Al/Mg bimetal was prepared by lost foam solid-liquid compound casting,and the effects of mechanical vibration on the filling and solidification behavior,microstructure and performance of the bimetal were investigated....Al/Mg bimetal was prepared by lost foam solid-liquid compound casting,and the effects of mechanical vibration on the filling and solidification behavior,microstructure and performance of the bimetal were investigated.Results show that the mechanical vibration has a remarkable influence on the filling and solidification processes.It is found that after mechanical vibration,the filling rate increases and the filling rate at different times is more uniform than that without vibration.In addition,the mechanical vibration also increases the wettability between liquid AZ91D and A356 inlays.The mechanical vibration reduces the horizontal and vertical temperature gradient of the casting and makes the temperature distribution of the whole casting more uniform.Compared to the Al/Mg bimetal without vibration,the shear strength is improved by 39.76%after the mechanical vibration is applied,due to the decrease of the inclusions and Al_(12)Mg_(17) dendrites,and the refinement and uniform distribution of the Mg_(2)Si particles in the interface of the Al/Mg bimetal.展开更多
Investment and suction casting （ISC） represents an economic and promising process route to fabricate auto-motive exhaust valves of γ-TiAI based alloys, but information available on the metal flow and the temperatur...Investment and suction casting （ISC） represents an economic and promising process route to fabricate auto-motive exhaust valves of γ-TiAI based alloys, but information available on the metal flow and the temperature changeseduring mould filling and solidification process for the ISC process is meager. A sequentially coupled mathematical flow-thermal model, based on the commercial finite-volume/finite-difference code FLOW-3D and the finite-element code PROCAST, has been developed to investigate the ISC process. In term of calcu-lating the flow and temperature fields during the filling and solidification stages, potential defects including the gas bubbles and the surface air entrainment occurred in the mould filling process and the shrinkage porosities formed in the solidification process are predicted and the reasons for the formation of these defects are also analyzed. The effects of filling pressure difference control methods and moulds on gas bubble and surface air entrainment behavior are presented. It is found that by changing the filling pressure difference control methods from general suction casting to ＂air leakage＂ suction casting and reducing air leakage flow rates, the gas bubbles are eliminated effectively, and the surface air entrainment attenuate dramatically. With resort to a mould with a tetragonal runner, the surface air entrainment decrease to the lowest level. Finally, the water analogue and suction casting experiments of exhaust valves are implemented for further validation of the simulation results.展开更多
基金This work was funded by the National Natural Science Foundation of China(Nos.52075198,52271102 and 52205359)the China Postdoctoral Science Foundation(No.2021M691112).
文摘Al/Mg bimetal was prepared by lost foam solid-liquid compound casting,and the effects of mechanical vibration on the filling and solidification behavior,microstructure and performance of the bimetal were investigated.Results show that the mechanical vibration has a remarkable influence on the filling and solidification processes.It is found that after mechanical vibration,the filling rate increases and the filling rate at different times is more uniform than that without vibration.In addition,the mechanical vibration also increases the wettability between liquid AZ91D and A356 inlays.The mechanical vibration reduces the horizontal and vertical temperature gradient of the casting and makes the temperature distribution of the whole casting more uniform.Compared to the Al/Mg bimetal without vibration,the shear strength is improved by 39.76%after the mechanical vibration is applied,due to the decrease of the inclusions and Al_(12)Mg_(17) dendrites,and the refinement and uniform distribution of the Mg_(2)Si particles in the interface of the Al/Mg bimetal.
文摘Investment and suction casting （ISC） represents an economic and promising process route to fabricate auto-motive exhaust valves of γ-TiAI based alloys, but information available on the metal flow and the temperature changeseduring mould filling and solidification process for the ISC process is meager. A sequentially coupled mathematical flow-thermal model, based on the commercial finite-volume/finite-difference code FLOW-3D and the finite-element code PROCAST, has been developed to investigate the ISC process. In term of calcu-lating the flow and temperature fields during the filling and solidification stages, potential defects including the gas bubbles and the surface air entrainment occurred in the mould filling process and the shrinkage porosities formed in the solidification process are predicted and the reasons for the formation of these defects are also analyzed. The effects of filling pressure difference control methods and moulds on gas bubble and surface air entrainment behavior are presented. It is found that by changing the filling pressure difference control methods from general suction casting to ＂air leakage＂ suction casting and reducing air leakage flow rates, the gas bubbles are eliminated effectively, and the surface air entrainment attenuate dramatically. With resort to a mould with a tetragonal runner, the surface air entrainment decrease to the lowest level. Finally, the water analogue and suction casting experiments of exhaust valves are implemented for further validation of the simulation results.