Reinforced concrete （RC） columns lacking adequately detailed transverse reinforcement do not possess the necessary ductility to dissipate seismic energy during a major earthquake without severe strength degradation....Reinforced concrete （RC） columns lacking adequately detailed transverse reinforcement do not possess the necessary ductility to dissipate seismic energy during a major earthquake without severe strength degradation. In this paper, a new retrofit method, which utilized fiber-reinforced plastics （FRP） confinement mechanism and anchorage of embedded bars, was developed aiming to retrofit non-ductile large RC rectangular columns to prevent the damage of the plastic hinges. Carbon FRP （CFRP） sheets and glass FRP （GFRP） bars were used in this test, and five scaled RC columns were tested to examine the function of this new method for improving the ductility of columns. Responses of columns were examined before and after being retrofitted. Test results indicate that this new composite method can be very effective to improve the anti-seismic behavior of non-ductile RC columns compared with normal CFRP sheets retrofitted column.展开更多
The potential usage of virgin Low density polyethelyne (LDPE) reinforced with different concentrations (2%, 5% and 6% by weight) of treated rice straw with different lengths (2 mm, 4 mm and 6 mm) is investigated to pr...The potential usage of virgin Low density polyethelyne (LDPE) reinforced with different concentrations (2%, 5% and 6% by weight) of treated rice straw with different lengths (2 mm, 4 mm and 6 mm) is investigated to produce high value products that have technical and environmental demand. The two treatment methods used for rice straw are alkali and acidic treatments of rice straw. The removal of impurities and waxy substances from fiber surface avoid creation of rougher topography after treatment and improves the quality of fiber, also content of hemi cellulose and lignin decrease so increase effectiveness of fiber due to dispersing of fiber in matrix. The reinforcing material is embedded in the matrix material to enhance tensile and flexural behaviors of the synthesized composite. The result of investigating these two mechanical properties, using statistical analysis & design of experiments, showed an enhancement in the mechaniccal properties of the virgin polymer composite compared to the virgin polymer. The flexural stress of the composite increased three times the virgin flexural stress, while the tensile stress increased eight times the original tensile stress.展开更多
The interfacial debonding in fiber-reinforced plastic(FRP)strengthened repair material will affect the bonding strength and lead to failure of the repair without warning.Unfortunately the interfacial damage is normall...The interfacial debonding in fiber-reinforced plastic(FRP)strengthened repair material will affect the bonding strength and lead to failure of the repair without warning.Unfortunately the interfacial damage is normally invisible and often in the form of a patch rather than a through-width crack.Therefore,a debonding patch detection technique based on fiber optic interferometry is proposed.A quasi-impulse loading is applied with a rubberhead hammer and the total elongation of a surface-mounted optical fiber along the length of the repair material is measured as a function of load position.When a debonding patch is present,the induced sudden slope or sign change on the plot of fiber integral strain v.s.load position will reveal the extent and the location of the debonded area.The results of the study indicate that the proposed technique is applicable for debonding patch detection in repaired members under various support conditions.展开更多
基金Project supported by the Science Foundation of Shanghai Municipal Commission of Science and Technology （Grant No.07QA14025）.Acknowledgment The authors thank Dr. WU Yu-fei, the assistant professor of the City University of Hong Kong for providing good suggestion and help during the test. This research was also supported by the grant from the Research Grant Council of the Hong Kong Special Administrative Region （Grant No.Cityu1113/04E）.
文摘Reinforced concrete （RC） columns lacking adequately detailed transverse reinforcement do not possess the necessary ductility to dissipate seismic energy during a major earthquake without severe strength degradation. In this paper, a new retrofit method, which utilized fiber-reinforced plastics （FRP） confinement mechanism and anchorage of embedded bars, was developed aiming to retrofit non-ductile large RC rectangular columns to prevent the damage of the plastic hinges. Carbon FRP （CFRP） sheets and glass FRP （GFRP） bars were used in this test, and five scaled RC columns were tested to examine the function of this new method for improving the ductility of columns. Responses of columns were examined before and after being retrofitted. Test results indicate that this new composite method can be very effective to improve the anti-seismic behavior of non-ductile RC columns compared with normal CFRP sheets retrofitted column.
文摘The potential usage of virgin Low density polyethelyne (LDPE) reinforced with different concentrations (2%, 5% and 6% by weight) of treated rice straw with different lengths (2 mm, 4 mm and 6 mm) is investigated to produce high value products that have technical and environmental demand. The two treatment methods used for rice straw are alkali and acidic treatments of rice straw. The removal of impurities and waxy substances from fiber surface avoid creation of rougher topography after treatment and improves the quality of fiber, also content of hemi cellulose and lignin decrease so increase effectiveness of fiber due to dispersing of fiber in matrix. The reinforcing material is embedded in the matrix material to enhance tensile and flexural behaviors of the synthesized composite. The result of investigating these two mechanical properties, using statistical analysis & design of experiments, showed an enhancement in the mechaniccal properties of the virgin polymer composite compared to the virgin polymer. The flexural stress of the composite increased three times the virgin flexural stress, while the tensile stress increased eight times the original tensile stress.
基金supported by the National Natural Science Foundation of China(No.51278156)the Basic Project of Shenzhen Science & Technology Program(No.JCYJ2017030155815876)
文摘The interfacial debonding in fiber-reinforced plastic(FRP)strengthened repair material will affect the bonding strength and lead to failure of the repair without warning.Unfortunately the interfacial damage is normally invisible and often in the form of a patch rather than a through-width crack.Therefore,a debonding patch detection technique based on fiber optic interferometry is proposed.A quasi-impulse loading is applied with a rubberhead hammer and the total elongation of a surface-mounted optical fiber along the length of the repair material is measured as a function of load position.When a debonding patch is present,the induced sudden slope or sign change on the plot of fiber integral strain v.s.load position will reveal the extent and the location of the debonded area.The results of the study indicate that the proposed technique is applicable for debonding patch detection in repaired members under various support conditions.