Cordierite honeycomb ceramics was treated with 1.5 M HNO3 , followed with 1.5 M NaOH at 93 ℃. The combination of acid treatment with alkali treatment significantly diminished the rebounding of coefficient of thermal ...Cordierite honeycomb ceramics was treated with 1.5 M HNO3 , followed with 1.5 M NaOH at 93 ℃. The combination of acid treatment with alkali treatment significantly diminished the rebounding of coefficient of thermal expansion （CTE） caused by heat treatment, a phenomenon observed in samples treated solely with acid. Inductively coupled plasma （ICP） analysis results reveal that the alkali treatment preferentially dissolved ＂free＂ SiO2 left in the acid-treated samples, which is considered to be a key factor responsible for the CTE rebounding.展开更多
Beryllium aluminum cyclosilicate, an ore of beryllium was reinforced in Aluminum matrix to fabricate Al-beryl composites using powder metallurgy. Effect of the content of beryllium aluminum cyclosilicate on microstruc...Beryllium aluminum cyclosilicate, an ore of beryllium was reinforced in Aluminum matrix to fabricate Al-beryl composites using powder metallurgy. Effect of the content of beryllium aluminum cyclosilicate on microstructural hardness and thermal expansion was studied. The coefficient of thermal expansion of Al-beryl composite was measured in the temperature range between 50oC to 360oC using dilatometer and was theoretically studied using thermo-elastic models, and these models were used to explain abnormalities observed experimentally. The hardness of Al-beryl metal matrix composites increased with the increase in beryl percentage. Vacuum sintering of Al-beryl metal matrix composites at 600oC inhibited excellent bonding between the matrix and the particulate increasing the strength of the composite. The result shows the CTE significantly increased with increasing temperature but decreased with increasing reinforcement. At higher temperatures, CTE of Al-beryl metal matrix composites with 5 wt%, 10 wt% and 15 wt% of beryllium aluminum cyclosilicate was 21 ppm/K, 18.2 ppm/K, and 16.8 ppm/K. The CTE values were found to be comparable with theoretical results. The turner model showed conformance with experimental results, was well suited to the experimental results.展开更多
A novel material of ZrMnMo3012 with negative thermal expansion is presented. The phase transition temperature and coemcient of thermal expansion （CTE） are investigated by temperature-dependent x-ray diffraction and ...A novel material of ZrMnMo3012 with negative thermal expansion is presented. The phase transition temperature and coemcient of thermal expansion （CTE） are investigated by temperature-dependent x-ray diffraction and Raman spectra. It is shown that ZrMnMo3012 adopts monoclinic structure with space group P21/a （No. 14） from 298 to 358K and transforms to orthorhombic with space group Pnma （No. 62） above 363K. The linear CTE obtained from the results of XRD refinement is -2.80 × 10-6 K-1 from 363 to 873 K. The CTE of the bulk cylinder ceramic measured by a thermal dilatometer is -4.7× 10-6 K-1 from 373 to 773K approximatively.展开更多
The thermal expansion mismatch between cement mortar and aggregate at high temperature is one of the main reasons causing the deterioration of concrete at high temperature.In this study,the thermal damage of concrete ...The thermal expansion mismatch between cement mortar and aggregate at high temperature is one of the main reasons causing the deterioration of concrete at high temperature.In this study,the thermal damage of concrete caused by the thermal expansion mismatch between aggregate and cement mortar was investigated using a meso-scale concrete model.The meso-scale concrete model is composed of mortar,aggregate and the interfacial transition zone(ITZ).Laboratory tests on the mechanical properties of cement mortar at high temperature were conducted to provide the necessary mechanical parameter for the meso-scale concrete model.The simulation results show that the particle size,content,distribution and mechanical properties of the aggregate have an effect on the thermal damage of concrete at high temperature.The smaller the particle size of concrete aggregate and the higher the elastic modulus of aggregate,the greater the damage of concrete under high temperature.Due to the increasing thermal expansion difference between aggregate and cement mortar,and the deterioration of the cement mortar with the increasing temperature,the damage of concrete increased sharply after 500℃.展开更多
基金Funded bythe International Cooperation Project of Jiangsu Prov-ince(No.BZ2001043)
文摘Cordierite honeycomb ceramics was treated with 1.5 M HNO3 , followed with 1.5 M NaOH at 93 ℃. The combination of acid treatment with alkali treatment significantly diminished the rebounding of coefficient of thermal expansion （CTE） caused by heat treatment, a phenomenon observed in samples treated solely with acid. Inductively coupled plasma （ICP） analysis results reveal that the alkali treatment preferentially dissolved ＂free＂ SiO2 left in the acid-treated samples, which is considered to be a key factor responsible for the CTE rebounding.
文摘Beryllium aluminum cyclosilicate, an ore of beryllium was reinforced in Aluminum matrix to fabricate Al-beryl composites using powder metallurgy. Effect of the content of beryllium aluminum cyclosilicate on microstructural hardness and thermal expansion was studied. The coefficient of thermal expansion of Al-beryl composite was measured in the temperature range between 50oC to 360oC using dilatometer and was theoretically studied using thermo-elastic models, and these models were used to explain abnormalities observed experimentally. The hardness of Al-beryl metal matrix composites increased with the increase in beryl percentage. Vacuum sintering of Al-beryl metal matrix composites at 600oC inhibited excellent bonding between the matrix and the particulate increasing the strength of the composite. The result shows the CTE significantly increased with increasing temperature but decreased with increasing reinforcement. At higher temperatures, CTE of Al-beryl metal matrix composites with 5 wt%, 10 wt% and 15 wt% of beryllium aluminum cyclosilicate was 21 ppm/K, 18.2 ppm/K, and 16.8 ppm/K. The CTE values were found to be comparable with theoretical results. The turner model showed conformance with experimental results, was well suited to the experimental results.
基金Supported by the National Natural Science Foundation of China under Grant Nos 11574276,51503185 and 51302249the Doctoral Fund of the Ministry of Education of China under Grant No 20114101110003
文摘A novel material of ZrMnMo3012 with negative thermal expansion is presented. The phase transition temperature and coemcient of thermal expansion （CTE） are investigated by temperature-dependent x-ray diffraction and Raman spectra. It is shown that ZrMnMo3012 adopts monoclinic structure with space group P21/a （No. 14） from 298 to 358K and transforms to orthorhombic with space group Pnma （No. 62） above 363K. The linear CTE obtained from the results of XRD refinement is -2.80 × 10-6 K-1 from 363 to 873 K. The CTE of the bulk cylinder ceramic measured by a thermal dilatometer is -4.7× 10-6 K-1 from 373 to 773K approximatively.
基金financially supported by the Major Special Projects in Anhui Province,China(No.202003c08020005)the Key Projects in Hunan Province,China(No.2020GK2045)+1 种基金the Science and Technology Innovation Program of Hunan Province,China(No.2021RC4036)Postgraduate Scientific Research Innovation Project of Hunan Province,China(No.CX20211079)。
基金supported by the open Fund of State Key Laboratory of Disaster Reduction in Civil Engineering(Grant No.SLDRCE15-03)Beijing major science and technology projects(Grant No.Z191100008019002).
文摘The thermal expansion mismatch between cement mortar and aggregate at high temperature is one of the main reasons causing the deterioration of concrete at high temperature.In this study,the thermal damage of concrete caused by the thermal expansion mismatch between aggregate and cement mortar was investigated using a meso-scale concrete model.The meso-scale concrete model is composed of mortar,aggregate and the interfacial transition zone(ITZ).Laboratory tests on the mechanical properties of cement mortar at high temperature were conducted to provide the necessary mechanical parameter for the meso-scale concrete model.The simulation results show that the particle size,content,distribution and mechanical properties of the aggregate have an effect on the thermal damage of concrete at high temperature.The smaller the particle size of concrete aggregate and the higher the elastic modulus of aggregate,the greater the damage of concrete under high temperature.Due to the increasing thermal expansion difference between aggregate and cement mortar,and the deterioration of the cement mortar with the increasing temperature,the damage of concrete increased sharply after 500℃.