Sepiolite （S9, B10, B20, B40） and boehmite have been added to an intumecent flame retardant （IFR） system to produce the halogen-free and fire-resistant ethylene-vinyl acetate copolymer （EVM） rubber. The rubber c...Sepiolite （S9, B10, B20, B40） and boehmite have been added to an intumecent flame retardant （IFR） system to produce the halogen-free and fire-resistant ethylene-vinyl acetate copolymer （EVM） rubber. The rubber contains ammonium polyphosphate （APP） as acid source, double pentaerythritol （D-PER） as carbon source and melamine （MN） as gas source. The effects of nano-filler sepiolite and boehmite on the fire-resistant property of EVM rubber based on IFR system were investigated. The test results show that the system with nano-filler of sepiolite B10 has the best fire-resistant property. The process of smoke emission and thermal decomposition, the element composition of char surface and the micro morphology of intumecent char layer of the EVM IFR system with nano-filler were also studied by NBS chamber, thermogravimetric （TG） analysis, X- ray photoelectron spectroscopy （XPS） and scanning electron microscope （SEM）.展开更多
Ethylene-vinyl acetate copolymer(EVA) as a kind of effective polymeric pour point depressant has been extensively used in the pipeline transportation of crude oil to inhibit wax deposition and improve the low temperat...Ethylene-vinyl acetate copolymer(EVA) as a kind of effective polymeric pour point depressant has been extensively used in the pipeline transportation of crude oil to inhibit wax deposition and improve the low temperature fluidity of crude oil. In this work, molecular dynamics simulations were performed to investigate the effect of EVA on wax-hydrate coexistence system to evaluate the application potentiality of EVA to the flow assurance of deep-sea oil-gas-water multiphase flow system. Our simulation results reveal that wax molecules gradually stretched and stacked from random coiling to a directional and ordered crystalline state during the process of wax solidification. The strong affinity of polar vinyl acetate side chains of EVA to neighboring water molecules made the EVA molecule prefer being in a curly state,which disrupted the ordered crystallization of surrounding wax molecules and delayed the solidification rate of wax cluster. In addition, it is found that EVA cocrystallized with wax molecules to form eutectic when the wax was fully solidified. The simulation results of hydrate nucleation and growth show that the EVA molecule displayed a two-sided effect on gas adsorption of wax crystals, which was the key factor that affected the nucleation and growth of hydrates in the methane-water system. The nonpolar hydrocarbon backbone of EVA increased the diffusion rate of methane and water, allowing more methane to diffuse to the surface of wax crystals, reducing the methane concentration in aqueous solutions and inhibiting the hydrate formation. On the other hand, the nonpolar vinyl acetate chains had a repulsive effect on methane, which reduced the adsorption area of methane on the eutectic surface and decreased the adsorption threshold value of the wax crystal. The excluded methane molecules would continue dissociating in the aqueous phase and participating in the nucleation and growth process of hydrates.Therefore, the probability of hydrate formation would be increased. It was worth noting that the inhibition performance of EVA on hydrate formation mainly played a significant role in the system with small wax crystal, while its hydrate promotion effect played a dominant role in the system with lager wax crystal. In summary, EVA could significantly inhibit both of the wax and hydrate deposition for the waxgas-water multiphase system with low wax content. When the wax content in the system was high, the role of EVA was mainly played in the alleviation of wax crystallization rather than the gas hydrates. The results of the present work can contribute to a better understanding of EVA on wax deposition and hydrate formation, and provide theoretical support of the potential industrial applications of EVA.展开更多
为了获得热稳定、阻燃和力学性能均较好的复合材料,以高密度聚乙烯/乙烯-醋酸乙烯酯(HDPE/EVA)共混物为基体,可膨胀石墨(EG)作为无卤阻燃剂,通过熔融共混方法制备了HDPE/EVA/EG阻燃复合材料.采用热重分析(TGA)、锥形量热仪、电子扫描电...为了获得热稳定、阻燃和力学性能均较好的复合材料,以高密度聚乙烯/乙烯-醋酸乙烯酯(HDPE/EVA)共混物为基体,可膨胀石墨(EG)作为无卤阻燃剂,通过熔融共混方法制备了HDPE/EVA/EG阻燃复合材料.采用热重分析(TGA)、锥形量热仪、电子扫描电镜(SEM)等方法研究了钛酸酯偶联剂改性前后EG对复合材料的热稳定性能、阻燃性能以及力学性能的影响.研究结果表明,EG能提高聚合物基体材料的热稳定性能和阻燃性能,但力学性能降低;用钛酸酯偶联剂对EG改性后,HDPE/EVA/EG复合材料的断裂伸长率从232.3%提高到315.3%,拉伸强度由9.0 MPa增到了10.0 MPa,冲击强度由88 k J/m2提高到129 k J/m2.偶联剂的存在提高了EG与基体间的界面粘结力,使阻燃复合材料的综合力学性能得到改善.展开更多
基金Sponsored by Project in National Key Technology R&D Program(2006BAE03B05-2)
文摘Sepiolite （S9, B10, B20, B40） and boehmite have been added to an intumecent flame retardant （IFR） system to produce the halogen-free and fire-resistant ethylene-vinyl acetate copolymer （EVM） rubber. The rubber contains ammonium polyphosphate （APP） as acid source, double pentaerythritol （D-PER） as carbon source and melamine （MN） as gas source. The effects of nano-filler sepiolite and boehmite on the fire-resistant property of EVM rubber based on IFR system were investigated. The test results show that the system with nano-filler of sepiolite B10 has the best fire-resistant property. The process of smoke emission and thermal decomposition, the element composition of char surface and the micro morphology of intumecent char layer of the EVM IFR system with nano-filler were also studied by NBS chamber, thermogravimetric （TG） analysis, X- ray photoelectron spectroscopy （XPS） and scanning electron microscope （SEM）.
基金financial support received from National Natural Science Foundation of China(22178378 and 22127812)"Tianchi Talent"Recruitment Program,Xinjiang Tianshan Innovation Team(2022TSYCTD0002)Xinjiang Uygur Region"One Case,One Policy"Strategic Talent Introduction Project(XQZX20240054)are gratefully acknowledged.
文摘Ethylene-vinyl acetate copolymer(EVA) as a kind of effective polymeric pour point depressant has been extensively used in the pipeline transportation of crude oil to inhibit wax deposition and improve the low temperature fluidity of crude oil. In this work, molecular dynamics simulations were performed to investigate the effect of EVA on wax-hydrate coexistence system to evaluate the application potentiality of EVA to the flow assurance of deep-sea oil-gas-water multiphase flow system. Our simulation results reveal that wax molecules gradually stretched and stacked from random coiling to a directional and ordered crystalline state during the process of wax solidification. The strong affinity of polar vinyl acetate side chains of EVA to neighboring water molecules made the EVA molecule prefer being in a curly state,which disrupted the ordered crystallization of surrounding wax molecules and delayed the solidification rate of wax cluster. In addition, it is found that EVA cocrystallized with wax molecules to form eutectic when the wax was fully solidified. The simulation results of hydrate nucleation and growth show that the EVA molecule displayed a two-sided effect on gas adsorption of wax crystals, which was the key factor that affected the nucleation and growth of hydrates in the methane-water system. The nonpolar hydrocarbon backbone of EVA increased the diffusion rate of methane and water, allowing more methane to diffuse to the surface of wax crystals, reducing the methane concentration in aqueous solutions and inhibiting the hydrate formation. On the other hand, the nonpolar vinyl acetate chains had a repulsive effect on methane, which reduced the adsorption area of methane on the eutectic surface and decreased the adsorption threshold value of the wax crystal. The excluded methane molecules would continue dissociating in the aqueous phase and participating in the nucleation and growth process of hydrates.Therefore, the probability of hydrate formation would be increased. It was worth noting that the inhibition performance of EVA on hydrate formation mainly played a significant role in the system with small wax crystal, while its hydrate promotion effect played a dominant role in the system with lager wax crystal. In summary, EVA could significantly inhibit both of the wax and hydrate deposition for the waxgas-water multiphase system with low wax content. When the wax content in the system was high, the role of EVA was mainly played in the alleviation of wax crystallization rather than the gas hydrates. The results of the present work can contribute to a better understanding of EVA on wax deposition and hydrate formation, and provide theoretical support of the potential industrial applications of EVA.
文摘为了获得热稳定、阻燃和力学性能均较好的复合材料,以高密度聚乙烯/乙烯-醋酸乙烯酯(HDPE/EVA)共混物为基体,可膨胀石墨(EG)作为无卤阻燃剂,通过熔融共混方法制备了HDPE/EVA/EG阻燃复合材料.采用热重分析(TGA)、锥形量热仪、电子扫描电镜(SEM)等方法研究了钛酸酯偶联剂改性前后EG对复合材料的热稳定性能、阻燃性能以及力学性能的影响.研究结果表明,EG能提高聚合物基体材料的热稳定性能和阻燃性能,但力学性能降低;用钛酸酯偶联剂对EG改性后,HDPE/EVA/EG复合材料的断裂伸长率从232.3%提高到315.3%,拉伸强度由9.0 MPa增到了10.0 MPa,冲击强度由88 k J/m2提高到129 k J/m2.偶联剂的存在提高了EG与基体间的界面粘结力,使阻燃复合材料的综合力学性能得到改善.