The deposition of active materials directly onto metal wires is a general strategy to prepare wire-shaped electrodes for flexible and wearable energy storage devices. However, it is still a critical challenge to coat ...The deposition of active materials directly onto metal wires is a general strategy to prepare wire-shaped electrodes for flexible and wearable energy storage devices. However, it is still a critical challenge to coat active materials onto the aimed metal wires because of their smooth surface and small specific surface area. In this work, high porous nickel yarns（PNYs） was fabricated using commercial nylon yarns as templates through step-wise electroless plating, electroplating and calcination processes. The PNYs are composed of multiplied fibers with hollow tubular structure of 5–10 μm in diameter, allowing the imbibition of carbon nanotubes（CNTs） solution by a facile capillary action process. The prepared CNTs/PNY electrodes showed a typical electrochemical double layer capacitive performance and the constructed allsolid flexible wire-shaped symmetric supercapacitors provided a specific capacitance of 4.67 F/cm3 with good cycling stability at a current density of 0.6 A/cm3.展开更多
基金supported by Priority Academic Program Development of Jiangsu Higher Education Institutions (YX03001)Jiangsu National Synergetic Innovation Center for Advanced Materials (SICAM)+3 种基金Synergistic Innovation Center for Organic Electronics and Information Displays, Jiangsu Provincial NSF (BK20160890, BK20141424, BK20150863)Jiangsu Province "Six Talent Peak" (2014-XCL-014)Qing Lan Project of Jiangsu ProvinceScientific Research Foundation of NUPT (NY214183, NY215014, NY215152)
文摘The deposition of active materials directly onto metal wires is a general strategy to prepare wire-shaped electrodes for flexible and wearable energy storage devices. However, it is still a critical challenge to coat active materials onto the aimed metal wires because of their smooth surface and small specific surface area. In this work, high porous nickel yarns（PNYs） was fabricated using commercial nylon yarns as templates through step-wise electroless plating, electroplating and calcination processes. The PNYs are composed of multiplied fibers with hollow tubular structure of 5–10 μm in diameter, allowing the imbibition of carbon nanotubes（CNTs） solution by a facile capillary action process. The prepared CNTs/PNY electrodes showed a typical electrochemical double layer capacitive performance and the constructed allsolid flexible wire-shaped symmetric supercapacitors provided a specific capacitance of 4.67 F/cm3 with good cycling stability at a current density of 0.6 A/cm3.