The deformation and micro-voids formation mechanisms in ferrite / bainite（ F / B） multi-phase steel with the volume fraction of bainite less than 50% were studied by numerical simulation and experimental observation...The deformation and micro-voids formation mechanisms in ferrite / bainite（ F / B） multi-phase steel with the volume fraction of bainite less than 50% were studied by numerical simulation and experimental observation. The results show that the micro-strain concentrates at the soft / hard phase（ F / B） interface in the multi-phase steel,which should be correlated with the mechanism of incoordinate deformation. During the necking of the steel,the micro-voids initially form around the F / B interface,which also form in ferrite and bainite with the severe strain. The micro-voids in bainite are more dense and finer than those in ferrite. The failure mechanism of bainite is the coalescence of micro-voids,and the failure mechanism of ferrite is the growth and tearing of micro-voids. Due to the different failure mechanisms of ferrite and bainite,a suitable part of soft phase would be beneficial to the capability of anti-failure of F / B multi-phase steel during the ductile fracture.展开更多
基金Item Sponsored by National Basic Research Program of China(2010CB630801)
文摘The deformation and micro-voids formation mechanisms in ferrite / bainite（ F / B） multi-phase steel with the volume fraction of bainite less than 50% were studied by numerical simulation and experimental observation. The results show that the micro-strain concentrates at the soft / hard phase（ F / B） interface in the multi-phase steel,which should be correlated with the mechanism of incoordinate deformation. During the necking of the steel,the micro-voids initially form around the F / B interface,which also form in ferrite and bainite with the severe strain. The micro-voids in bainite are more dense and finer than those in ferrite. The failure mechanism of bainite is the coalescence of micro-voids,and the failure mechanism of ferrite is the growth and tearing of micro-voids. Due to the different failure mechanisms of ferrite and bainite,a suitable part of soft phase would be beneficial to the capability of anti-failure of F / B multi-phase steel during the ductile fracture.