The effects of single-stage solution treatment(SST),enhanced solution treatment(EST),high-temperature pre-precipitation(HTPP)and multi-stage solution treatment(MST)on the microstructure,mechanical properties and corro...The effects of single-stage solution treatment(SST),enhanced solution treatment(EST),high-temperature pre-precipitation(HTPP)and multi-stage solution treatment(MST)on the microstructure,mechanical properties and corrosion resistance of the as-extruded 7055 aluminium alloy(AA7055)helical profile were investigated using differential scanning calorimetry(DSC),optical microscopy(OM),scanning electron microscopy(SEM),electron back-scattered diffraction(EBSD)and transmission electron microscopy(TEM).It was observed that EST and MST could promote the dissolution of the second-phase particles compared with the traditional SST,and the intergranular phases were distinctly discontinuously distributed after HTPP and MST.There was obvious difference in the main texture type and texture strength for the alloy after different solid solution treatments.HTPP could improve the corrosion resistance of the alloy by regulating the intergranular phases,but the mechanical properties were severely weakened.While the good corrosion resistance of the alloy could be obtained by MST without obvious strength loss.As a result,the MST is an ideal solid solution treatment scheme for AA7055.展开更多
TS-1/SiO_2 extrudate was post-treated with mixed solution of tetrapropyl ammonium hydroxide(TPAOH)and various ammonium salts solution(NH_4F,(NH_4)_3PO_4,(NH_4)_2CO_3,(NH_4)_2SO_4,NH_4CH_3CO_2,NH_4NO_3,NH_4Cl and(NH_4)...TS-1/SiO_2 extrudate was post-treated with mixed solution of tetrapropyl ammonium hydroxide(TPAOH)and various ammonium salts solution(NH_4F,(NH_4)_3PO_4,(NH_4)_2CO_3,(NH_4)_2SO_4,NH_4CH_3CO_2,NH_4NO_3,NH_4Cl and(NH_4)_2TiF_6).The obtained hierarchical TS-1 catalysts were characterized by many techniques and tested for propylene epoxidation using hydrogen peroxide as an oxidant in a fixed-bed reactor.It was shown that the physicochemical and catalytic properties of the treated TS-1/SiO_2 extrudate depended on the types of ammonium salts added.Compared to the treatment with TPAOH alone,the treatment with a mixed solution of TPAOH and some ammonium salts can greatly improve the catalytic properties of the treated TS-1/SiO_2 extrudate.Some of these ammonium salts were favorable for the incorporation of titanium in the framework,and the beneficial effect depended on the types of ammonium salt.TS-1/SiO_2 extrudate treated with a mixed solution of TPAOH and(NH_4)_3PO_4 exhibited the highest catalyst stability in propylene epoxidation.Such catalytic property can be correlated to high crystallinity,more framework titanium,large specific surface area and large external surface area.展开更多
基金the financial supports from the National Natural Science Foundation of China(No.51975330)Science Fund for Distinguished Young Scholars of Shandong Province,China(No.JQ201810)the Key Research and Development Program of Shandong Province,China(No.2019JZZY010360).
文摘The effects of single-stage solution treatment(SST),enhanced solution treatment(EST),high-temperature pre-precipitation(HTPP)and multi-stage solution treatment(MST)on the microstructure,mechanical properties and corrosion resistance of the as-extruded 7055 aluminium alloy(AA7055)helical profile were investigated using differential scanning calorimetry(DSC),optical microscopy(OM),scanning electron microscopy(SEM),electron back-scattered diffraction(EBSD)and transmission electron microscopy(TEM).It was observed that EST and MST could promote the dissolution of the second-phase particles compared with the traditional SST,and the intergranular phases were distinctly discontinuously distributed after HTPP and MST.There was obvious difference in the main texture type and texture strength for the alloy after different solid solution treatments.HTPP could improve the corrosion resistance of the alloy by regulating the intergranular phases,but the mechanical properties were severely weakened.While the good corrosion resistance of the alloy could be obtained by MST without obvious strength loss.As a result,the MST is an ideal solid solution treatment scheme for AA7055.
基金supported by National Natural Science Foundation of China (No. 21276183)
文摘TS-1/SiO_2 extrudate was post-treated with mixed solution of tetrapropyl ammonium hydroxide(TPAOH)and various ammonium salts solution(NH_4F,(NH_4)_3PO_4,(NH_4)_2CO_3,(NH_4)_2SO_4,NH_4CH_3CO_2,NH_4NO_3,NH_4Cl and(NH_4)_2TiF_6).The obtained hierarchical TS-1 catalysts were characterized by many techniques and tested for propylene epoxidation using hydrogen peroxide as an oxidant in a fixed-bed reactor.It was shown that the physicochemical and catalytic properties of the treated TS-1/SiO_2 extrudate depended on the types of ammonium salts added.Compared to the treatment with TPAOH alone,the treatment with a mixed solution of TPAOH and some ammonium salts can greatly improve the catalytic properties of the treated TS-1/SiO_2 extrudate.Some of these ammonium salts were favorable for the incorporation of titanium in the framework,and the beneficial effect depended on the types of ammonium salt.TS-1/SiO_2 extrudate treated with a mixed solution of TPAOH and(NH_4)_3PO_4 exhibited the highest catalyst stability in propylene epoxidation.Such catalytic property can be correlated to high crystallinity,more framework titanium,large specific surface area and large external surface area.