The effect of Ti and Zr content on the structure,mechanics and energy-release characteristics of Ti—Zr—Ta alloys

Energetic structural materials(ESMs)are a new type of structural materials with bearing and damage characteristics.In this work the microstructure,mechanical properties and energy release characteristics of multi-element Ti-Zr-Ta alloys with good casting performance were studied.The microstructure of the Ti_(x)ZrTa alloys gradually change from BCC+HCP to single BCC structure with the increase of Ti.While the Ti_(2)Zr_(y)Ta alloys was still uniform and single BCC structure with the increase of Zr.The evolution of microstructure and composition then greatly affect the mechanical properties and energy-release characteristics of Ti-Zr-Ta alloys.The synergistic effect of dual phase structure increases the fracture strain of Ti_(x)ZrTa(x=0.2,0.5)with the Ti content decreases,while the fracture strain of Ti_(x)ZrTa(x=2.0,3.0,4.0)gradually increase with the Ti content increases caused by the annihilation of the obstacles for dislocation movement.And as Zr content increases,the fracture strain of Ti_(2)Zr_(y)Ta alloys decrease,then the oxidation reaction rate and fragmentation degree gradually increase.The higher oxidation rate and the lager exposed oxidation area jointly leads the higher releasing energy efficiency of Ti_(x)ZrTa alloys with low Ti content and Ti_(2)Zr_(y)Ta alloys with high Zr content.

Microstructural evolution and energetic characteristics of TiZrHfTa_(0.7)W_(0.3)high-entropy alloy under high strain rates and its application in high-velocity penetration

Energetic structural materials(ESMs)integrated a high energy density and rapid energy release with the ability to serve as structural materials.Here,a novel triple-phase TiZrHfTa_(0.7)W_(0.3)high-entropy alloy(HEA)was fabricated and investigated as a potential ESM.A hierarchical microstructure was obtained with a main metastable body-centered-cubic(BCC)matrix with distributed Ta-W-rich BCC precipitates of various sizes and interwoven hexagonal close-packed(HCP)lamellar nano-plates.The compressive me-chanical properties were tested across a range of strain rates and demonstrated a brittle-to-ductile tran-sition as the strain rate increased while maintaining a high ultimate strength of approximately 2.5 GPa.This was due to the phase transformation from metastable matrix BCC to HCP structures.In addition,during the dynamic deformation,metal combustion originating from the failure surface was observed.Furthermore,the composition of the fragments was studied,and the results indicated that the addition of tungsten promoted combustion.Finally,the potential application of this HEA was evaluated by high-velocity penetration tests,and the results were compared to other typical structural materials for pene-trators and bullets.A comparison was conducted by assessing the geometries of the penetration channel employing two dimensionless parameters normalized by the projectile size,representing longitudinal and lateral damage,respectively.The normalized depth of the TiZrHfTa_(0.7)W_(0.3)HEA projectile was comparable to those of the other investigated materials,but the normalized diameter was the largest,showing an excellent ability to deliver lateral damage.