The discarded feathers / ethylene vinyl acetate copolymer( EVA) thermoplastic composite materials was obtained with discarded feathers as reinforced material and EVA powders as matrix material by hot pressing method. ...The discarded feathers / ethylene vinyl acetate copolymer( EVA) thermoplastic composite materials was obtained with discarded feathers as reinforced material and EVA powders as matrix material by hot pressing method. Sound absorption properties were studied by changing mass ratio of discarded feathers and EVA,thickness of composite materials,hot pressing pressure and hot pressing temperature. It was found that the sound absorption properties of composite materials were good when the mass ratio of discarded feathers and EVA was 1: 1,thickness of composite materials was 30 mm,hot pressing pressure was 8 MPa,and hot pressing temperature was 80 ℃. Under the optimum conditions,the effect of composite density on sound absorption property was analyzed. In a certain range,the sound absorption property was enhanced with the decrease of the composite density.When the composite density was 0. 1g /cm^3, the maximum absorption coefficient was 0.96. Finally,the capillary theory was used to calculate the maximum sound absorption coefficient of discarded feathers / EVA thermoplastic composite materials. The good agreements of experimental results and calculated results proved the validity of the theoretical models.展开更多
Sepiolite （S9, B10, B20, B40） and boehmite have been added to an intumecent flame retardant （IFR） system to produce the halogen-free and fire-resistant ethylene-vinyl acetate copolymer （EVM） rubber. The rubber c...Sepiolite （S9, B10, B20, B40） and boehmite have been added to an intumecent flame retardant （IFR） system to produce the halogen-free and fire-resistant ethylene-vinyl acetate copolymer （EVM） rubber. The rubber contains ammonium polyphosphate （APP） as acid source, double pentaerythritol （D-PER） as carbon source and melamine （MN） as gas source. The effects of nano-filler sepiolite and boehmite on the fire-resistant property of EVM rubber based on IFR system were investigated. The test results show that the system with nano-filler of sepiolite B10 has the best fire-resistant property. The process of smoke emission and thermal decomposition, the element composition of char surface and the micro morphology of intumecent char layer of the EVM IFR system with nano-filler were also studied by NBS chamber, thermogravimetric （TG） analysis, X- ray photoelectron spectroscopy （XPS） and scanning electron microscope （SEM）.展开更多
Hydrogels composed of poly(vinyl alcohol)(PVA) and poly(ethylene glycol)(PEG) were synthesized using glutaraldehyde as crosslinker and investigated for controlled delivery of the common anti-inflammatory drug, ibuprof...Hydrogels composed of poly(vinyl alcohol)(PVA) and poly(ethylene glycol)(PEG) were synthesized using glutaraldehyde as crosslinker and investigated for controlled delivery of the common anti-inflammatory drug, ibuprofen(IBF). To regulate the drug delivery, solid inclusion complexes(ICs) of IBF in β–cyclodextrin(β–CD) were prepared and added to the hydrogels. The ICs were prepared by the microwave irradiation method, which is more environmentally benign. The formation of IC was confirmed by various analytical techniques and the synthesized hydrogels were also characterized. Controlled release of drug was achieved from the hydrogels containing the ICs in comparison to the rapid release from hydrogels containing free IBF.The preliminary kinetic analysis emphasized the crucial role of β–CD in the drug release process that influences the polymer relaxation, thereby leading to prolonged release. The cytotoxicity assay validated the hydrogels as non-toxic in nature and hence can be utilized for controlled delivery of IBF.展开更多
Poly （ethyleneglycol monomethylether） methacrylate （PEGMM）was synthesized by means of the reaction of methacrylyl chloride with sodium monomethylpolyethyleneglycoxide and was characterized by FTIR,;H-NMR,and ultra...Poly （ethyleneglycol monomethylether） methacrylate （PEGMM）was synthesized by means of the reaction of methacrylyl chloride with sodium monomethylpolyethyleneglycoxide and was characterized by FTIR,;H-NMR,and ultraviolet spectrometries. A series of poly （vinyl alcohol）-graft-PEGMM （PVA-g-PEGMM ）and methyl methacrylate-PEGMM copolymer （PMMA-PEGMM） were prepared and tested for antithrombogenicity in vitro. The results indicate that the antithrombogenicity of the copolymers basically increases with the increasing of the DP of polyoxyethylene （POE） chain and tends to a plateau after the DP around 114,i.e. the long chain structure of POE is favourable to the antithrombogenicityof its copolymers ;moreover, the extent of the improvement ofantithrombogenicity also relates to the PEGMM content of the copolymers and the kind of the matrix that the POE chains are located on. These results are consistent with the anticipation of the hypothesis of maintaining proteins normal conformations for blood compatible bioraaterials.展开更多
文摘The discarded feathers / ethylene vinyl acetate copolymer( EVA) thermoplastic composite materials was obtained with discarded feathers as reinforced material and EVA powders as matrix material by hot pressing method. Sound absorption properties were studied by changing mass ratio of discarded feathers and EVA,thickness of composite materials,hot pressing pressure and hot pressing temperature. It was found that the sound absorption properties of composite materials were good when the mass ratio of discarded feathers and EVA was 1: 1,thickness of composite materials was 30 mm,hot pressing pressure was 8 MPa,and hot pressing temperature was 80 ℃. Under the optimum conditions,the effect of composite density on sound absorption property was analyzed. In a certain range,the sound absorption property was enhanced with the decrease of the composite density.When the composite density was 0. 1g /cm^3, the maximum absorption coefficient was 0.96. Finally,the capillary theory was used to calculate the maximum sound absorption coefficient of discarded feathers / EVA thermoplastic composite materials. The good agreements of experimental results and calculated results proved the validity of the theoretical models.
基金Sponsored by Project in National Key Technology R&D Program(2006BAE03B05-2)
文摘Sepiolite （S9, B10, B20, B40） and boehmite have been added to an intumecent flame retardant （IFR） system to produce the halogen-free and fire-resistant ethylene-vinyl acetate copolymer （EVM） rubber. The rubber contains ammonium polyphosphate （APP） as acid source, double pentaerythritol （D-PER） as carbon source and melamine （MN） as gas source. The effects of nano-filler sepiolite and boehmite on the fire-resistant property of EVM rubber based on IFR system were investigated. The test results show that the system with nano-filler of sepiolite B10 has the best fire-resistant property. The process of smoke emission and thermal decomposition, the element composition of char surface and the micro morphology of intumecent char layer of the EVM IFR system with nano-filler were also studied by NBS chamber, thermogravimetric （TG） analysis, X- ray photoelectron spectroscopy （XPS） and scanning electron microscope （SEM）.
文摘Hydrogels composed of poly(vinyl alcohol)(PVA) and poly(ethylene glycol)(PEG) were synthesized using glutaraldehyde as crosslinker and investigated for controlled delivery of the common anti-inflammatory drug, ibuprofen(IBF). To regulate the drug delivery, solid inclusion complexes(ICs) of IBF in β–cyclodextrin(β–CD) were prepared and added to the hydrogels. The ICs were prepared by the microwave irradiation method, which is more environmentally benign. The formation of IC was confirmed by various analytical techniques and the synthesized hydrogels were also characterized. Controlled release of drug was achieved from the hydrogels containing the ICs in comparison to the rapid release from hydrogels containing free IBF.The preliminary kinetic analysis emphasized the crucial role of β–CD in the drug release process that influences the polymer relaxation, thereby leading to prolonged release. The cytotoxicity assay validated the hydrogels as non-toxic in nature and hence can be utilized for controlled delivery of IBF.
文摘Poly （ethyleneglycol monomethylether） methacrylate （PEGMM）was synthesized by means of the reaction of methacrylyl chloride with sodium monomethylpolyethyleneglycoxide and was characterized by FTIR,;H-NMR,and ultraviolet spectrometries. A series of poly （vinyl alcohol）-graft-PEGMM （PVA-g-PEGMM ）and methyl methacrylate-PEGMM copolymer （PMMA-PEGMM） were prepared and tested for antithrombogenicity in vitro. The results indicate that the antithrombogenicity of the copolymers basically increases with the increasing of the DP of polyoxyethylene （POE） chain and tends to a plateau after the DP around 114,i.e. the long chain structure of POE is favourable to the antithrombogenicityof its copolymers ;moreover, the extent of the improvement ofantithrombogenicity also relates to the PEGMM content of the copolymers and the kind of the matrix that the POE chains are located on. These results are consistent with the anticipation of the hypothesis of maintaining proteins normal conformations for blood compatible bioraaterials.