Isolated Mn2O_(3) nanotubes and nanofibers were prepared very easily at a large scale with the liquid-phase catalysis method.The Mn2O_(3) nanotubes had dimensions of 30–50 nm(exterior diameter)and 0.2–1.0 mm(length)...Isolated Mn2O_(3) nanotubes and nanofibers were prepared very easily at a large scale with the liquid-phase catalysis method.The Mn2O_(3) nanotubes had dimensions of 30–50 nm(exterior diameter)and 0.2–1.0 mm(length),approximately.The Mn2O_(3) nanofibers had dimensions of 10–30 nm(diameter)and 0.4–2.0 mm(length),approxim-ately.Nano-Mn2O_(3) with different microstructures including nanotubes,nanofibers and nanoparticles could be selectively synthesized by controlling the contents and proportions of potassium permanganate and ferric nitrate.Ferric nitrate was an ideal catalyst for the preparation of Mn2O_(3) nanotube/fiber.When cobalt nitrate or nickel nitrate was used as catalyst,only amorphous nano-Mn2O_(3) was synthesized.X-ray diffraction(XRD)result shows that the Mn2O_(3) nanotube has a crystalline structure different from o-Mn2O_(3),t-Mn2O_(3),h-Mn2O_(3) and c-Mn2O_(3).展开更多
文摘Isolated Mn2O_(3) nanotubes and nanofibers were prepared very easily at a large scale with the liquid-phase catalysis method.The Mn2O_(3) nanotubes had dimensions of 30–50 nm(exterior diameter)and 0.2–1.0 mm(length),approximately.The Mn2O_(3) nanofibers had dimensions of 10–30 nm(diameter)and 0.4–2.0 mm(length),approxim-ately.Nano-Mn2O_(3) with different microstructures including nanotubes,nanofibers and nanoparticles could be selectively synthesized by controlling the contents and proportions of potassium permanganate and ferric nitrate.Ferric nitrate was an ideal catalyst for the preparation of Mn2O_(3) nanotube/fiber.When cobalt nitrate or nickel nitrate was used as catalyst,only amorphous nano-Mn2O_(3) was synthesized.X-ray diffraction(XRD)result shows that the Mn2O_(3) nanotube has a crystalline structure different from o-Mn2O_(3),t-Mn2O_(3),h-Mn2O_(3) and c-Mn2O_(3).