Many processes are used to join reinforcing bar (steel bar), but only a few of them, e.g. overlapping welding, gas pressure welding, thread joining, cold pressure sleeve joining, are able to be used on building sites ...Many processes are used to join reinforcing bar (steel bar), but only a few of them, e.g. overlapping welding, gas pressure welding, thread joining, cold pressure sleeve joining, are able to be used on building sites because the conditions of building sites are very particular. First, the work of joining reinforcing bar is mobile, that is to say, it must be moved from one place to another after having accomplished one joint. So it demands that the welding equipment (especially the welding head) must be convenient for moving. So it must be small and light. Second, the electricity capacity of the welding equipment can not be too large because the whole electricity capacity of a building site is limited. Third, the welding process ought to be simple because the situation og building sites is very poor and is on the open air. The more complex the process is, the more difficult the work will be. Fourth, the quality of the joint should be reliable and stable because it is impossible to check the quality of every joint, and there is no suitable way to do it even by now. For those reasons, the electroslag pressure butt welding has got great development recent years and is just suitable to be used on building sites to join vertical reinforcing bars. The article introduces its basic principle, processing, chief properties, and some test results.展开更多
Arc pressure is the key influencing factor to forming of molten pool. Countering the characteristic of tungsten inert gas arc welding with micro gap for tantalum sheet, according to the fundament of arc physics, a dis...Arc pressure is the key influencing factor to forming of molten pool. Countering the characteristic of tungsten inert gas arc welding with micro gap for tantalum sheet, according to the fundament of arc physics, a distribution model of arc pressure and forming mechanism of molten pool with micro butt gap are proposed, and the influences of arc pressure on forming of molten pool are discussed. Experimental researches for the dynamic formation process of weld molten pool by using high-speed vidicon camera show that when butt gap is appropriate, that is from 0. 1 to 0. 15 mm, molten metals formed on two workpiece uplift and grow up first, then are fused and form uniform molten pool finally.展开更多
文摘Many processes are used to join reinforcing bar (steel bar), but only a few of them, e.g. overlapping welding, gas pressure welding, thread joining, cold pressure sleeve joining, are able to be used on building sites because the conditions of building sites are very particular. First, the work of joining reinforcing bar is mobile, that is to say, it must be moved from one place to another after having accomplished one joint. So it demands that the welding equipment (especially the welding head) must be convenient for moving. So it must be small and light. Second, the electricity capacity of the welding equipment can not be too large because the whole electricity capacity of a building site is limited. Third, the welding process ought to be simple because the situation og building sites is very poor and is on the open air. The more complex the process is, the more difficult the work will be. Fourth, the quality of the joint should be reliable and stable because it is impossible to check the quality of every joint, and there is no suitable way to do it even by now. For those reasons, the electroslag pressure butt welding has got great development recent years and is just suitable to be used on building sites to join vertical reinforcing bars. The article introduces its basic principle, processing, chief properties, and some test results.
文摘Arc pressure is the key influencing factor to forming of molten pool. Countering the characteristic of tungsten inert gas arc welding with micro gap for tantalum sheet, according to the fundament of arc physics, a distribution model of arc pressure and forming mechanism of molten pool with micro butt gap are proposed, and the influences of arc pressure on forming of molten pool are discussed. Experimental researches for the dynamic formation process of weld molten pool by using high-speed vidicon camera show that when butt gap is appropriate, that is from 0. 1 to 0. 15 mm, molten metals formed on two workpiece uplift and grow up first, then are fused and form uniform molten pool finally.