Rapid alternating stress is formed in structure subjected to harsh thermal-acoustic loads,which will affect fatigue performance and reduce fatigue life seriously.First,fatigue experiment of superalloy thin-walled stru...Rapid alternating stress is formed in structure subjected to harsh thermal-acoustic loads,which will affect fatigue performance and reduce fatigue life seriously.First,fatigue experiment of superalloy thin-walled structure was carried out to obtain fatigue damage location and failure time of the experiment specimen,and S-iN curves of superalloy thin-walled structure at 723 K were fitted.Then,dynamic response simulation of superalloy thin-walled structure under the same load as experiment was implemented,and fatigue life was estimated based on the fatigue life prediction model which mainly included:improved rain-flow counting method,Morrow average stress model and Miner linear cumulative damage theory.Further,comparisons between simulation solutions and experimental results achieved a consistency,which verified the validity of the Fatigue Life Prediction Model(FLPM).Moreover,taking a rectangle plate as the analysis object,the distributions of Fain-low circulation blocks and damage levels of the structure were discussed respectively.Finally,current research indicates that in pre-buckling the structure is in softened area and fatigue life decreases with the increase of temperature;in post-buckling the structure is in hardened area and fatigue life increases with the increase of temperature within a certain range.展开更多
基金co-supported by Aviation Basic Science Fund Project of China(No.20151554002)Natural Sciences Key Project of Chengdu Aeronautic Polytechnic in China(No.061754)Natural Sciences General Project of Sichuan Province Education Department in China(No.18ZB0057).
文摘Rapid alternating stress is formed in structure subjected to harsh thermal-acoustic loads,which will affect fatigue performance and reduce fatigue life seriously.First,fatigue experiment of superalloy thin-walled structure was carried out to obtain fatigue damage location and failure time of the experiment specimen,and S-iN curves of superalloy thin-walled structure at 723 K were fitted.Then,dynamic response simulation of superalloy thin-walled structure under the same load as experiment was implemented,and fatigue life was estimated based on the fatigue life prediction model which mainly included:improved rain-flow counting method,Morrow average stress model and Miner linear cumulative damage theory.Further,comparisons between simulation solutions and experimental results achieved a consistency,which verified the validity of the Fatigue Life Prediction Model(FLPM).Moreover,taking a rectangle plate as the analysis object,the distributions of Fain-low circulation blocks and damage levels of the structure were discussed respectively.Finally,current research indicates that in pre-buckling the structure is in softened area and fatigue life decreases with the increase of temperature;in post-buckling the structure is in hardened area and fatigue life increases with the increase of temperature within a certain range.