Using ethylene glycol monovinyl polyoxyethylene ether,2-acrylamido-2-methylpropane sulfonic acid(AMPS)and acrylic acid as the main synthetic monomers,a high robustness polycarboxylate superplasticizer was prepared.The...Using ethylene glycol monovinyl polyoxyethylene ether,2-acrylamido-2-methylpropane sulfonic acid(AMPS)and acrylic acid as the main synthetic monomers,a high robustness polycarboxylate superplasticizer was prepared.The effects of initial temperature,ratio of acid to ether,amount of chain transfer agent,and synthesis process on the properties of the superplasticizer were studied.The molecular structure was characterized by GPC(Gel Permeation Chromatography)and IR(Infrared Spectrometer).As shown by the results,when the initial reaction temperature is 15℃,the ratio of acid to ether is 3.4:1 and the acrylic acid pre-neutralization is 15%,The AMPS substitution is 10%,the amount of chain transfer agent is 8%,and the performance of the synthesized superplasticizer is the best.Compared with commercially available ordinary polycarboxylate superplasticizer in C30 concrete prepared with manufactured sand and fly ash,the bleeding rate decreases by 52%,T50 decreases by 1.2 s,and the slump time decreases by 1.1 s.In C60 concrete prepared with fly ash and river sand,the bleeding rate decreases by 46%,T50 decreases by 0.8 s,and the slump time decreases by 3.2 s.展开更多
Graphene oxide(GO)as a new nano-enhancer in cement-based materials has gained wide attention.However,GO is easy to aggregate in alkaline cement mortar with poor dispersibility.This hinders its application in practical...Graphene oxide(GO)as a new nano-enhancer in cement-based materials has gained wide attention.However,GO is easy to aggregate in alkaline cement mortar with poor dispersibility.This hinders its application in practical infrastructure construction.In this work,GO-M18 polycarboxylate compound superplasticizer(GM)were obtained by compounding the M18 polycarboxylate superplasticizer with GO solution at different mass ratios.The dispersion of GM in alkaline solution was systematically studied.The phases and functional groups of GM were characterized by XRD and FTIR.The effects of GM on the cement mortar hydration and the formation of microstructure were investigated by measuring the heat of hydration,MIP,TG/DSC,and SEM.The results show that the long-chain structure of the M18 polycarboxylate superplasticizer can increase the interlayer spacing of GO and weaken the force between GO sheets.The modified GO can be uniformly dispersed in the cement slurry.GM can accelerate the early hydration process of cement,which can increase the content of Ca(OH)2 and decrease the grain size.It can optimize the pore size distribution of cement-based materials,increase the density of harmless and less harmful pores,thereby improving mechanical properties.Such methods can transform traditional cement-based materials into stronger,more durable composites,which prolong the life of cement-based materials and reduce the amount of cement used for later maintenance.This provides an idea for achieving sustainability goals in civil engineering.展开更多
Effects of polycarboxylate-type superplasticizer(PC) molecular structure on the hydration heat of tricalcium silicate(C3S) paste and polymerization degree of hydration products(C-S-H gel) were researched by usin...Effects of polycarboxylate-type superplasticizer(PC) molecular structure on the hydration heat of tricalcium silicate(C3S) paste and polymerization degree of hydration products(C-S-H gel) were researched by using TAM AIR isothermal microcalorimetry(TA) and 29Si nuclear magnetic resonance(NMR).Methoxy polyethylene glycol-methacrylates-based polycarboxylate superplasticizers with different side chain lengths and main chain lengths were employed.PC molecules with shorter main chain or longer side chains caused stronger retardation of C3S early hydration and lesser increase of C3S 3 d hydration degree.NMR measurement indicated that the incorporation of PC increased the hydration degree of C3S paste and the polymerization degree of silicon-oxygen tetrahedron of C-S-H gel.The tendency for C3S 7 d hydration degree to improve was more pronounced while PC molecules with longer main chain or shorter side chain were added.Whereas,PC molecules with longer main chains or longer side chains increased the 7 d polymerization degree of C-S-H gel.展开更多
Bridge polycarboxylate superplasticizers(PCs) with crosslink structure were synthesized by using polyethyleneglycol di-acrylate(PEGdA), replacing partial polyethyleneglycol mono-acrylate (PEGmA) as crosslinking ...Bridge polycarboxylate superplasticizers(PCs) with crosslink structure were synthesized by using polyethyleneglycol di-acrylate(PEGdA), replacing partial polyethyleneglycol mono-acrylate (PEGmA) as crosslinking agent. Structures of bridge PCs were analyzed by gel permeation chromatography, and dispersion ability was evaluated by cement paste dispersity variation on time and rheology test. The experimental results showed that, molecular weight(MW) of bridge PCs increased with increase of PEGdA proportion, and MW distribution curve changed from Gaussian to fiat like, which meant notable increase of highly crosslinked copolymer. Bridge PCs led to decreased initial cement paste dispersity and better dispersity retention due to slow releasing. Further research showed that, PEGdA proportion had slight effect on polymerization degree of backbone, MW distribution of backbone deviated from Gaussian distribution and shoulder peaks appeared on distribution curve when PEGdA increased.展开更多
Circulating fluidized bed combustion (CFBC) ash exhibits the desirable pozzolanic activity which makes it a potential supplementary cementitious material to replace cement for concrete production. However, the high ...Circulating fluidized bed combustion (CFBC) ash exhibits the desirable pozzolanic activity which makes it a potential supplementary cementitious material to replace cement for concrete production. However, the high unburnt carbon content and porous surface structure of CFBC ash may adsorb water reducer and thereby significantly reduce the efficiency of water-reducing agents. The adsorption mechanism of polycarboxylate superplasticizer in CFBC ash-Portland cement paste was investigated by ultraviolet-visible spectrophotometer, and the conception of "invalid adsorption site" of CFBC ash was presented. The results show that the adsorption behavior of polycarboxylate superplasticizer in coal ash-Portland cement paste can be described by Langmuir isothermal adsorption equation. The adsorption capacity of CFBC ash-Portland cement paste is higher than that of pulverized coal combustion (PCC) fly ash-Portland cement paste. Moreover, the adsorption amount of polycarboxylate superplasticizer increases with the ratio of ash-to-cement in the paste. At last, the fluidity of CFBC ash-Portland cement paste is lower than that of the PCC fly ash paste. This work suggests that when CFBC ash is used as concrete admixture, the poor flowability of the cementitious system due to the high adsorption of water and water-reducing agent should be taken into consideration.展开更多
Molecular structures of polycarboxylate(PCE) superplasticizer significantly affect the rheological properties of cement paste. Consequently, we employed self-synthesized PCE copolymers with different carboxylic dens...Molecular structures of polycarboxylate(PCE) superplasticizer significantly affect the rheological properties of cement paste. Consequently, we employed self-synthesized PCE copolymers with different carboxylic densities to investigate their influence on the rheological behavior of cement paste. Three typical rheological models were applied to analyze the rheological properties, including Power-law model, Bingham model as well as Herschel-Buikley model. In addition, the thixotropical performances of cement paste in the presence of PCE with different carboxylic densities were investigated. The results show that the carboxylic density of PCE greatly influences the dispersing performance of PCE superplasticizers. As carboxylic density increases, the dispersing capability of PCE improves, and P(PEG1-AA6) possesses the strongest dispersing capability, the initial fluidity and 1 h fluidity of cement paste are both the highest, and cement paste has the lowest viscosity and the smallest hysteresis loop.展开更多
The dispersion ability of polycarboxylate superplasticizer(PCE) in fresh concrete was much impeded by clay impurities. To improve the dispersion of PCE in the clay-contained concrete, a novel PCE with carboxyl as a ...The dispersion ability of polycarboxylate superplasticizer(PCE) in fresh concrete was much impeded by clay impurities. To improve the dispersion of PCE in the clay-contained concrete, a novel PCE with carboxyl as a specific branched chain terminal group was synthesized, using modified polyether as the raw material which was prepared through esterification between hexahydrophthalic anhydride(HHPA) and isobutenyl polyoxyethylene ether(IPEG) with hydroxy as the terminal group. The esterification product and PCE molecular structure were characterized by infrared spectroscopy and ~1HNMR resonance. The results confirmed that the product molecular structure was a comb-type copolymer with long-chain terminal carboxyl group and PEO attached directly to the backbone chain. The as-synthesized PCEs had favorable dispersibility in cement than conventional PCE in the presence of montmorillonite(Mmt) clay. This can be attributed to the introduction of electronegative carboxyl to PCE long-chain terminal group, which reduces the adsorption of PCE on Mmt, and thus improves the tolerance of PCE to the Mmt.展开更多
The effects of various factors on the synthesis process and the performances of product, including batch feeding way and the dosage of the radical initiator, the system concentration, the reaction temperature and the ...The effects of various factors on the synthesis process and the performances of product, including batch feeding way and the dosage of the radical initiator, the system concentration, the reaction temperature and the reaction time were discussed. A kind of polycarboxylate superplasticizer with allyl alcohol polyethylene glycol, maleic anhydride and methacrylic acid sulfonic sodium as main raw materials has been synthesized. Their relative effectiveness as dispersants was evaluated in cement paste by measuring paste fluidity. The optimum parameters of technology and the appropriate proportion of raw materials were obtained. As a result,the new high performance superplasticizer suitable for high-performance concrete has been synthesized. The structure of copolymer was characterized and analyzed by FT-IR spectra. Results indicated that product copolymer structure was consistent with the ideal molecular structure designed.展开更多
The infl uence law of clay on mortar fluidity mixed with polycarboxylate superplasticizer was studied. Several methods of inhibiting clay adsorption of polycarboxylate superplasticizer were discussed. The experimental...The infl uence law of clay on mortar fluidity mixed with polycarboxylate superplasticizer was studied. Several methods of inhibiting clay adsorption of polycarboxylate superplasticizer were discussed. The experimental results show that clay has signifi cant effect on the dispersion of polycarboxylate superplasticizer and montmorillonite clay has more signifi cant impact on mortar fluidity than other clays. The pH value and the salts of the solution can affect the adsorption of clay to polycarboxylate superplasticizer. The incorporation of a small amount of sodium hydroxide solution, sodium silicate or cationic surfactants can improve the effect of the clay on the dispersion of polycarboxylate superplasticizer.展开更多
A low adsorption clay-resistant polycarboxylate superplasticizer(KN-PC)was synthesized using acrylic acid and isopentenol polyoxyethylene ether as the main reaction materials.The structural characterization and clay-r...A low adsorption clay-resistant polycarboxylate superplasticizer(KN-PC)was synthesized using acrylic acid and isopentenol polyoxyethylene ether as the main reaction materials.The structural characterization and clay-resistant mechanism of the KN-PC were explored using Fourier transform infrared spectroscopy and X-ray diffraction,and the effect of the KN-PC on the performance of composite paste with various montmorillonite(MMT)contents was analyzed.Compared with ordinary polycarboxylate superplasticizer(PC),the KN-PC has a low sensitivity to the MMT.By the action of the MMT,the adsorption dosage of the KN-PC on the MMT is much smaller than that of the PC.展开更多
A procedure was developed for the determination of residual monomers in polycarboxylate superplasticizer (PCs) by reversed-phase high performance liquid chromatography (RP-HPLC).Four kinds of residual monomers wer...A procedure was developed for the determination of residual monomers in polycarboxylate superplasticizer (PCs) by reversed-phase high performance liquid chromatography (RP-HPLC).Four kinds of residual monomers were well separated and determined on a SinoChrom ODS-BP (C18) column with mobile phases composed of acetonitrile and phosphate buffer solution.The monomers were detected by UV detector at 205 nm and quantitatively analyzed with an external standard method.For those residual monomers,the linear response ranged from 4.0×10-6 mol·L-1 to 2.0×10-3 mol·L-1.The determination limit of acrylic acid,sodium methylallyl sulfonate and 2-Acrylamido-2-methylpropane sulfonic acid was 0.02×10-5 mol·L-1,while that of methoxy-polyethylene glycol monoacrylate was 0.1×10-5 mol·L-1.The relative standard deviation (RSD) of high concentration samples was less than 1%,while that of the low concentration samples was between 1%-4%.The standard (additional) recovery ratio was 97.4% -104.2%.展开更多
A series of polycarboxylate-based superplasticizers(PCs) with different structures were synthesized and the effects of chemical structure on zeta potential and rheological property of cement paste were studied. Residu...A series of polycarboxylate-based superplasticizers(PCs) with different structures were synthesized and the effects of chemical structure on zeta potential and rheological property of cement paste were studied. Residual monomers in each sample of PCs were quantitatively determined. The property of the polymers in cement was tested by micro-electrophoresis apparatus and R/S rheometer. Results showed that the zeta potential and its rheological properties are related with the side-chain length and density of PCs. The PCs having shorter side chain and lower side chain density exhibit higher anionic charge density, thus resulting in higher zeta potential. The effect of side chain density on zeta potential is more notable compared with that of side-chain length, and thus affecting the initial shear yield stress and apparent viscosity of the cement paste. In addition, although increasing the side chain length will result in reduction of the anionic charge density, the steric hindrance effect is obvious, which can effectively improve the dispersion of the cement particles, and reduce the viscosity and shear yield stress of slurry.展开更多
The effects of circulating fluid bed(CFB) ash on the adsorption performance of polycarboxylate superplasticiser and the mechanism of this influence on the dispersive property of the polycarboxylate superplasticiser we...The effects of circulating fluid bed(CFB) ash on the adsorption performance of polycarboxylate superplasticiser and the mechanism of this influence on the dispersive property of the polycarboxylate superplasticiser were investigated by determing the cement paste fluidity, total organic carbon adsorption, infrared spectroscopic analyses and ζ potential test. The experimental results show that the addition of an inorganic salt into the mixture to change the content of SO42-and Fe2O3can improve the adaptability between the CFB ash and polycarboxylate superplasticiser. Adsorption may occur between the polycarboxylate superplasiciser and Fe2O3, SO42-or other components in CFB ash, leading to a significant reduction in paste fluidity. As the content of Na2SO4in CFB ash reaches 3% or Fe2O3reaches 9%, the paste loses its liquidity. The organic carbon content in the liquor decreases with an increase in Na2SO4or Fe2O3content. Adding some Ba(NO3)2and Na2S to the liquor can recover the organic carbon content to a certain extent, and the absolute value of ζ potential will increase. The addition of Ba(-NO3)2or Na2S reduces the adsorption property of Na2SO4or Fe2O3in CFB ash on the polycarboxylate superplasticiser.展开更多
Influences of different superplasticizers ( STP. KSJSTO and LMS-P) on rheological behavior of low-cement castables and the mechanisms were analyzed. The shear stress and viscosity under different shear rates of matr...Influences of different superplasticizers ( STP. KSJSTO and LMS-P) on rheological behavior of low-cement castables and the mechanisms were analyzed. The shear stress and viscosity under different shear rates of matrix slurry were determined using a NXS-I IA rotary viscometer. Effects of different admixtures on the rheological properties of slurry was analyzed theoretically. Sodium tripolyphosphate and poly'carboxylate superplasticizers KS-JSTO and LMS-P) can improve the fluidity and initial setting time. With STP. the slurry is plastic flow. With KS-JS70 or LMS-P increasing, the slurrv changes from plastic.flow, pseudoplastic flow to dilatant flow successively. Th, e optimum dosages of STP. KS-JSTO and LMS-P are 0. 15%. 0. 25% and 0. 40%, respectively. KS-JS70 and LMS-P can significantly reduce the slurry viscosity and shear stress to improve the workability of construction. Both shear stress and viscosity shall be taken into account for on-site construction.展开更多
A new kind of polycarboxylate superplasticizer with high slump loss resistance was obtained by designing scheduled molecular structure.The number average molecular mass of the polymer was characterized by the gel perm...A new kind of polycarboxylate superplasticizer with high slump loss resistance was obtained by designing scheduled molecular structure.The number average molecular mass of the polymer was characterized by the gel permeation chromatography measurements.And chemical structure of the polymer was observed by the Fourier transform infrared spectroscopy(FT-IR).The results show that the good workable maintaining of self-compacting concrete could be achieved through direct adjustment of number average molecular mass and different unsaturated monomer in synthetic process.The FT-IR analysis illustrated that the high slump loss resistance of polycarboxylate superplasticizers with ester and carboxyl group and expectations of molecular structure were designed.展开更多
Polycarboxylate(PC) superplasticizers with different chemical structures were synthesized through free radical co-polymerization reaction.A total organic carbon analyzer was used to investigate adsorption behaviors ...Polycarboxylate(PC) superplasticizers with different chemical structures were synthesized through free radical co-polymerization reaction.A total organic carbon analyzer was used to investigate adsorption behaviors of PCs,and to evaluate influences of soluble salts on absorption properties of PCs.It is found that adsorption ratios of PCs on cement particles decrease greatly with the addition of Na2SO4;the adsorption ratio of ethers PC with Hydroxyethyl methacrylate(HEMA) group first increases then decreases with the addition of NaCl;the adsorption ratio of esters PC with short side chains first decreases then increases,while the adsorption ratio of ethers PC with HEMA group decreases with the addition of CaCl2;the adsorption ratio of esters PC with short side chains decreases with the addition of Ca(NO3)2;AlCl3 causes the decrease of the adsorption ratio of ethers PC with HEMA group.展开更多
The polymerization of acrylonitrile (AN) in aqueous nitric acid initiated by ' cage ' vanadyl polycarboxylate (P=VO)-thiourea (TU) complex was investigated. The overall rate ofpolymerization isThe relationship...The polymerization of acrylonitrile (AN) in aqueous nitric acid initiated by ' cage ' vanadyl polycarboxylate (P=VO)-thiourea (TU) complex was investigated. The overall rate ofpolymerization isThe relationship between the induction period (τ) and the temperature of polymerization as well as the concentrations of reactants can be expressed as follows :The molecular weight of polyacrylonitrile increases with increasing monomer concentration and decreases with increasing temperature of polymerization and concentrations of vanadyl polycarboxylate and thioureaThe polymerization mechanism was proposed and discussed.展开更多
Polycarboxylate water-reducing admixture possesses the capability which could meet with the comprehensive performance of high performance concrete used in passenger dedicated line engineering.The problems of polycarbo...Polycarboxylate water-reducing admixture possesses the capability which could meet with the comprehensive performance of high performance concrete used in passenger dedicated line engineering.The problems of polycarboxylates water-reducing admixtures existed in the engineering application of were analyzed.At present the key for polycarboxylates application was to settle the compatibility between the water-reducing admixture and the cement and to keep the quality retention of this admixture.展开更多
基金the Scientific Research Foundation of Hubei University of Technology(GCRC2020012).
文摘Using ethylene glycol monovinyl polyoxyethylene ether,2-acrylamido-2-methylpropane sulfonic acid(AMPS)and acrylic acid as the main synthetic monomers,a high robustness polycarboxylate superplasticizer was prepared.The effects of initial temperature,ratio of acid to ether,amount of chain transfer agent,and synthesis process on the properties of the superplasticizer were studied.The molecular structure was characterized by GPC(Gel Permeation Chromatography)and IR(Infrared Spectrometer).As shown by the results,when the initial reaction temperature is 15℃,the ratio of acid to ether is 3.4:1 and the acrylic acid pre-neutralization is 15%,The AMPS substitution is 10%,the amount of chain transfer agent is 8%,and the performance of the synthesized superplasticizer is the best.Compared with commercially available ordinary polycarboxylate superplasticizer in C30 concrete prepared with manufactured sand and fly ash,the bleeding rate decreases by 52%,T50 decreases by 1.2 s,and the slump time decreases by 1.1 s.In C60 concrete prepared with fly ash and river sand,the bleeding rate decreases by 46%,T50 decreases by 0.8 s,and the slump time decreases by 3.2 s.
基金funded by the National Natural Science Foundation of China(No.51872137)and Priority Academic Program Development of Jiangsu Higher Education Institutions(PAPD)。
文摘Graphene oxide(GO)as a new nano-enhancer in cement-based materials has gained wide attention.However,GO is easy to aggregate in alkaline cement mortar with poor dispersibility.This hinders its application in practical infrastructure construction.In this work,GO-M18 polycarboxylate compound superplasticizer(GM)were obtained by compounding the M18 polycarboxylate superplasticizer with GO solution at different mass ratios.The dispersion of GM in alkaline solution was systematically studied.The phases and functional groups of GM were characterized by XRD and FTIR.The effects of GM on the cement mortar hydration and the formation of microstructure were investigated by measuring the heat of hydration,MIP,TG/DSC,and SEM.The results show that the long-chain structure of the M18 polycarboxylate superplasticizer can increase the interlayer spacing of GO and weaken the force between GO sheets.The modified GO can be uniformly dispersed in the cement slurry.GM can accelerate the early hydration process of cement,which can increase the content of Ca(OH)2 and decrease the grain size.It can optimize the pore size distribution of cement-based materials,increase the density of harmless and less harmful pores,thereby improving mechanical properties.Such methods can transform traditional cement-based materials into stronger,more durable composites,which prolong the life of cement-based materials and reduce the amount of cement used for later maintenance.This provides an idea for achieving sustainability goals in civil engineering.
基金Funded by the National Basic Research Program of China(973 Program)(No.2009CB623201)
文摘Effects of polycarboxylate-type superplasticizer(PC) molecular structure on the hydration heat of tricalcium silicate(C3S) paste and polymerization degree of hydration products(C-S-H gel) were researched by using TAM AIR isothermal microcalorimetry(TA) and 29Si nuclear magnetic resonance(NMR).Methoxy polyethylene glycol-methacrylates-based polycarboxylate superplasticizers with different side chain lengths and main chain lengths were employed.PC molecules with shorter main chain or longer side chains caused stronger retardation of C3S early hydration and lesser increase of C3S 3 d hydration degree.NMR measurement indicated that the incorporation of PC increased the hydration degree of C3S paste and the polymerization degree of silicon-oxygen tetrahedron of C-S-H gel.The tendency for C3S 7 d hydration degree to improve was more pronounced while PC molecules with longer main chain or shorter side chain were added.Whereas,PC molecules with longer main chains or longer side chains increased the 7 d polymerization degree of C-S-H gel.
基金Funded by the Western Region Traffic Construction Technology Program of the Ministry of Transport of China(No.2007319811130)
文摘Bridge polycarboxylate superplasticizers(PCs) with crosslink structure were synthesized by using polyethyleneglycol di-acrylate(PEGdA), replacing partial polyethyleneglycol mono-acrylate (PEGmA) as crosslinking agent. Structures of bridge PCs were analyzed by gel permeation chromatography, and dispersion ability was evaluated by cement paste dispersity variation on time and rheology test. The experimental results showed that, molecular weight(MW) of bridge PCs increased with increase of PEGdA proportion, and MW distribution curve changed from Gaussian to fiat like, which meant notable increase of highly crosslinked copolymer. Bridge PCs led to decreased initial cement paste dispersity and better dispersity retention due to slow releasing. Further research showed that, PEGdA proportion had slight effect on polymerization degree of backbone, MW distribution of backbone deviated from Gaussian distribution and shoulder peaks appeared on distribution curve when PEGdA increased.
基金Funded by the National Natural Science Foundation of China(Nos.51132010 and 51272222)the Programs for Science and Technology Development of Yantai City,Shandong Province,China(No.2012ZH249)
文摘Circulating fluidized bed combustion (CFBC) ash exhibits the desirable pozzolanic activity which makes it a potential supplementary cementitious material to replace cement for concrete production. However, the high unburnt carbon content and porous surface structure of CFBC ash may adsorb water reducer and thereby significantly reduce the efficiency of water-reducing agents. The adsorption mechanism of polycarboxylate superplasticizer in CFBC ash-Portland cement paste was investigated by ultraviolet-visible spectrophotometer, and the conception of "invalid adsorption site" of CFBC ash was presented. The results show that the adsorption behavior of polycarboxylate superplasticizer in coal ash-Portland cement paste can be described by Langmuir isothermal adsorption equation. The adsorption capacity of CFBC ash-Portland cement paste is higher than that of pulverized coal combustion (PCC) fly ash-Portland cement paste. Moreover, the adsorption amount of polycarboxylate superplasticizer increases with the ratio of ash-to-cement in the paste. At last, the fluidity of CFBC ash-Portland cement paste is lower than that of the PCC fly ash paste. This work suggests that when CFBC ash is used as concrete admixture, the poor flowability of the cementitious system due to the high adsorption of water and water-reducing agent should be taken into consideration.
基金the State Key Laboratory of Silicate Materials for Architectures(SYSJJ2018-09)the Shaanxi Provincial High Performance Concrete Engineering Laboratory(SHPC201701)
文摘Molecular structures of polycarboxylate(PCE) superplasticizer significantly affect the rheological properties of cement paste. Consequently, we employed self-synthesized PCE copolymers with different carboxylic densities to investigate their influence on the rheological behavior of cement paste. Three typical rheological models were applied to analyze the rheological properties, including Power-law model, Bingham model as well as Herschel-Buikley model. In addition, the thixotropical performances of cement paste in the presence of PCE with different carboxylic densities were investigated. The results show that the carboxylic density of PCE greatly influences the dispersing performance of PCE superplasticizers. As carboxylic density increases, the dispersing capability of PCE improves, and P(PEG1-AA6) possesses the strongest dispersing capability, the initial fluidity and 1 h fluidity of cement paste are both the highest, and cement paste has the lowest viscosity and the smallest hysteresis loop.
文摘The dispersion ability of polycarboxylate superplasticizer(PCE) in fresh concrete was much impeded by clay impurities. To improve the dispersion of PCE in the clay-contained concrete, a novel PCE with carboxyl as a specific branched chain terminal group was synthesized, using modified polyether as the raw material which was prepared through esterification between hexahydrophthalic anhydride(HHPA) and isobutenyl polyoxyethylene ether(IPEG) with hydroxy as the terminal group. The esterification product and PCE molecular structure were characterized by infrared spectroscopy and ~1HNMR resonance. The results confirmed that the product molecular structure was a comb-type copolymer with long-chain terminal carboxyl group and PEO attached directly to the backbone chain. The as-synthesized PCEs had favorable dispersibility in cement than conventional PCE in the presence of montmorillonite(Mmt) clay. This can be attributed to the introduction of electronegative carboxyl to PCE long-chain terminal group, which reduces the adsorption of PCE on Mmt, and thus improves the tolerance of PCE to the Mmt.
基金Funded by the National Natural Science Foundation of China(No.50972170)
文摘The effects of various factors on the synthesis process and the performances of product, including batch feeding way and the dosage of the radical initiator, the system concentration, the reaction temperature and the reaction time were discussed. A kind of polycarboxylate superplasticizer with allyl alcohol polyethylene glycol, maleic anhydride and methacrylic acid sulfonic sodium as main raw materials has been synthesized. Their relative effectiveness as dispersants was evaluated in cement paste by measuring paste fluidity. The optimum parameters of technology and the appropriate proportion of raw materials were obtained. As a result,the new high performance superplasticizer suitable for high-performance concrete has been synthesized. The structure of copolymer was characterized and analyzed by FT-IR spectra. Results indicated that product copolymer structure was consistent with the ideal molecular structure designed.
基金Funded by the National Natural Science Foundation of China(50872151)the Beijing Municipal Education Commission Program Projects and Beijing University of Civil Engineering and Architecture,Dr.Fund
文摘The infl uence law of clay on mortar fluidity mixed with polycarboxylate superplasticizer was studied. Several methods of inhibiting clay adsorption of polycarboxylate superplasticizer were discussed. The experimental results show that clay has signifi cant effect on the dispersion of polycarboxylate superplasticizer and montmorillonite clay has more signifi cant impact on mortar fluidity than other clays. The pH value and the salts of the solution can affect the adsorption of clay to polycarboxylate superplasticizer. The incorporation of a small amount of sodium hydroxide solution, sodium silicate or cationic surfactants can improve the effect of the clay on the dispersion of polycarboxylate superplasticizer.
基金Funded by National Natural Science Foundation of China(No.51778378)。
文摘A low adsorption clay-resistant polycarboxylate superplasticizer(KN-PC)was synthesized using acrylic acid and isopentenol polyoxyethylene ether as the main reaction materials.The structural characterization and clay-resistant mechanism of the KN-PC were explored using Fourier transform infrared spectroscopy and X-ray diffraction,and the effect of the KN-PC on the performance of composite paste with various montmorillonite(MMT)contents was analyzed.Compared with ordinary polycarboxylate superplasticizer(PC),the KN-PC has a low sensitivity to the MMT.By the action of the MMT,the adsorption dosage of the KN-PC on the MMT is much smaller than that of the PC.
基金Funded by the Western Region Traffic Construction Technology Program of the Ministry of Communications of China(No.2007319811130)
文摘A procedure was developed for the determination of residual monomers in polycarboxylate superplasticizer (PCs) by reversed-phase high performance liquid chromatography (RP-HPLC).Four kinds of residual monomers were well separated and determined on a SinoChrom ODS-BP (C18) column with mobile phases composed of acetonitrile and phosphate buffer solution.The monomers were detected by UV detector at 205 nm and quantitatively analyzed with an external standard method.For those residual monomers,the linear response ranged from 4.0×10-6 mol·L-1 to 2.0×10-3 mol·L-1.The determination limit of acrylic acid,sodium methylallyl sulfonate and 2-Acrylamido-2-methylpropane sulfonic acid was 0.02×10-5 mol·L-1,while that of methoxy-polyethylene glycol monoacrylate was 0.1×10-5 mol·L-1.The relative standard deviation (RSD) of high concentration samples was less than 1%,while that of the low concentration samples was between 1%-4%.The standard (additional) recovery ratio was 97.4% -104.2%.
基金Funded by the Western Region Traffic Construction Technology Program of the Ministry of Communications of China(No.2007319811130)
文摘A series of polycarboxylate-based superplasticizers(PCs) with different structures were synthesized and the effects of chemical structure on zeta potential and rheological property of cement paste were studied. Residual monomers in each sample of PCs were quantitatively determined. The property of the polymers in cement was tested by micro-electrophoresis apparatus and R/S rheometer. Results showed that the zeta potential and its rheological properties are related with the side-chain length and density of PCs. The PCs having shorter side chain and lower side chain density exhibit higher anionic charge density, thus resulting in higher zeta potential. The effect of side chain density on zeta potential is more notable compared with that of side-chain length, and thus affecting the initial shear yield stress and apparent viscosity of the cement paste. In addition, although increasing the side chain length will result in reduction of the anionic charge density, the steric hindrance effect is obvious, which can effectively improve the dispersion of the cement particles, and reduce the viscosity and shear yield stress of slurry.
基金Funded by the National Key Research and Development Program of China(2017YFC0602903)the National Natural Science Foundation of China(51834001)
文摘The effects of circulating fluid bed(CFB) ash on the adsorption performance of polycarboxylate superplasticiser and the mechanism of this influence on the dispersive property of the polycarboxylate superplasticiser were investigated by determing the cement paste fluidity, total organic carbon adsorption, infrared spectroscopic analyses and ζ potential test. The experimental results show that the addition of an inorganic salt into the mixture to change the content of SO42-and Fe2O3can improve the adaptability between the CFB ash and polycarboxylate superplasticiser. Adsorption may occur between the polycarboxylate superplasiciser and Fe2O3, SO42-or other components in CFB ash, leading to a significant reduction in paste fluidity. As the content of Na2SO4in CFB ash reaches 3% or Fe2O3reaches 9%, the paste loses its liquidity. The organic carbon content in the liquor decreases with an increase in Na2SO4or Fe2O3content. Adding some Ba(NO3)2and Na2S to the liquor can recover the organic carbon content to a certain extent, and the absolute value of ζ potential will increase. The addition of Ba(-NO3)2or Na2S reduces the adsorption property of Na2SO4or Fe2O3in CFB ash on the polycarboxylate superplasticiser.
文摘Influences of different superplasticizers ( STP. KSJSTO and LMS-P) on rheological behavior of low-cement castables and the mechanisms were analyzed. The shear stress and viscosity under different shear rates of matrix slurry were determined using a NXS-I IA rotary viscometer. Effects of different admixtures on the rheological properties of slurry was analyzed theoretically. Sodium tripolyphosphate and poly'carboxylate superplasticizers KS-JSTO and LMS-P) can improve the fluidity and initial setting time. With STP. the slurry is plastic flow. With KS-JS70 or LMS-P increasing, the slurrv changes from plastic.flow, pseudoplastic flow to dilatant flow successively. Th, e optimum dosages of STP. KS-JSTO and LMS-P are 0. 15%. 0. 25% and 0. 40%, respectively. KS-JS70 and LMS-P can significantly reduce the slurry viscosity and shear stress to improve the workability of construction. Both shear stress and viscosity shall be taken into account for on-site construction.
文摘A new kind of polycarboxylate superplasticizer with high slump loss resistance was obtained by designing scheduled molecular structure.The number average molecular mass of the polymer was characterized by the gel permeation chromatography measurements.And chemical structure of the polymer was observed by the Fourier transform infrared spectroscopy(FT-IR).The results show that the good workable maintaining of self-compacting concrete could be achieved through direct adjustment of number average molecular mass and different unsaturated monomer in synthetic process.The FT-IR analysis illustrated that the high slump loss resistance of polycarboxylate superplasticizers with ester and carboxyl group and expectations of molecular structure were designed.
基金Funded by the National Natural Science Foundation of China(No. 50872151)
文摘Polycarboxylate(PC) superplasticizers with different chemical structures were synthesized through free radical co-polymerization reaction.A total organic carbon analyzer was used to investigate adsorption behaviors of PCs,and to evaluate influences of soluble salts on absorption properties of PCs.It is found that adsorption ratios of PCs on cement particles decrease greatly with the addition of Na2SO4;the adsorption ratio of ethers PC with Hydroxyethyl methacrylate(HEMA) group first increases then decreases with the addition of NaCl;the adsorption ratio of esters PC with short side chains first decreases then increases,while the adsorption ratio of ethers PC with HEMA group decreases with the addition of CaCl2;the adsorption ratio of esters PC with short side chains decreases with the addition of Ca(NO3)2;AlCl3 causes the decrease of the adsorption ratio of ethers PC with HEMA group.
基金This project is supported by the National Natural Science Foundation of China.
文摘The polymerization of acrylonitrile (AN) in aqueous nitric acid initiated by ' cage ' vanadyl polycarboxylate (P=VO)-thiourea (TU) complex was investigated. The overall rate ofpolymerization isThe relationship between the induction period (τ) and the temperature of polymerization as well as the concentrations of reactants can be expressed as follows :The molecular weight of polyacrylonitrile increases with increasing monomer concentration and decreases with increasing temperature of polymerization and concentrations of vanadyl polycarboxylate and thioureaThe polymerization mechanism was proposed and discussed.
文摘Polycarboxylate water-reducing admixture possesses the capability which could meet with the comprehensive performance of high performance concrete used in passenger dedicated line engineering.The problems of polycarboxylates water-reducing admixtures existed in the engineering application of were analyzed.At present the key for polycarboxylates application was to settle the compatibility between the water-reducing admixture and the cement and to keep the quality retention of this admixture.