Polyvinyl alcohol (PVA) colloid stabilized Polyvinyl acetate (PVAc) based wood adhesive has poor performance in highly humid conditions. Currently, the addition of natural fillers in the wood adhesive is one of the mo...Polyvinyl alcohol (PVA) colloid stabilized Polyvinyl acetate (PVAc) based wood adhesive has poor performance in highly humid conditions. Currently, the addition of natural fillers in the wood adhesive is one of the most effective ways to enhance the performance of PVAc wood adhesive in highly moist conditions. Microcrystalline cellulose (MCC) are strong renewable, bio-based material and has great potential in a reinforcement of the polymeric matrix. Hence, the present work investigates the applicability of microcrystalline cellulose incorporated 3% and 5% in situ emulsion polymerization PVAc wood adhesives. Effect on physical, thermal and mechanical properties was studied by viscosity, pH, contact angle measurement, differential scanning calorimetry (DSC) and pencil hardness test of films. Emulsions with different proportions of MCC were prepared and the shear strength of the applied adhesive on wood was measured. The viscosity of the adhesives was increased by increasing the concentration of MCC. The mechanical properties like tensile strength of adhesives with MCC were measured by universal tensile machine (UTM). Thermal stability was studied by differential scanning calorimetry (DSC). The tensile shear strength demonstrates that MCC can improve bonding strength as compared to PVAc Homo based adhesive in the wet condition which was validated through a contact angle study. The hardness of PVAc films were also changed positively by the addition of MCC. Here, we studied the effect of the addition of different concentrations of MCC materials in situ polymerization of PVAc on their performance properties.展开更多
Synthetic wood adhesives, consisting of urea-formaldehyde resins (UF), phenol-formaldehyde resins (PF), melamine-formaldehyde resins (MF), and polyurethane resins, are widely used. For UF and MF, most investigations a...Synthetic wood adhesives, consisting of urea-formaldehyde resins (UF), phenol-formaldehyde resins (PF), melamine-formaldehyde resins (MF), and polyurethane resins, are widely used. For UF and MF, most investigations are concerned with reducing free formaldehyde content;for PF, most studies focused on finding new alternative chemicals to replace phenol. These adhesives come under the Carcinogenic, Mutagenic, and Reprotoxic chemicals (CMR) category. Due to global energy issues and dependency on petroleum sources, the focus has shifted to look for alternative and renewable raw material sources for wood adhesives. Conventionally available wood adhesives are polyvinyl alcohol (PVA) stabilized, with drawbacks like poor water resistance, poor heat resistance, low-temperature workability, and it’s based on petroleum resources. Polyvinyl acetate (PVAc) is non-resistant to moisture polymer, and if such adhesive joints are exploited in a moist environment, its strength substantially decreases. Sufficiently moisture-resistant adhesive joints are obtained by modifying PVAc dispersion with special compounds like reactive comonomer, Silanes, and modified PVA. To improve the workability at low temperature, Vinyl acetate (VAc) is copolymerized with specific comonomers like butyl acetate without affecting the performance properties. Here, we aim to present an overview of the research trend of PVAc-based adhesives in the wood industry. The review summarizes the current state of research PVAc-based adhesives.展开更多
The seeded semicontinuous emulsion multi-copolymerization of butyl acrylate (BA), 2-ethylhexyl acrylate (2EHA), methyl methacrylate (MMA), 2-hydroxyl propyl acrylate (HOPA) and acrylic acid (AA) was used to prepare th...The seeded semicontinuous emulsion multi-copolymerization of butyl acrylate (BA), 2-ethylhexyl acrylate (2EHA), methyl methacrylate (MMA), 2-hydroxyl propyl acrylate (HOPA) and acrylic acid (AA) was used to prepare the acrylic latexes with high-solid content. The effects of monomer emulsion feed rates (R(a)) and (R/E)(E) values, the ratio of emulsifier amount between the initial charge (R) and the addition monomer emulsion (E), on the polymerization reaction features, the viscosities, surface tensions,particle sizes and particle sizes distributions of latexes, T-g and the insoluble fractions of films, the 180 degrees peel strength, tack and holding power of pressure-sensitive adhesive (PSA) tapes, prepared from the latexes, were studied. Experimental study shows that the grafting and crosslinking fraction in the PSA tapes must be controlled within a suitable range to keep the balance of the 180 degrees peel strength, tack and holding power.展开更多
Conductive adhesive tape is one kind of electromagnetic interference(EMI)shielding materials for electronic packaging.However,the inferior conductivity of the pressure-sensitive adhesive(PSA)layer results in serious e...Conductive adhesive tape is one kind of electromagnetic interference(EMI)shielding materials for electronic packaging.However,the inferior conductivity of the pressure-sensitive adhesive(PSA)layer results in serious electromagnetic leakage at the conjunctions between the conductive tapes and target objects.Adding conductive fillers is a traditional method for highly conductive adhesive tapes.However,the content of conductive fillers is needed to reach the percolation threshold,which is usually as high as tens of percent.High-content fillers result in significant loss of adhesive property and high fabrication cost.Herein,we introduce a rational architecture of conductive microsphere monolayer(CMM)in the PSA layer.The CMM connects the top and bottom surfaces of the PSA layer and improves its conductivity in the z-direction.Importantly,low contents of conductive microspheres(≤5%(mass fraction,w))can achieve the target of conductivity improvement,but not result in the serious loss of the adhesive property.Therefore,the strategy of CMMs can balance the tradeoff between the conductivity and the adhesive property of conductive PSA tapes.Finally,we demonstrate the superior EMI shielding performance of as-made conductive adhesive tapes,indicating their potential applications as the advanced EMI shielding materials in the electronic packaging.展开更多
文摘Polyvinyl alcohol (PVA) colloid stabilized Polyvinyl acetate (PVAc) based wood adhesive has poor performance in highly humid conditions. Currently, the addition of natural fillers in the wood adhesive is one of the most effective ways to enhance the performance of PVAc wood adhesive in highly moist conditions. Microcrystalline cellulose (MCC) are strong renewable, bio-based material and has great potential in a reinforcement of the polymeric matrix. Hence, the present work investigates the applicability of microcrystalline cellulose incorporated 3% and 5% in situ emulsion polymerization PVAc wood adhesives. Effect on physical, thermal and mechanical properties was studied by viscosity, pH, contact angle measurement, differential scanning calorimetry (DSC) and pencil hardness test of films. Emulsions with different proportions of MCC were prepared and the shear strength of the applied adhesive on wood was measured. The viscosity of the adhesives was increased by increasing the concentration of MCC. The mechanical properties like tensile strength of adhesives with MCC were measured by universal tensile machine (UTM). Thermal stability was studied by differential scanning calorimetry (DSC). The tensile shear strength demonstrates that MCC can improve bonding strength as compared to PVAc Homo based adhesive in the wet condition which was validated through a contact angle study. The hardness of PVAc films were also changed positively by the addition of MCC. Here, we studied the effect of the addition of different concentrations of MCC materials in situ polymerization of PVAc on their performance properties.
文摘Synthetic wood adhesives, consisting of urea-formaldehyde resins (UF), phenol-formaldehyde resins (PF), melamine-formaldehyde resins (MF), and polyurethane resins, are widely used. For UF and MF, most investigations are concerned with reducing free formaldehyde content;for PF, most studies focused on finding new alternative chemicals to replace phenol. These adhesives come under the Carcinogenic, Mutagenic, and Reprotoxic chemicals (CMR) category. Due to global energy issues and dependency on petroleum sources, the focus has shifted to look for alternative and renewable raw material sources for wood adhesives. Conventionally available wood adhesives are polyvinyl alcohol (PVA) stabilized, with drawbacks like poor water resistance, poor heat resistance, low-temperature workability, and it’s based on petroleum resources. Polyvinyl acetate (PVAc) is non-resistant to moisture polymer, and if such adhesive joints are exploited in a moist environment, its strength substantially decreases. Sufficiently moisture-resistant adhesive joints are obtained by modifying PVAc dispersion with special compounds like reactive comonomer, Silanes, and modified PVA. To improve the workability at low temperature, Vinyl acetate (VAc) is copolymerized with specific comonomers like butyl acetate without affecting the performance properties. Here, we aim to present an overview of the research trend of PVAc-based adhesives in the wood industry. The review summarizes the current state of research PVAc-based adhesives.
基金This work was supported by the National Natural Science Foundation of China
文摘The seeded semicontinuous emulsion multi-copolymerization of butyl acrylate (BA), 2-ethylhexyl acrylate (2EHA), methyl methacrylate (MMA), 2-hydroxyl propyl acrylate (HOPA) and acrylic acid (AA) was used to prepare the acrylic latexes with high-solid content. The effects of monomer emulsion feed rates (R(a)) and (R/E)(E) values, the ratio of emulsifier amount between the initial charge (R) and the addition monomer emulsion (E), on the polymerization reaction features, the viscosities, surface tensions,particle sizes and particle sizes distributions of latexes, T-g and the insoluble fractions of films, the 180 degrees peel strength, tack and holding power of pressure-sensitive adhesive (PSA) tapes, prepared from the latexes, were studied. Experimental study shows that the grafting and crosslinking fraction in the PSA tapes must be controlled within a suitable range to keep the balance of the 180 degrees peel strength, tack and holding power.
基金the financial support from the National Natural Science Foundation of China(Grant No.62074154)Shenzhen Science and Technology Program(Grant Nos.JSGG20210802153000002,JCYJ20210324102208023).
文摘Conductive adhesive tape is one kind of electromagnetic interference(EMI)shielding materials for electronic packaging.However,the inferior conductivity of the pressure-sensitive adhesive(PSA)layer results in serious electromagnetic leakage at the conjunctions between the conductive tapes and target objects.Adding conductive fillers is a traditional method for highly conductive adhesive tapes.However,the content of conductive fillers is needed to reach the percolation threshold,which is usually as high as tens of percent.High-content fillers result in significant loss of adhesive property and high fabrication cost.Herein,we introduce a rational architecture of conductive microsphere monolayer(CMM)in the PSA layer.The CMM connects the top and bottom surfaces of the PSA layer and improves its conductivity in the z-direction.Importantly,low contents of conductive microspheres(≤5%(mass fraction,w))can achieve the target of conductivity improvement,but not result in the serious loss of the adhesive property.Therefore,the strategy of CMMs can balance the tradeoff between the conductivity and the adhesive property of conductive PSA tapes.Finally,we demonstrate the superior EMI shielding performance of as-made conductive adhesive tapes,indicating their potential applications as the advanced EMI shielding materials in the electronic packaging.