INFLUENCES OF ACID POST-TREATMENT ON THE MORPHOLOGY OF SOAP-FREE P(MMA-EA-MAA)PARTICLES PREPARED BY SEEDED EMULSION POLYMERIZATION

Soap-free poly（methyl methacrylate-ethyl acrylate-methacrylic acid） latex particles with narrow size distribution were synthesized by seeded emulsion polymerization, and the porous particles were created by a stepwise alkali/acid treatment method. Effects of acid treatment conditions on the particle morphology were investigated. Results show that one to three pores were formed inside most of particles after post-treatment. At pH 7.0, when the treatment temperature was lower than 70℃, the size of particles and the volume of pores remained almost unchanged, and these two values increased significantly when the temperature was higher than 70℃. Both the particle size and the pore volume decreased with the increase of initial pH value and treatment time in the acid treatment. As the pH was below 4.0 and the treatment time was longer than 180 min, the particles shrunk in size.

SYNTHESIS OF BOWL-LIKE PARTICLES BY EMULSION POLYMERIZATION AND RELEASE BEHAVIOR OF SOLVENT FROM THE PARTICLES

Poly(styrene-glycidyl methacrylate) particles having bowl-shaped hollow structures were synthesized by swollen seed emulsion polymerization. The PS emulsion synthesized through soap-free emulsion polymerization was swollen by toluene, and then the mixture of second monomers was added under polymerization condition. So a thin shell of poly(styrene-glycidyl methacrylate) cross-linked by triethylene glycol diacrylate was formed around the swollen PS particle. The bowl-shaped particles were obtained after the collapsing of the thin shell when the toluene emanated from the particles, but the shapes were effected by the degrees of cross-linking. The shape of the particles was observed by SEM. The release behavior of solvent from the particles was examined by TG.

PARTICLE MORPHOLOGY OF POLY(VINYL CHLORIDE)RESIN PREPARED BY SUSPENDED EMULSION POLYMERIZATION

Suspended emulsion polymerization was used to prepare poly(vinyl chloride) (PVC) resin. Fine PVC particleswere formed at low polymerization conversions. The amount of fine panicles decreases as conversion increases anddisappears at conversions greater than 30%. Scanning electron micrographs show that PVC grains are composed of looselycoalesced primary particles, especially for PVC resins prepared in the presence of poly(vinyl alcohol) dispersant. The size ofprimary particles increases and porosity decreases with the increase of conversion. In view of the particle features of PVCresin, a particle formation mechanism including the formation of primary particles and grains is proposed. The formationprocess of primary particles includes the formation of particle nuclei, coalescence of particle nuclei to form primary particles,and growth of primary particles. PVC grains are formed by the coagulation of primary particles. The loose coalescence ofprimary particles is caused by the colloidal stability of primary particles and the low swelling degree of vinyl chloride in the primary particles.

Preparation of poly （methyl methacrylate）／nanometer calcium carbonate composite by in-situ emulsion polymerization

Methyl methacrylate (MMA) emulsion polymerization in the presence of nanometer calcium carbonate(nano-CaCO3) surface modified with γ-methacryloxypropyltrimethoxysilane (MPTMS) was carried out to prepare poly (methyl methacrylate) (PMMA)/nano-CaCO3 composite. The reaction between nano-CaCO3 and MPTMS, and the grafting of PMMA onto nano-CaCO3 were confirmed by infrared spectrum. The grafting ratio and grafting efficiency of PMMA on nano-CaCO3 modified with MPTMS were much higher than that on nano-CaCO3 modified with stearic acid. The grafting ratio of PMMA increased as the weight ratio between MMA and nano-CaCO3 increased, while the grafting efficiency of PMMA decreased. Transmission electron micrograph showed that nano-CaCO3 covered with PMMA was formed by in-situ emulsion polymerization.

MORPHOLOGY EVOLUTION OF POLY(St-co-BuA)/SILICA NANOCOMPOSITE PARTICLES SYNTHESIZED BY EMULSION POLYMERIZATION

Poly（St-co-BuA）/silica nanocomposite latexes were synthesized via conventional emulsion polymerization in the presence of 3-（trimethoxysilyl）propyl methacrylate modified colloidal nano-silica. The effects of surface property, particle size and content of colloidal nano-silica as well as the concentrations of monomer and surfactant on the morphology of nanocomposite latex particles were investigated by transmission electron microscope （TEM） and scanning electron microscope （SEM） in detail. Various interesting morphologies such as grape-like, Chinese gooseberry-like, pomegranate-like and normal core-shell structures were observed. Droplet nucleation mechanism competing with micelle nucleation mechanism was proposed to explain the morphological evolution of the nanocomposite particles.

Measurement methods of particle size distribution in emulsion polymerization

The particle size distribution of polymer always develops in emulsion polymerization systems,and certain key phenomena/mechanisms as well as properties of the final product are significantly affected by this distribution.This review mainly focuses on the measurement methods of particle size distribution rather than average particle size during the emulsion polymerization process,including the existing off-line,on-line,and in-line measurement methods.Moreover,the principle,resolution,performance,advantages,and drawbacks of various methods for evaluating particle size distribution are contrasted and illustrated.Besides,several possible development directions or solutions of the in-line measurement technology are explored.

Preparation of multihollow P(St-MAA) particles by sequence soap-free/soap emulsion polymerization and followed by stepwise alkali/acid posttreatment

The effects of ionic emulsifier, sodium dodecylbenzene sulfate (SDBS), on the formation of the multihollow structures in sub-micron sized polymer particles produced by alkali/acid posttreatment were investigated. The original latex particles with narrow size distribution were synthesized by a new sequence emulsifier-free/emulsifier emulsion copolymerization of styrene (St) and methacrylic acid (MAA). Results indicated that the pore size decreased and the pore number increased with the increase of SDBS amount, and the morphology of the posttreated latex particles was also significantly influenced by the introducing time of SDBS in the preparation of the original latex particles, and a suitable introducing time was 3 h of polymerization. (c) 2007 Cheng You Kan. Published by Elsevier B.V. on behalf of Chinese Chemical Society. All rights reserved.

Influence of Suspended Emulsion Polymerization Conditions on Particle Characteristics of Polyvinyl Chloride Resin

Suspended emulsion polymerization of vinyl chloride was carried out in a 5 L autoclave. The influence of agitation, polymerization conversion, dispersant and surfactant on the average particle size (PS) and particle size distribution (PSD), particle morphology and porosity of polyvinyl chloride (PVC) resin was investigated. It showed that the agitator had great influence on the smooth operation of polymerization, PS and PSD. The PS increased and PSD became narrow as polymerization conversion became high. The porosity decreased with the increase of conversion. A convenient choice of additives, both dispersants and non-ionic surfactants, allows one to adjust PS and PSD. The PS decreased with the addition of polyvinyl alcohol or hydroxypropyl methylcellulose dispersants,and increased with the addition of Span surfactants. The addition of dispersants or surfactants also affected the morphology and porosity of resin, and PVC resin with looser agglomeration and homogeneous distribution of primary particles was prepared.

PREPARATION AND CHARACTERIZATION OF AFFINITY POLYMER BASIC MICROSPHERES BY SOAP-FREE EMULSION POLYMERIZATION

Poly(styrene-co-glycidyl methacrylate) latex microspheres with uniform size and high-density epoxy groups on the surface were prepared by soap-free emulsion polymerization with batch wise operation mode in the presence of 2.2′- azobis(2-methylpropionamidine) dihydrochloride as an initiator.The kinetics of soap-free emulsion polymerization and the effects of polymerization factors were examined.In addition,the optimum polymerization conditions of poly(styrene-co- glycidyl methacrylate) latex microspheres for...

Preparation of Self-crosslinked Fluorocarbon Polymer Emulsion with Core-shell Structure by the Method of Soap-free Emulsion Polymerization

Using methyl methacrylate （MMA）, butyl acrylate（BA） and hexafluorobutyl acrylate（HFBA） as main raw materials, we prepared self-crosslinked fluorocarbon polymer emulsion with core-shell structure via soap-free emulsion polymerization when the conception of particle design and polymer morphology was adopted. Moreover, the influence of mole ratio of BA to MAA, pH value on the oligomer was studied. And the effects of the added amount of oligomer, self-crosslinked monomer and HFBA, mass ratio of BA to MMA, reaction temperature and the initiator on the polymerization technology and the performance of the product, were investigated and optimized. The structure and performance of the fluorocarbon polymer emulsion were characterized and tested with FTIR, TEM, MFT and contact angle and water absorption of the latex film. The experimental results show that the optimal conditions for preparing fluorocarbon polymer emulsion are as follows： for preparing the oligomer, tool ratio of BA to MAA is equal to 1.0 ： 1.60, and pH value is controlled within the range of 8.0 and 9.0; for preparing fluorocarbon polymer emulsion, the added amount of oligmer[P（BA/MANa）] is 6%; mass ratio of BA to MMA is 40 ＂ 60; the added amount of self-crosslinked monomer is 2%, the added amount of HFBA is 15 %; reaction temperature is 80 ℃; the mixture of potassium persulfate and sodium bisulfite is used as the initiator. The film-forming stability of the fluorocarbon polymer emul- sion and the performance of the latex film, which is prepared with the soap-free emulsion polymerization, are better than that prepared with the conventional emulsion polymerization.

Synthesis of Bowl-like Particles by Emulsion Polymerization and Release Behavior of Solvent from the Particles

Bowl-like poly (styrene-co-glycidyl methacrylate) was synthesized by swollen seeded emulsion polymerization. The polymerization was carried out in PS seed emulsion swollen by toluene, whereby the bowl-like particles formed at last. The shape was observed by SEM. These particles became ball-like when swollen by toluene, observed by optical microscope, and the release behavior of solvent from them was examined.

Polyaniline-based electrocatalysts through emulsion polymerization:Electrochemical and electrocatalytic performances

One of the major challenges associated with fuel cells is the design of highly efficient electrocatalysts to reduce the high overpotential of the oxygen reduction reaction (ORR). Here we report Polyaniline (PANI) based micro/nanomaterials with or without transition metals, prepared by the emulsion polymerization and subsequent heat treatment. PANI microspheres with the diameter of about 0.7 mu m have been prepared in basic (NH3 solution) condition, using two different types of surfactant (CTAB, SDS) as the stabilizer, ammonium persulphate (APS) as oxidant with aniline/surfactants molar ratio at 1/1 under the hydrothermal treatment. PANI nanorods, Fe-PANI, and Fe-Co-PANI have been synthesized in acidic (HCI) medium with aniline/surfactants molar ratio at 1/2 and polymerization carried out without stirring for 24 h. Products mainly Fe-Co-PANI have shown high current density with increasing sweep rate and excellent specific capacitance 1753 F/g at the scan rate of 1 mV/s. Additionally, it has shown high thermal stability by thermogravimetric analysis (TGA). Fe-PANI has been investigated for excellent performance toward ORR with four electron selectivity in the basic electrolyte. The PANI-based catalysts from emulsion polymerization demonstrate that the method is valuable for making non-precious metal heterogeneous electrocatalysts for ORR or energy storage and conversion technology. (C) 2016 Science Press and Dalian Institute of Chemical Physics, Chinese Academy of Sciences. Published by Elsevier B.V. and Science Press. All rights reserved.

Nonionic Polymerizable Emulsifier in High-Solids-Content Acrylate Emulsion Polymerization

Stable high-solids-content acrylate emulsion were obtained with a nonionic polymerizable emulsifier allyloxy nonylphenoxy poly （ethyleneoxy） （10） ether （ANPEO10）, and a conventional emulsifier OP-10 as a reference sample. 1H NMR proves that the polymerizable emulsifier ANPEO10 has been incorporated into the resulted acrylate polymers. TEM demonstrates that there are some differences in the particle morphologies. AFM proves that the polymerizable emulsifier ANPEO10 migrating to the surface of the emulsion film was much less than the conventional emulsifier OP-10. The polymerizable emulsifier ANPEO10 can enhance the adhesion with glass plate compared to the conventional emulsifier. Furthermore, with increasing amount of emulsifier, the surface free energy of the films first decreased and then increased, and the adhesion with glass plate is initially enhanced and then attenuated. The water-resistance and solvent-resistance of the films prepared by the polymerizable emulsifier ANPEO10 are superior to those prepared by the conventional emulsifier OP-10.

KINETICS OF SUSPENDED EMULSION POLYMERIZATION OF METHYL METHACRYLATE

The kinetics of suspended emulsion polymerization of methyl methacrylate (MMA), in which water acted as the dispersed phase and the mixture of NMA and cyclohexane as the continuous phase, was investigated. It showed that the initial polymerization rate (R-p0) and steady-state polymerization rate (R-p) were proportional to the mass ratio between water and oil phase, and increased as the polymerization temperature, the potassium persulphate concentration ([I]) and the Tween20 emulsifier concentration ([S]) increased. The relationships between the polymerization rate and [I] and [S] were obtained as follows: R-p0 proportional to [I](0.73)[S](0.32) and R-p proportional to [I](0.71)[S](0.23). The above exponents were close to those obtained from normal MMA emulsion polymerization. It also showed that the average molecular weight of the resulting poly(methyl methacrylate) decreased as the polymerization temperature, [I] and [S] increased. Thus, MMA suspended emulsion polymerization could be considered as a combination of many miniature emulsion polymerizations proceeding in water drops and obeyed the classical kinetics of MMA emulsion polymerization.

Effect of Polymerization Condition on Particle Size Distribution in St/BA/MAA Emulsion Polymerization Process

A series of St/BA/MAA emulsion polymerizations was carried out. By using PCS (photon correlation spectroscopy), the particle size distribution (PSD) of the whole St/BA/MAA emulsion polymerization process was gotten easily and quickly. The effect of polymerization condition on PSD in St/BA/MAA emulsion process was discussed.

Thermal Emulsion Polymerization without any Conventional Initiators and Emulsifiers

Stable poly（styrene-co-sodium styrene sulfonate） （P（St-NaSS） nanoparticles with broader size distribution were synthesized by thermal emulsion polymerization without any conventional initiators and emulsifiers. The obtained polymer nanoparticles have higher potential, and the particle sizes have broad distribution. The stability of polymer particles originated from the addition of small amounts of ionic comonomer, NaSS, which can act as an emulsifier in somewhat. The monomer conversion could reach up to about 28 wt% in 48 h, and did not increase by further polymerization when higher polymerization temperature （120℃） was employed. This polymerization system may be give some further understand for mechanism of emulsion polymerization.

Self-assembly of Gradient Copolymer Synthesized by Spontaneous Batch RAFT Emulsion Polymerization and Its Application on Encapsulating Ag Nanoparticles

The gradient copolymers of acrylic acid and trifluoroethyl methacrylate（coded as P（TFEMAgrad-AA）） were synthesized via reversible addition-fragmentation transfer（RAFT） emulsifier-free emulsion polymerization. The spontaneous batch feeding approach was used to control the gradient chain sequence. Transmission electron microscopy（TEM） analysis revealed that the P（TFEMA-grad-AA） can self-assemble to form spherical micelles, rodlike micelles or vesicles in selective solvents. Morphological transition of the P（TFEMA-grad-AA） micelles was sensitive to the water content of the dioxane/water mixed solvent. More interestingly, Ag nanoparticles（NPs） were encapsulated by the P（TFEMA-grad-AA） micelles during the selfassembly process. The gradient chain sequence made the Ag NPs easily enter the core of the micelles, even when P（TFEMA-grad-AA） had less hydrophobic fluoro-units and more hydrophilic units. TEM images with energy dispersive spectrometer indicated that the nanocomposite micelles consisted of a Ag NPs core and a gradient copolymer shell.

Investigation on the Inverse Emulsion Polymerization of Acrylic Acid

Polyacrylic acid particles in nano-scale were synthesized using an inverse (W/O) emulsion polymerization method. The particle size and size change of inverse micelles which solubilize a part of monomer solution was monitored by PCS (photon correlation spectroscopy) and the particles of polyacrylic acid were viewed in scanning electron microscope for the first time. It was concluded that the inverse micelles were primarily the polymerization reaction sites.

Random Model and Simulation for Nucleation Stage of Emulsion Polymerization

The method of mathematical model and further computer simulation is an effective way to the theoretical study of emulsion polymerization and the scale-up of the reactors. In this work, Monte Carlo method has been used to simulate the nucleation of emulsion polymerization. The effects of emulsifier concentration [S] and initiator concentration [I] on various parameters such as the number of the particles (N p), the average diameter of the latex particles (D p), monomer conversion (x) and average radical number per particle (n) have been studied. The quantitative equations between [S], [I] and N p are in accord absolutely with the classical theory of Smith-Ewart.

Study on N-Phenylmaleimide/Styrene /Acrylonitrile Copolymer Prepared by Emulsion Polymerization

The emulsion polymerization of N-phenylmaleimide, Styrene and acrylonitrile was studied. The thermal property of this copolymer was measures by dynamic thermomechanical analysis(DMA). The mechanical properties, such as tensile strength, hardness and fie-cural Strength were StUdied experimentally. The results indicated that not only the monomer component but also the polymerization technologies have effect on the properties of the copolymer. The optimum monomer content and suitable polymerization method were obtained.