Annealing process will have greatly influence on microstructure of V,Ti and N microalloyed low carbon steel sheets.In this paper,the experimental steels with given amount of V,Ti and N elements were annealed at 4 rout...Annealing process will have greatly influence on microstructure of V,Ti and N microalloyed low carbon steel sheets.In this paper,the experimental steels with given amount of V,Ti and N elements were annealed at 4 routes to simulate batch annealing and continuous annealing processes,respectively.The enameling tests for the annealed steel sheets were undergone in same enameling and firing processes to study the relationship between microstructure and fishscale.The result shows that the cold-rolled steel sheets annealed at 750 ℃for 6 minutes even for 30 minutes exhibit excellent fishscale resistance.展开更多
The precipitates and hydrogen permeation behavior in three kinds of hot rolled low carbon heavy plate steels for enameling were analyzed; then, both sides of the steels were enameled. The experimental results show tha...The precipitates and hydrogen permeation behavior in three kinds of hot rolled low carbon heavy plate steels for enameling were analyzed; then, both sides of the steels were enameled. The experimental results show that a large amount of coarse Ti4 Cz $2 and fine Ti（C, N） particles exist in the optimized Ti-bearing steel, quite a lot of fine Ti（C,N） particles exist in the optimized carbon steel, but only a little bit fine Ti（C,N） particles exist in the carbon steel. The fishscaling resistance of the steels can be correlated to the effective hydrogen diffusion coefficient, and a model of correlation between the effective hydrogen diffusion coefficient and the volume fraction of the precipitates was established and verified. The effective hydrogen diffusion coefficient should be lower than 3.96×10-6 cm2/s to avoid fishscaling in heavy plate steels.展开更多
文摘Annealing process will have greatly influence on microstructure of V,Ti and N microalloyed low carbon steel sheets.In this paper,the experimental steels with given amount of V,Ti and N elements were annealed at 4 routes to simulate batch annealing and continuous annealing processes,respectively.The enameling tests for the annealed steel sheets were undergone in same enameling and firing processes to study the relationship between microstructure and fishscale.The result shows that the cold-rolled steel sheets annealed at 750 ℃for 6 minutes even for 30 minutes exhibit excellent fishscale resistance.
文摘The precipitates and hydrogen permeation behavior in three kinds of hot rolled low carbon heavy plate steels for enameling were analyzed; then, both sides of the steels were enameled. The experimental results show that a large amount of coarse Ti4 Cz $2 and fine Ti（C, N） particles exist in the optimized Ti-bearing steel, quite a lot of fine Ti（C,N） particles exist in the optimized carbon steel, but only a little bit fine Ti（C,N） particles exist in the carbon steel. The fishscaling resistance of the steels can be correlated to the effective hydrogen diffusion coefficient, and a model of correlation between the effective hydrogen diffusion coefficient and the volume fraction of the precipitates was established and verified. The effective hydrogen diffusion coefficient should be lower than 3.96×10-6 cm2/s to avoid fishscaling in heavy plate steels.