Fluidized bed coating efficiency and morphology of coatings for producing Al-based nanocomposite hollow spheres

Abstract： We performed fluidized bed coating ofAl-based nanoeomposite powder-binder suspensions onto polymer substrates. The effects of the type and amount of the binder and nanoparticle additive on the coating process efficiency and coating characteristics were investigated. The efficiency decreased from 52% to 49% as the processing time increased from 15 to 20 min. However, the amount and thickness of the coating also increased as the processing time and amount of the binder were increased. The addition of nanoparticles to the system decreased the thickness of the coating from 222 to 207 μm when polyvinyl alcohol （PVA） was used as a binder. The suspension containing 3wt% R-4410 binder exhibited the greatest efficiency of 60%.

Oxide coating mechanism during fluidized bed reduction: solid-state reaction characteristics between iron ore particles and MgO

Experiments on the solid-state reaction between iron ore particles and MgO were performed to investigate the coating mechanism of MgO on the iron ore particles＇ surface during fluidized bed reduction. MgO powders and iron ore particles were mixed and compressed into briquettes and, subsequently, roasted at different temperatures and for different time periods. A Mg-containing layer was observed on the outer edge of the iron ore particles when the roasting temperature was greater than 1173 K. The concentration of Fe in the Mg-containing layer was evenly distributed and was approximately 10wt%, regardless of the temperature change. Boundary layers of Mg and Fe were observed outside of the iron ore particles. The change in concentration of Fe in the boundary layers was simulated using a gas–solid diffusion model, and the diffusion coefficients of Fe and Mg in these layers at different temperatures were calculated. The diffusion activation energies of Fe and Mg in the boundary layers in these experiments were evaluated to be approximately 176 and 172 k J/mol, respectively.

A brand new green coating technology for realizing the regulation of spherical propellant energy release process

To achieve the controllable release of energy of nitrocellulose-based propellants,this paper combines the cellulose-based nanocomposites aqueous coating(Surelease®-NC)with fluidized bed coating equipment to successfully prepare the coated spherical propellant for the first time.The effects of fluidized bed coating temperature,air velocity,flow speed and atomization pressure on the adhesion rate,coating integrity and coating uniformity of the coated spherical propellant were investigated,and the preparation of coated spherical propellant with homogeneous size and structural integrity was achieved for the first time.The microscopic morphology,chemical structure,water vapor adsorption behavior,combustion performance,and ageing resistance property of the coated spherical propellant were systematically investigated by,Fourier transforms infrared spectroscopy(FTIR),Micro confocal raman spectrometer,field scanning electron microscopy(SEM),dynamic vapor adsorption techniques,and closed bomb test,confirming the surface core-shell structure and the tightly bonded interfacial structure of coated spherical propellant.Meanwhile,the coated spherical propellant has good hygroscopic,excellent progressive burning and long storage stability.