For obtaining pure phase T12Ba2Ca2Cu3O10 （T1-2223） films with good superconducting properties, the growth technique is improved by dc magnetron sputtering and a triple post-annealing process. The triple post-anneali...For obtaining pure phase T12Ba2Ca2Cu3O10 （T1-2223） films with good superconducting properties, the growth technique is improved by dc magnetron sputtering and a triple post-annealing process. The triple post-annealing process comprises annealing twice in argon and once in oxygen at different temperatures. In the first low-temperature annealing phase in argon, T12Ba2CaCu2O8 （T1-2212） is obtained to effectively minimize evaporation in the next step. With the increase of temperature in the second annealing stage in argon, the previously prepared T1-2212 inter-phase is converted into T1-2223 phase. An additional annealing in oxygen is also adopted to improve the properties of T1-2223 films, each containing an optimal oxygen content value. The results of X-ray diffraction （XRD） θ-2θ scans, 09 scans and rotational φ scans show that each of the T1-2223 films has a high phase purity and an epitaxial structure. Smooth films are observed by scanning electron microscopy （SEM）. The critical temperatures Tc of the films are measured to be about 120 K and the critical current densities Jc can reach 4.0 MA/cm2 at 77 K at self field.展开更多
The influence of nitrogen concentration in mixed gas on temperature conditions, structure and phase composition of the TiN film deposited by arc spraying has been investigated. By electron microscopic investigations a...The influence of nitrogen concentration in mixed gas on temperature conditions, structure and phase composition of the TiN film deposited by arc spraying has been investigated. By electron microscopic investigations and X-ray diffraction phase analysis was recognized forming stages and structuring process of the film with main cubic phase (111) TiN. It was discovered that forming stages and process of structuring of ion-plasma TiN films are affected by both film temperature and its rate of heating.展开更多
Y_(1-x)Ho_xBa_2Cu_3O_(7-δ)(0<x<1) sinsle crystal thin films oriented with the caxis perpendicular to the sur-face were grown by DC magnetron sputtering technique. Target was pieced together with half of YBa_2Cu...Y_(1-x)Ho_xBa_2Cu_3O_(7-δ)(0<x<1) sinsle crystal thin films oriented with the caxis perpendicular to the sur-face were grown by DC magnetron sputtering technique. Target was pieced together with half of YBa_2Cu_3O_(7-δ)(YBCO) and half of HoBa_2Cu_3O_(7-δ)(HBCO) superconducting materials. As the distance between HBCO targetmaterial and substrate is varied , the Ho content in material is changed respectively. When the content of Ho is0. 7 (atom ratio) , the T_c>83K.展开更多
基金supported by the National Natural Science Foundation of China(Grant Nos.51002081 and 61176119)
文摘For obtaining pure phase T12Ba2Ca2Cu3O10 （T1-2223） films with good superconducting properties, the growth technique is improved by dc magnetron sputtering and a triple post-annealing process. The triple post-annealing process comprises annealing twice in argon and once in oxygen at different temperatures. In the first low-temperature annealing phase in argon, T12Ba2CaCu2O8 （T1-2212） is obtained to effectively minimize evaporation in the next step. With the increase of temperature in the second annealing stage in argon, the previously prepared T1-2212 inter-phase is converted into T1-2223 phase. An additional annealing in oxygen is also adopted to improve the properties of T1-2223 films, each containing an optimal oxygen content value. The results of X-ray diffraction （XRD） θ-2θ scans, 09 scans and rotational φ scans show that each of the T1-2223 films has a high phase purity and an epitaxial structure. Smooth films are observed by scanning electron microscopy （SEM）. The critical temperatures Tc of the films are measured to be about 120 K and the critical current densities Jc can reach 4.0 MA/cm2 at 77 K at self field.
文摘The influence of nitrogen concentration in mixed gas on temperature conditions, structure and phase composition of the TiN film deposited by arc spraying has been investigated. By electron microscopic investigations and X-ray diffraction phase analysis was recognized forming stages and structuring process of the film with main cubic phase (111) TiN. It was discovered that forming stages and process of structuring of ion-plasma TiN films are affected by both film temperature and its rate of heating.
文摘Y_(1-x)Ho_xBa_2Cu_3O_(7-δ)(0<x<1) sinsle crystal thin films oriented with the caxis perpendicular to the sur-face were grown by DC magnetron sputtering technique. Target was pieced together with half of YBa_2Cu_3O_(7-δ)(YBCO) and half of HoBa_2Cu_3O_(7-δ)(HBCO) superconducting materials. As the distance between HBCO targetmaterial and substrate is varied , the Ho content in material is changed respectively. When the content of Ho is0. 7 (atom ratio) , the T_c>83K.