natural Science Foundation of China(Grant No.11874430).
文摘Traditional dielectric electrorheological fluid(ER)is based on the interaction of dielectric particle polarization,and the yield stress is low,which cannot meet the application requirements.The giant ER(GER)effect is caused by orientations and interactions of polar molecules adsorbed on the particle surfaces.Despite the high yield stress,these polar molecules are prone to wear and fall off,resulting in a continuous reduction in shear stress of GER liquid,which is also not suitable for application.Here we introduce a new type of ER fluid called induced dipole dominant ER fluid(ID-ER),of which the particles contain oxygen vacancies or conductor microclusters both prepared by high energy ball milling(HEBM)technique.In the electric field E,oxygen vacancies or conductor microclusters form induced dipoles.Because the local electric field E_(loc) in the gaps between particles can be two to three orders of magnitude larger than E,the induced dipole moments must be large.The strong interactions of these induced dipoles make the yield stress of the ID-ER fluid reaching more than 100 kPa.Since there are oxygen vacancies or conductor microclusters everywhere in the particles,the particles will not lose the function due to surface wear during use.The experimental results show that the ID-ER fluid possesses the advantages of high shear stress,low current density,short response time,good temperature stability,long service life,and anti-settlement,etc.The comprehensive performance is much better than the existing ER materials,and also the preparation method is simple and easy to repeat,thus it should be a new generation of ER fluid suitable for practical applications.
基金This work was financially supported by the TUBITAK (Turkish Scientific and Technical Research Foundation)Süleyman Demirel University (Nos. TBAG-AY-344, SDU BAP 03-m-714)
文摘Electrorheological (ER) properties of polyaniline (PAni), pumice and polyaniline/pumice composites (PAPC) were investigated. Polyaniline and PAni/pumice composite were prepared by oxidative polymerization. PAni/pumice particlesbased ER suspensions were prepared in silicone oil (SO), and their ER behavior was investigated as a function of shear rate, electric field strength, concentration and temperature. Sedimentation stabilities of suspensions were determined. It has been found that ER activity of all the suspensions increases with increasing electric field strength, concentration and decreasing shear rate. It has shown that the suspensions have a typical shear thinning non-Newtonian viscoelastic behavior. Yield stress of composite suspensions increased linearly with increasing applied electric field strength and with concentrations of the particles. The effect of high temperature on ER activity of purrfice/silicone oil systems was also investigated.
基金Beijing Institute of Technology Science Foundation(000Y03)
文摘The problem of electrorheological(ER) technology’s application in the vibration isolation system is emphatically studied. Based on the particular characteristics of the electrorheological fluid (ERF) tunable damping, a metal-spring ER isolator is designed and its working principle is mainly discussed. By theoretical analysis of its simplified physical model, the dynamic response of an ER isolator is sensitive to the system equivalent spring stiffness K and ERF damping coefficient C. According to the dynamic performance tests, the result confirms that applying different electric field strength can change the dynamic peculiarity of the metal-spring ER isolator. The configuration design parameters of the ER equipment, such as the stiffness ratio of two fluid chambers and the size of the electric field, are important factors for the tunable range of ER isolator.
基金financially supported by the National Natural Science Foundation of China (Nos. 51174051 and 51090383)
文摘The electrorheological properties of CaO–SiO2–Al2O3–MgO–TiO2–Ti C slags were investigated to enhance understanding of the effect of TiC addition on the viscosity, yield stress, and fluid pattern of Ti-bearing slags in a direct-current electric field. The viscosities and shear stresses of 4wt% and 8wt% Ti C slags were found to increase substantially with increasing electric field intensity, whereas virtually no rheological changes were observed in the 0wt% TiC slag. The Herschel–Bulkley model was applied to demonstrate that the fluid pattern of the 4wt% TiC slag was converted from that of a Newtonian fluid to that of a Bingham fluid in response to the applied electric field; and the static yield stress increased linearly with the square of the electric field intensity.
文摘The yield stress of our newly developed electrorheological (ER) fluids consisting of dielectric nano-particles suspended in silicone oil reaches hundreds of kPa, which is orders of magnitude higher than that of conventional ones. We found that the polar molecules adsorbed on the particles play a decisive role in such new ER fluids. To explain this polar molecule dominated ER (PM-ER) effect a model is proposed based on the interaction of polar molecule-charge between the particles, where the local electric field is significantly enhanced and results in the polar molecules aligning in the direction of the electric field. The model can well explain the giant ER effect and a near-linear dependence of the yield stress on the electric field. The main effective factors for achieving high-performance PM-ER fluids are discussed. The PM-ER fluids with the yield stress higher than one MPa can be expected.
基金the National Natural Science Foundation of China! (No.19834020).
文摘We have prepared novel coated particles, with a conductor graphite core and a dielectric TiO2 coating, as the dispersed phase of electrorheological fluids. One order of magnitude enhancement in the shear stress is obtained by using such composite particles, when it is compared with that of TiO2 particles. The experimental results show a way to get excellent ER system.
文摘A new class of electrorheological (ER) material using rare earth (RE = Y) oxide as the substrate, NaNO3- doped Y2O3 materials, were synthesized using Na2CO3 and Y(NO3)3 as starting materials. Their ER performance, dielectric property, and crystal structure were studied. The results show that doping NaNO3 can markedly enhance the ER activity of the Y2O3 material. For the suspensions of these materials in dimethyl silicone oil, a clear dependence of the shear stress on the doping degree of NANO3 was observed, and the optimal value of Na/Y molar ratio of 0.6 in doping degree was discovered, the relative viscosity ηr( ηE/η0, E = 4.2 kV·mm^-1) of the suspensions is nine times higher than that of pure Y2O3 material. The new results of the relationship between ER effect and the microstructure were obtained, which are helpful for further understanding the mechanism of ER effect and synthesizing a good ER material.
基金NSF (50373034) Physics Chemistry National Key Subject Cultivation Point Grant of Jiangsu Province
文摘Nano-SiOdoped with rare earth carboxylate grafting continuous component of functional poly-silicone liquid, a kind of subsidence high-resistance. Electrorheological fluid (ERF) was synthesized. And its viscoelastic properties were investigated experimentally. The special polarization effect of rare earth in the ERF was also discussed. The forced oscillating behavior was obtained using a rheometer. The variation of the shear modulus of ERF subjected to various stress amplitude and frequency were investigated. The complex shear modulus and storage modulus of ERF were also given at different electric field intensities. Meanwhile, the creep and recovery characteristics of ERF were also measured. The equilibrium compliance Jc and the steady state recoverable compliance JR were investigated as a function of electric field strength and ratio of reactant, and the effect of ERF′s structure was analyzed. With increasing in electric field strength at fixed ratio of reactant, the plastic response diminishes, and the elastic behavior rose.
文摘According to the results of experiments and theoretical analysis, a phenomenon called "capture effect" is put forward, which could be used to describe the particles dynamic behavior of electrorheological (ER) suspensions. Then a "structure-force" mathematical model is established to explain this effect based on electrostatic energy density equation. The analysis results show that the dynamic coupling process of ER suspensions under an external electric filed is the function not only of the electric intensity, but also of the dielectric properties and the structure form.
文摘The structure transitions in cluster-cluster aggregation (CCA) and diffusion-limited aggregation (DLA) under external electric fields have been investigated by computer simulations. With the increase of external electric field, there exists a structure transition from disorder to order, i. e., the aggregates change from fractals of diffusion-limited CCA and DLA to the electrorheological chains parallel to electric field. Pair distribution shows, the system changes from local order to long-range order gradually with the external field rising.
文摘The new electrorheologicai (ER) material, a particle material composed of Y4O(OH)9(NO3) and NH4NO3, was obtained. They display better ER performance. The shear stress of the suspension of Y4O (OH)9 (NO3) ( NH4NO3 )2.8 material in dimethyl silicone oil reaches 1469 Pa at an electric field strength (E) of 4.2 kV·mm^-1 and the shear rate (7) of 150 s^-1 The relative shear stress, τ E/τ0( τE and τ0 are the shear stresses at E = 4.2 and 0 kV·mm^-1 respectively), is up to 29, which is 19 times that of pure Y2O3 material. The dielectric and conductive property of the materials play important roles in the modification of the ER effect of the particle materials. The researches on these new ER materials are very useful for obtaining a better understanding on the mechanism of the ER effect and finding an ideal ER material.
基金Funded by the National Natural Science Foundation of China(51478088)
文摘By using oxalate group-modified TiO2 nanoparticles as the dispersing phase, different kinds of silicone oil with various viscosities and terminal groups(hydroxyl, hydrogen, and methyl) were used as the dispersing media to prepare different electrorheological(ER) fluids. Their zero-field viscosity, yield stress under direct current electric fields, ER efficiency, shear stability, leakage current density, and sedimentation stability were tested to study the effect of carrier liquid on the properties of ER fluids. The results indicate that the zerofield viscosity, the yield stress, and the leakage current density increase with increasing viscosity of the silicone oils. The effects of the viscosity on the ER efficiency, the shear stability, and the sedimentation ratio depend on the competition between the viscous resistance and the aggregation of the particles. Among the three ER fluids prepared with silicone oil with different terminal groups, hydroxyl-terminated oil based sample has the highest zero-field viscosity, the highest field-induced yield stress and ER efficiency, the largest current density, and the best sedimentation stability.
文摘Ethylene propylene diene elastomers (EPDM) of various side chains and molecular weights were prepared as thin discs and the effects of electric field strength and temperature on the electromechanical properties were investigated. The electrical conductivity, the dielectric constant, the storage and loss moduli (G' and G'), the storage modulus response (ΔG’1000 V/mm), and the storage modulus sensitivity (ΔG’1000 V/mm/G’0) of the elastomers of different ethylene norbornene (ENB) contents and molecular weights were measured under electric field strengths varying from 0 V/mm to 1000 V/mm and at temperatures between 300 K and 380 K. The storage modulus response and sensitivity increase with increasing molecular weight and dielectric constant, consistent with the existing theory. However, for the case of EPDMs with different ENB contents, the storage modulus response and sensitivity vary inversely with the dielectric constant. EDPM is potentially a new type of electroactive materials.
基金Project (50771089) supported by the National Natural Science Foundation of China
文摘Based on a modified Maxwell-Wagner model,molecular dynamics is carried out to simulate the structural changes of ER(electrorheological) suspensions in a poiseuille flow field.The simulation results show that the flow assists in the collection of particles at the electrodes under a low pressure gradient,and the negative ER effect will show under a high pressure gradient.By analyzing the relationship curves of the shear stress and the pressure gradient in different relaxation time,it is found that for the same kind of ER suspensions materials,there is an optimal dielectric relaxation frequency.
基金Turkish Scientific and Technological Research Council for the financial support of this work (Project No: 112T811)
文摘Zinc borate(ZB)particles dispersed in silicone oil(SO)at concentrations of φ=5vol%-20vol% were subjected to dielectric analysis to elucidate their polarization strength,time,and mechanism.Results revealed that all virgin dispersions lacked polarization.Triton X-100,a non-ionic surfactant,was added to ZB/SO dispersions to enhance the polarizability of ZB particles.The addition of 1vol% Triton X-100 enhanced the polarizability of ZB/SO dispersions,and the 15vol% ZB/SO system provided the highest dielectric difference Δε′(the difference in ε′values at zero and infinite frequency,Δε′=ε0–ε∝)of 3.64.The electrorheological(ER)activities of the ZB/SO/Triton-X dispersion system were determined through the ER response test,and viscoelastic behaviors were investigated via oscillation tests.A recoverable deformation of 36% under an applied electrical field strength of 1.5 kV/mm was detected through creep and creep recovery tests.
基金The authors are thankful to the support of the National Natural Science Foundation of China(Grant No.50135030).
文摘Graphite/TiO2 composite particles were obtained by sol-gel technique in this paper. The structure and characteristic of the composite particles are analyzed by XRD, SEM and TG-DTA. The electrorheological properties of the ER fluid containing the particles were measured by a Couette-type rheometer under shear rates of 1-136 s-1 and AC electric fields of 0-3 kV/mm. The experimental results show that the leaking current density of the ER fluid is higher than that of pure titanium dioxide particles dispersed in damping oil. The shear yield stress of the ER fluid increases with increasing electric field and exhibits a typical Bingham flow behavior. The suspension demonstrates an excellent ER performance (τ/τo=1200) compared with conventional ER fluids (τ/τ0 ≤500). The sedimentation of the ER fluid is improved obviously due to the coating effect of the particles.