A self-made single-roll stirring (SRS) machine was used to manufacturesemisolid A2017 alloy, the mechanism of A2017 alloy formation was investigated. It was shown thatA2017 dendrites growing on the rough roll surface ...A self-made single-roll stirring (SRS) machine was used to manufacturesemisolid A2017 alloy, the mechanism of A2017 alloy formation was investigated. It was shown thatA2017 dendrites growing on the rough roll surface are crashed into fragments by the roll, which moveand grow freely then contribute the formation of finer spherical microstruc-ture. When casting at710-750℃, fine and homogeneous spherical or elliptical grains of A2017 alloy were obtained.Extending forming mould has been designed and was installed at the exit of roll-shoe gap. A2017alloy was formed by extending continuously at the semisolid state on SRS machine. Throughcontrolling pouring temperature, semisolid forming and extending extrusion was combined organically.A2017 product with fine surface and rectangular transection of 14 mm x 25 mm was obtained. Bycontrast to the national standard, the fracture strength and elongation of A2017 products producedfrom extending semisolid extrusion have been improved with an increase of 100 MPa and 29%,respectively.展开更多
基金This project is financially supported by State Key Fundamental Research of "973" Development Plan (No. G2000067208-4)
文摘A self-made single-roll stirring (SRS) machine was used to manufacturesemisolid A2017 alloy, the mechanism of A2017 alloy formation was investigated. It was shown thatA2017 dendrites growing on the rough roll surface are crashed into fragments by the roll, which moveand grow freely then contribute the formation of finer spherical microstruc-ture. When casting at710-750℃, fine and homogeneous spherical or elliptical grains of A2017 alloy were obtained.Extending forming mould has been designed and was installed at the exit of roll-shoe gap. A2017alloy was formed by extending continuously at the semisolid state on SRS machine. Throughcontrolling pouring temperature, semisolid forming and extending extrusion was combined organically.A2017 product with fine surface and rectangular transection of 14 mm x 25 mm was obtained. Bycontrast to the national standard, the fracture strength and elongation of A2017 products producedfrom extending semisolid extrusion have been improved with an increase of 100 MPa and 29%,respectively.