Flame spray synthesis (FSS), a combination of the flame spray technology and Self-propagation High-temperature Synthesis (SHS) was developed for preparing fine-ceramic-containing composite coatings. It can simplify th...Flame spray synthesis (FSS), a combination of the flame spray technology and Self-propagation High-temperature Synthesis (SHS) was developed for preparing fine-ceramic-containing composite coatings. It can simplify the preparations of powder to synthesize and deposit the desired materials in one step. The preliminary results obtained from TiC-Fe cermet coatings by FSS process are reported. The peculiar microstructure of the composite coatings, which contains very fine (<1m) and round TiC and alternate TiC-rich (Hv=11€*13GPa) and TiC-poor layers (Hv=3.0 -6.0GPa), is expected to play an important role in their tribological properties.展开更多
Wide-angle light scattering(WALS)was used for in situ measurements of droplet and nanoparticle size distributions during the synthesis of titania and iron oxide particles from liquid precursor solutions in the standar...Wide-angle light scattering(WALS)was used for in situ measurements of droplet and nanoparticle size distributions during the synthesis of titania and iron oxide particles from liquid precursor solutions in the standardized SpraySyn burner for spray flame synthesis.Titania was synthesized from titanium tetraisopropoxide(TTIP)and iron oxide from iron(II)nitrate nonahydrate(INN)using ethanol(EtOH)as solvent.Scattering images were taken at heights up to 120 mm above the burner surface and classified into droplet and particle scattering.Droplet size distributions were derived from a sequential analysis of scattering data containing the oscillating Mie pattern,the lognormal size distribution parameters for spherical and fractal particle fractions from a multivariate approach on averaged particle scattering data.The results show that the precursor addition leads to altered evaporation behavior and even droplet disruption probably induced by puffing or micro-explosions compared to pure EtOH.In the case of TTIP(a hygroscopic alkoxide),the synthesis of a large fraction of spheres was observed,while the nitrate INN leads to the formation of mostly fractal aggregates.展开更多
文摘Flame spray synthesis (FSS), a combination of the flame spray technology and Self-propagation High-temperature Synthesis (SHS) was developed for preparing fine-ceramic-containing composite coatings. It can simplify the preparations of powder to synthesize and deposit the desired materials in one step. The preliminary results obtained from TiC-Fe cermet coatings by FSS process are reported. The peculiar microstructure of the composite coatings, which contains very fine (<1m) and round TiC and alternate TiC-rich (Hv=11€*13GPa) and TiC-poor layers (Hv=3.0 -6.0GPa), is expected to play an important role in their tribological properties.
基金funded by the German Research Foundation DFG under grants WI1602/16-1 and WI1602/16-2.
文摘Wide-angle light scattering(WALS)was used for in situ measurements of droplet and nanoparticle size distributions during the synthesis of titania and iron oxide particles from liquid precursor solutions in the standardized SpraySyn burner for spray flame synthesis.Titania was synthesized from titanium tetraisopropoxide(TTIP)and iron oxide from iron(II)nitrate nonahydrate(INN)using ethanol(EtOH)as solvent.Scattering images were taken at heights up to 120 mm above the burner surface and classified into droplet and particle scattering.Droplet size distributions were derived from a sequential analysis of scattering data containing the oscillating Mie pattern,the lognormal size distribution parameters for spherical and fractal particle fractions from a multivariate approach on averaged particle scattering data.The results show that the precursor addition leads to altered evaporation behavior and even droplet disruption probably induced by puffing or micro-explosions compared to pure EtOH.In the case of TTIP(a hygroscopic alkoxide),the synthesis of a large fraction of spheres was observed,while the nitrate INN leads to the formation of mostly fractal aggregates.