The nitrile butadiene rubber(NBR)hardness effect on the sealing characteristics of hydraulic O-ring rod seals is analyzed based on a mixed lubrication elastohydrodynamic model.Parameterized studies are conducted to re...The nitrile butadiene rubber(NBR)hardness effect on the sealing characteristics of hydraulic O-ring rod seals is analyzed based on a mixed lubrication elastohydrodynamic model.Parameterized studies are conducted to reveal the mechanism of the influence of rubber hardness on the static and dynamic behavior of seals.The optimized selections of rubber hardness are then investigated under different conditions.Results show that the low hardness seal is prone to stress concentration due to the extrusion effect under high pressure conditions;it is also more prone to leaking.A high hardness seal can better prevent leakage by reducing film thickness but it will cause large frictional power loss and increase the probability of wear failure.The choice of low hardness is recommended to reduce friction with the premise that leakage requirements are met.展开更多
Experimental studies on load decay and leak rate of O-rings made of two kindsof silicone rubber are conducted. The results show that the characteristic of load decay isrelative to the material and temperature of O-rin...Experimental studies on load decay and leak rate of O-rings made of two kindsof silicone rubber are conducted. The results show that the characteristic of load decay isrelative to the material and temperature of O-rings; the rate of load decay increases with the riseof temperature; the effects of load decay on leak rate of O-rings are negligible at roomtemperature, but they are notable at high temperature, and they are related to the material ofO-rings. On the basis of study on the theory of load decay and analysis to the results ofexperiments, a theoretical model is developed to describe the load decay characteristic of O-rings,and it matches the experimental data very well. By the study of time-temperature equivalence of loaddecay, the interconvertting equation of test data of load decay at different temperatures isobtained.展开更多
基金supported by the National Natural Science Foundation of China(No.52005470)the Natural Science Foundation of Zhejiang Province(No.LQ21E050020)the Fundamental Research Funds for the Provincial Universities of Zhejiang(No.2021YW17),China.
文摘The nitrile butadiene rubber(NBR)hardness effect on the sealing characteristics of hydraulic O-ring rod seals is analyzed based on a mixed lubrication elastohydrodynamic model.Parameterized studies are conducted to reveal the mechanism of the influence of rubber hardness on the static and dynamic behavior of seals.The optimized selections of rubber hardness are then investigated under different conditions.Results show that the low hardness seal is prone to stress concentration due to the extrusion effect under high pressure conditions;it is also more prone to leaking.A high hardness seal can better prevent leakage by reducing film thickness but it will cause large frictional power loss and increase the probability of wear failure.The choice of low hardness is recommended to reduce friction with the premise that leakage requirements are met.
基金This project is supported by 863 Program of China (No. 863-2-4-4-7).
文摘Experimental studies on load decay and leak rate of O-rings made of two kindsof silicone rubber are conducted. The results show that the characteristic of load decay isrelative to the material and temperature of O-rings; the rate of load decay increases with the riseof temperature; the effects of load decay on leak rate of O-rings are negligible at roomtemperature, but they are notable at high temperature, and they are related to the material ofO-rings. On the basis of study on the theory of load decay and analysis to the results ofexperiments, a theoretical model is developed to describe the load decay characteristic of O-rings,and it matches the experimental data very well. By the study of time-temperature equivalence of loaddecay, the interconvertting equation of test data of load decay at different temperatures isobtained.