Overwhelming low ammonia escape and low temperature denitration efficiency via MnOx-decorated two-dimensional MgAl layered double oxides

Low temperature catalysts are attracting increasing attention in the selective catalytic reduction(SCR)of NO with NH3.Mn Ox-decorated Mg Al layered double oxide(Mn/Mg Al-LDO)was synthesized via a facile fast pour assisted co-precipitation(FP-CP)process.Compared to the Mn/Mg Al-LDO obtained via slow drop assisted coprecipitation(SD-CP)method,the Mn/Mg Al-LDO(FP-CP)has excellent activity.The Mn/Mg Al-LDO(FP-CP)catalyst was shown to possess a high NO conversion rate of 76%-100%from 25 to 150℃,which is much better than the control Mn/Mg Al-LDO(SD-CP)(29.4%-75.8%).In addition,the Mn/Mg Al-LDO(FP-CP)offered an enhanced NO conversion rate of 97%and a N2selectivity of 97.3%at 100℃;the NO conversion rate was 100%and the N2selectivity was 90%at 150℃with a GHSV of 60,000 h^-1.The Mn/Mg Al-LDO(FP-CP)catalyst exhibited a smaller fragment nano-sheet structure(sheet thickness of 7.23 nm).An apparent lattice disorder was observed in the HRTEM image confirming the presence of many defects.The H2-TPR curves show that the Mn/Mg Al-LDO(FP-CP)catalyst has abundant reducing substances.Furthermore,the enhanced surface acidity makes the NH3concentration of the Mn/Mg Al-LDO(FP-CP)catalyst lower than 100 ml·m^-3after the reaction from 25 to 400℃.This can effectively reduce the ammonia escape rate in the SCR reaction.Thus,the Mn/Mg Al-LDO(FP-CP)catalyst has potential applications in stationary industrial installations for environmentally friendly ultra-low temperature SCR.