Preparation and characterization of conducting polymer-coated thermally expandable microspheres

The thermally expandable microspheres（TEMs） were prepared via suspension polymerization with acrylonitrile（AN）, methyl methacrylate（MMA） and methyl acrylate（MA） as monomers and n-hexane as the blowing agent. Meanwhile, a novel type of functional and conductive thermal expandable microsphere was obtained through strongly covering the surface of microsphere by conductive polymers with the mass loading of 1.5%. The optimal conditions to prepare high foaming ratio and equally distributed microcapsules were investigated with AN-MMA-MA in the proportion of 70%/20%/10%（m/m/m）, and 25 wt% of n-hexane in oil phase. The further investigation results showed that the unexpanded TEMs were about 30 μm in diameter and the maximum expansion ratio was nearly 125 times of original volume. The polypyrrole（PPy） was smoothly coated on the surface of the TEMs and the expansion property of PPy-coated TEMs was almost the same as the uncoated TEMs. Moreover, the structure and expanding performance of TEMs and PPy-coated TEMs were characterized by scanning electron microscopy（SEM）, laser particle size analyzer and dilatometer（DIL）.

Preparation and properties of thermoexpandable polymeric microspheres

In this paper, thermoexpandable polymeric microspheres were prepared by suspension polymerization with acrylonitrile （AN） and methyl methacrylate （MMA） as monomers and/-butane as a blowing agent. The micromorphology and thermal stability were researched by polarized microscopy and TGA. The diameter of the expandable microspheres increased from about 20μm （unexpanded） to 40-80 μm （expanded） upon heating. The maximum expansion volume was higher than 22 times of the original volume and the density of the expanded microspheres was about 16.7 kg/m3. The blowing agent content in microspheres was about 20 wt% and To.e., Tm.e. and To.s. were 80℃, 120-130℃ and 140-145℃, respectively.

Constructing mild expanded graphite microspheres by pressurized oxidation combined microwave treatment for enhanced lithium storage

The modified graphite anode materials have some prominent advantages over other anode materials in the industrial applications.A novel simple and gentle method is proposed to synthesize the mild expanded graphite microspheres(MEGMs) from flake graphite spheres through a combined modified pressurized oxidation combined with the microwave treatment.The microstructural results demonstrate that moderately expanded MEGMs with an expansion volume between 4 and 10 ml·g^(-1)exhibit a highly microporous structure with an enlarged interlayer spacing,a decreased microcrystalline size,as well as an increased number of functional groups on the surface,resulting in the increased storage sites and spaces for lithium ions and the enhanced diffusion rate of lithium ions.When used as the anode material for lithium-ion batteries,the MEGM-T75t30 obtained by oxidation treatment at 75℃ for 30 min followed by microwave irradiation for expansion displays a high reversible capacity of 446.7 mAh·g^(-1) at 100 mA·g^(-1) after 100 cycles and excellent rate performance(330 and 116 mAh·g^(-1) at 800 and 3200 mA·g^(-1),respectively).Therefore,the MEGMs prepared by this convenient and mild method show excellent electrochemical properties and good application potential.