Although polyimide fibers are excellent intrinsic flame-retardant fibers, their price is so high that they are rarely used in clothing. To expand their application, the polyimide fibers were blended with flame-retarda...Although polyimide fibers are excellent intrinsic flame-retardant fibers, their price is so high that they are rarely used in clothing. To expand their application, the polyimide fibers were blended with flame-retardant viscose fibers at a ratio of 30∶70, and the blended yarns were woven with flame-retardant polyester filaments. Fabrics with different parameters, including fabric weaves, warp yarn densities, and fabric layers, were designed, and the effects of those fabric parameters on mechanical properties and flame-retardant properties were tested and analyzed. The results show that the tearing load of the fabrics is affected by fabric weaves, warp yarn densities, and fabric layers, and the tearing load of the weft mountain weave fabric and the twill weave fabric is higher than that of the plain weave fabric. The bursting load of the fabric increases with the increase of warp yarn densities and layers. Among the tested fabric samples, the triple-layer twill fabric has the best flame-retardant performance, which meets the standard of flame-retardant protective fabric Grade B1 level. The research of this paper would provide guidance for the development and production of polyimide blended fabrics.展开更多
The main purpose of this research work is to improve anti-static properties of Cashmere fabric by introducing application comprising anti-static agent by foaming which was made with cationic waterborne polyurethane an...The main purpose of this research work is to improve anti-static properties of Cashmere fabric by introducing application comprising anti-static agent by foaming which was made with cationic waterborne polyurethane and graphene-CNC. Cashmere fabric was cut into 10 pieces of sample cloth of 5 cm * 5 cm size, washed with acetone solution, and then dried in an oven at 60℃. Three forms of waterborne polyurethanes such as two forms of Cationic waterborne polyurethane (CWPU) and a form of Anionic waterborne polyurethane (AWPU) were synthesized. Cellulose nanocrystalline (CNC)/graphite powder solution with the ratio of 0.5/1, 1/1, 2/1 was prepared by ultrasonic probe stripping method, and the concentration of graphite powder was ensured to be 1 mg/ml. The fabric was treated with anionic and cationic WPUs foaming solution until the weight gain reached 2.5 - 3.5 wt%. After drying, the elastic cloth was foamed with graphene solution until the graphite content of the cloth was close to 10%, 20%, 40%, 60% respectively, and then dried for reserving. Characterization properties of pure graphite powder, pure CNC and graphene solution with different proportions of three components were tested by Fourier transform infrared spectrometer (FTIR), X-ray diffraction (XRD), Thermalgravitimetric analysis (TGA) and scanning electron microscopy (SEM). Take the original cloth, only WPU treated cloth and four clothes with different graphite content for the fabric performance test.展开更多
基金National Natural Science Foundation of China (No.11802161)Natural Science Foundation of Fujian Province,China (No.2020J05160)Startup Foundation for Doctors of Quanzhou Normal University,China (No.H18012)。
文摘Although polyimide fibers are excellent intrinsic flame-retardant fibers, their price is so high that they are rarely used in clothing. To expand their application, the polyimide fibers were blended with flame-retardant viscose fibers at a ratio of 30∶70, and the blended yarns were woven with flame-retardant polyester filaments. Fabrics with different parameters, including fabric weaves, warp yarn densities, and fabric layers, were designed, and the effects of those fabric parameters on mechanical properties and flame-retardant properties were tested and analyzed. The results show that the tearing load of the fabrics is affected by fabric weaves, warp yarn densities, and fabric layers, and the tearing load of the weft mountain weave fabric and the twill weave fabric is higher than that of the plain weave fabric. The bursting load of the fabric increases with the increase of warp yarn densities and layers. Among the tested fabric samples, the triple-layer twill fabric has the best flame-retardant performance, which meets the standard of flame-retardant protective fabric Grade B1 level. The research of this paper would provide guidance for the development and production of polyimide blended fabrics.
文摘The main purpose of this research work is to improve anti-static properties of Cashmere fabric by introducing application comprising anti-static agent by foaming which was made with cationic waterborne polyurethane and graphene-CNC. Cashmere fabric was cut into 10 pieces of sample cloth of 5 cm * 5 cm size, washed with acetone solution, and then dried in an oven at 60℃. Three forms of waterborne polyurethanes such as two forms of Cationic waterborne polyurethane (CWPU) and a form of Anionic waterborne polyurethane (AWPU) were synthesized. Cellulose nanocrystalline (CNC)/graphite powder solution with the ratio of 0.5/1, 1/1, 2/1 was prepared by ultrasonic probe stripping method, and the concentration of graphite powder was ensured to be 1 mg/ml. The fabric was treated with anionic and cationic WPUs foaming solution until the weight gain reached 2.5 - 3.5 wt%. After drying, the elastic cloth was foamed with graphene solution until the graphite content of the cloth was close to 10%, 20%, 40%, 60% respectively, and then dried for reserving. Characterization properties of pure graphite powder, pure CNC and graphene solution with different proportions of three components were tested by Fourier transform infrared spectrometer (FTIR), X-ray diffraction (XRD), Thermalgravitimetric analysis (TGA) and scanning electron microscopy (SEM). Take the original cloth, only WPU treated cloth and four clothes with different graphite content for the fabric performance test.