The method of producing ferronickel at low temperature(1250–1400℃)has been applied since the 1950s at Nippon Yakin Kogyo,Oheyama Works,Japan.Limestone was used as an additive to adjust the slag composition for lower...The method of producing ferronickel at low temperature(1250–1400℃)has been applied since the 1950s at Nippon Yakin Kogyo,Oheyama Works,Japan.Limestone was used as an additive to adjust the slag composition for lowering the slag melting point.The ferronickel product was recovered by means of a magnetic separator from semi-molten slag and metal after water quenching.To increase the efficiency of magnetic separation,a large particle size of ferronickel is desired.Therefore,in this study,the influences of CaO,CaF_(2),and H_(3)BO_(3) additives on the evolution of ferronickel particle at≤1250℃were investigated.The experiments were conducted at 900–1250℃with the addition of CaO,CaF_(2),and H_(3)BO_(3).The reduction processes were carried out in a horizontal tube furnace for 2 h under argon atmosphere.At 1250℃,with the CaO addition of 10 wt%of the ore weight,ferronickel particles with size of 20μm were obtained.The ferronickel particle size increased to 165μm by adding 10 wt%CaO and 10 wt%CaF_(2).The addition of boric acid further increased the ferronickel particle size to 376μm,as shown by the experiments with the addition of 10 wt%CaO,10 wt%CaF_(2),and 10 wt%H_(3)BO_(3).展开更多
基金the Program of Research,Community Service,and Innovation of the Institut Teknologi Bandung(P3MI–ITB)for funding this research。
文摘The method of producing ferronickel at low temperature(1250–1400℃)has been applied since the 1950s at Nippon Yakin Kogyo,Oheyama Works,Japan.Limestone was used as an additive to adjust the slag composition for lowering the slag melting point.The ferronickel product was recovered by means of a magnetic separator from semi-molten slag and metal after water quenching.To increase the efficiency of magnetic separation,a large particle size of ferronickel is desired.Therefore,in this study,the influences of CaO,CaF_(2),and H_(3)BO_(3) additives on the evolution of ferronickel particle at≤1250℃were investigated.The experiments were conducted at 900–1250℃with the addition of CaO,CaF_(2),and H_(3)BO_(3).The reduction processes were carried out in a horizontal tube furnace for 2 h under argon atmosphere.At 1250℃,with the CaO addition of 10 wt%of the ore weight,ferronickel particles with size of 20μm were obtained.The ferronickel particle size increased to 165μm by adding 10 wt%CaO and 10 wt%CaF_(2).The addition of boric acid further increased the ferronickel particle size to 376μm,as shown by the experiments with the addition of 10 wt%CaO,10 wt%CaF_(2),and 10 wt%H_(3)BO_(3).