FePt granular films were prepared by direct current facing-target magnetron sputtering system onto glass substrates and subsequently in-situ annealed in vacuum. Vibrating sample magnetometer, X-ray diffraction and sca...FePt granular films were prepared by direct current facing-target magnetron sputtering system onto glass substrates and subsequently in-situ annealed in vacuum. Vibrating sample magnetometer, X-ray diffraction and scanning probe microscope were applied to study the magnetic properties, microstructures, morphologies and domain structures of the samples. （FePt）27Ti73 bilayer films were fabricated at various conditions to investigate the effect of Ti on FePt grains. The results show that without Ti matrix layer, FePt films deposited onto the glass substrates are fcc disordered; with addition of Ti matrix layer, FePt/Ti films form a ternary （FePt）27Ti73 alloy possessing fcc and L10 （111） mixed texture. FePt/（FePt）27Ti73 films with perfectly ordered L10（111） structure and unique magnetic properties can be obtained at Ti thickness of 35nm and substrate temperature of 250℃. The maximum coercivity is more than 240kA/m and the squareness ratio is more than 0.9. The obtained results suggest that the granular FePt/（FePt）27Ti73 films can be applicable to ultrahigh-density magnetic recording media.展开更多
TiCoTi granular films were prepared by DC facing-target magnetron sputtering system onto glass substrates and subsequently in situ annealing in vacuum. Structural of Ti (t nm)/Co (40 nm)/Ti (t nm) films were investiga...TiCoTi granular films were prepared by DC facing-target magnetron sputtering system onto glass substrates and subsequently in situ annealing in vacuum. Structural of Ti (t nm)/Co (40 nm)/Ti (t nm) films were investigated in detail, which shows that the majority Co nanograins are formed as the hexagonal-close-packed (HCP) structure. Vibrating sample magnetometer (VSM) and scanning probe microscope (SPM) were applied to study the magnetic properties, morphologies and domain structures of these samples. It has been found that the structure and magnetic properties of the Ti/Co/Ti films depend strongly on the Ti layer thickness. The out-of-plane coercivities (Hc) of the film is maximum about 78.8 kA·m-1 when t=5 nm with annealing at 300 ℃; the distributing of grains of the sample is uniformity; and the average size of particles is about 13 nm. The obtained results suggest that this system is perpendicular anisotropy and might be applicable to perpendicular magnetic recording media.展开更多
基金Project(10274018) supported by the National Natural Science Foundation of China project(Z200102) supported the KeyFoundation of Hebei Normal University project(2002116) supported the Foundation Education Department of of Hebei Provin
文摘FePt granular films were prepared by direct current facing-target magnetron sputtering system onto glass substrates and subsequently in-situ annealed in vacuum. Vibrating sample magnetometer, X-ray diffraction and scanning probe microscope were applied to study the magnetic properties, microstructures, morphologies and domain structures of the samples. （FePt）27Ti73 bilayer films were fabricated at various conditions to investigate the effect of Ti on FePt grains. The results show that without Ti matrix layer, FePt films deposited onto the glass substrates are fcc disordered; with addition of Ti matrix layer, FePt/Ti films form a ternary （FePt）27Ti73 alloy possessing fcc and L10 （111） mixed texture. FePt/（FePt）27Ti73 films with perfectly ordered L10（111） structure and unique magnetic properties can be obtained at Ti thickness of 35nm and substrate temperature of 250℃. The maximum coercivity is more than 240kA/m and the squareness ratio is more than 0.9. The obtained results suggest that the granular FePt/（FePt）27Ti73 films can be applicable to ultrahigh-density magnetic recording media.
基金This work was financially supported by the National Natural Science Foundation of China (No.10274018) and the Foundation of Hebei Provincial Education Department (No.2002116).
文摘TiCoTi granular films were prepared by DC facing-target magnetron sputtering system onto glass substrates and subsequently in situ annealing in vacuum. Structural of Ti (t nm)/Co (40 nm)/Ti (t nm) films were investigated in detail, which shows that the majority Co nanograins are formed as the hexagonal-close-packed (HCP) structure. Vibrating sample magnetometer (VSM) and scanning probe microscope (SPM) were applied to study the magnetic properties, morphologies and domain structures of these samples. It has been found that the structure and magnetic properties of the Ti/Co/Ti films depend strongly on the Ti layer thickness. The out-of-plane coercivities (Hc) of the film is maximum about 78.8 kA·m-1 when t=5 nm with annealing at 300 ℃; the distributing of grains of the sample is uniformity; and the average size of particles is about 13 nm. The obtained results suggest that this system is perpendicular anisotropy and might be applicable to perpendicular magnetic recording media.