Periclase-spinel bricks were prepared using sintered magnesia,flotation magnesia,fused magnesium aluminate spinel and calcined Al_(2)O_(3)fines as the starting materials and calcium lignosulfonate as the binder,mixing...Periclase-spinel bricks were prepared using sintered magnesia,flotation magnesia,fused magnesium aluminate spinel and calcined Al_(2)O_(3)fines as the starting materials and calcium lignosulfonate as the binder,mixing,shaping and firing at 1650℃.Flotation magnesia particles were used to replace ordinary sintered magnesia particles and different amounts of calcined Al_(2)O_(3)fines were extra-added(0%,3%and 5%,by mass)to investigate their effects on the properties of periclase-spinel bricks.The results show that:the periclase-spinel bricks prepared with flotation magnesia particles have reduced apparent porosity and cold compressive strength,and enhanced bulk density,thermal shock resistance,hot strength and hot toughness.As the calcined Al_(2)O_(3)fines addition increases,the apparent porosity and the cold compressive strength decrease,and the bulk density,the thermal shock resistance,the hot strength and the hot toughness are improved.展开更多
文摘Periclase-spinel bricks were prepared using sintered magnesia,flotation magnesia,fused magnesium aluminate spinel and calcined Al_(2)O_(3)fines as the starting materials and calcium lignosulfonate as the binder,mixing,shaping and firing at 1650℃.Flotation magnesia particles were used to replace ordinary sintered magnesia particles and different amounts of calcined Al_(2)O_(3)fines were extra-added(0%,3%and 5%,by mass)to investigate their effects on the properties of periclase-spinel bricks.The results show that:the periclase-spinel bricks prepared with flotation magnesia particles have reduced apparent porosity and cold compressive strength,and enhanced bulk density,thermal shock resistance,hot strength and hot toughness.As the calcined Al_(2)O_(3)fines addition increases,the apparent porosity and the cold compressive strength decrease,and the bulk density,the thermal shock resistance,the hot strength and the hot toughness are improved.