When a metal is subject to cyclic loading with cyclic stress values much lower than its tensile strength,fatigue occurs due to accumulative and irreversible damages developed in the microstructure,causing service fail...When a metal is subject to cyclic loading with cyclic stress values much lower than its tensile strength,fatigue occurs due to accumulative and irreversible damages developed in the microstructure,causing service failure of the metal workpiece or even fatal disaster in the worst cases.To develop materials with higher fatigue limit and longer fatigue life relies on reducing or suppressing展开更多
文摘When a metal is subject to cyclic loading with cyclic stress values much lower than its tensile strength,fatigue occurs due to accumulative and irreversible damages developed in the microstructure,causing service failure of the metal workpiece or even fatal disaster in the worst cases.To develop materials with higher fatigue limit and longer fatigue life relies on reducing or suppressing