Five experimental self-shielded flux cored wires are fabricated withdifferent amount of Fe_2O_3 in the flux. The effect of Fe_2O_3 on welding technology and mechanicalproperties of weld metals deposited by these wires...Five experimental self-shielded flux cored wires are fabricated withdifferent amount of Fe_2O_3 in the flux. The effect of Fe_2O_3 on welding technology and mechanicalproperties of weld metals deposited by these wires are studied. The results show that with theincrease of Fe_2O_3 in the mix, the melting point of the pretreated mix is increased. LiBaF_3 andBaFe_(12)O_(19), which are very low in inherent moisture, are formed after the pretreatment. Themechanical properties are evaluated to the weld metals. The low temperature notch toughness of theweld metals is increased linearly with the Fe_2O_3 content in the flux due to the balance betweenFe_2O_3 and residual Al in the weld metal. The optimum Fe_2O_3 content in flux is 2.5 percent approx3.5 percent.展开更多
The variation in arc characteristics and behavior of metal transfer with the change in pulse parameters has been studied by high speed video camera during pulse current flux-cored arc weld deposition.A comparative stu...The variation in arc characteristics and behavior of metal transfer with the change in pulse parameters has been studied by high speed video camera during pulse current flux-cored arc weld deposition.A comparative study of similar nature has also been carried out during flux-cored arc weld deposition in globular and spray transfer modes.The effect of pulse parameters has been studied by considering their mean current and arc voltage.The arc characteristics studied by its root diameter,projected diameter and length,and the behavior of metal transfer noted by the metal transfer model and the droplet diameter have been found to vary significantly with the pulse parameters.The observation may help in understanding the arc characteristics with respect to the variation in pulse parameters which may be beneficial in using pulse current FCAW to produce desired weld quality.展开更多
In this work, we utilized high-speed video photography to investigate the arc characteristics, metal transfer behavior, and welding spatter of the pulse-current flux-cored arc welding(P-FCAW) process in the horizontal...In this work, we utilized high-speed video photography to investigate the arc characteristics, metal transfer behavior, and welding spatter of the pulse-current flux-cored arc welding(P-FCAW) process in the horizontal position. The results indicate the presence of a stable ‘‘flux pole'' during both the pulse-on and pulse-off periods when the mean current ranged from 140 to 170 A. The existence of this ‘‘flux pole'' was beneficial for droplet transfer in the‘‘axial droplet transfer'' mode. With respect to welding spatter, with an increase in the welding current, we observed three kinds of spatter—explosive spatter,rebounded droplet spatter, and scattering spatter. With an increase in the pulse current from 310.6 to 345.6 A, the deflection of the arc reduced from 30.4° to 16.6°, which positively influenced the arc rigidity, particularly in the horizontal position.展开更多
Quenched and Tempered （Q＆T） steels are widely used in the construction of military vehicles due to its high strength to weight ratio and high hardness. These steels are prone to hydrogen induced cracking （HIC） an...Quenched and Tempered （Q＆T） steels are widely used in the construction of military vehicles due to its high strength to weight ratio and high hardness. These steels are prone to hydrogen induced cracking （HIC） and softening in the heat affected zone （HAZ） after welding. The use of austenitic stainless steel （ASS） consumables to weld the above steel was the only available remedy to avoid HIC because of higher solubility for hydrogen in austenitic phase. Recent studies revealed that low hydrogen ferritic （LHF） steel consumables can also be used to weld Q＆T steels, which can give very low hydrogen levels in the weld deposits and required resistance against cold cracking. Hence, in this investigation an attempt has been made to study the performance of armour grade Q＆T steel joints fabricated by flux cored arc welding with LHF steel consumables. Two different consumables namely （i） austenitic stainless steel and （ii） low hydrogen ferritic steel have been used to fabricate the joints by flux cored arc welding （FCAW） process. The joints fabricated by LHF consumable exhibited superior transverse tensile properties due to the presence of ferrite microstructure in weld metal. The joints fabricated by ASS consumable showed higher impact toughness due to the presence of austenitic phase in weld metal microstructure. The HAZ softening in coarse grain heat affected zone （CGHAZ） is less in the joints fabricated using LHF consumable due to the lower heat input involved during fabrication compared to the joints fabricated using ASS consumables.展开更多
The formation mechanism of inclusion in welds with different aluminum contents was determined based on thermodynamic equilibrium in self-shielded flux cored arc welds.Inclusions in welds were systematically studied by...The formation mechanism of inclusion in welds with different aluminum contents was determined based on thermodynamic equilibrium in self-shielded flux cored arc welds.Inclusions in welds were systematically studied by optical microscopy,scanning microscopy and image analyzer.The results show that the average size and the contamination rate of inclusions in low-aluminum weld are lower than those in high-aluminum weld.Highly faceted AlN inclusions with big size in the high-aluminum weld are more than those in low-aluminum weld.As a result,the low temperature impact toughness of low-aluminum weld is higher than that of high-aluminum weld.Finally,the thermodynamic analysis indicates that thermodynamic result agrees with the experimental data.展开更多
In this investigation, an attempt has been made to study the influence of welding consumables on the factors that influence cold cracking of armour grade quenched and tempered （Q＆.T） steel welds. Flux cored arc wel...In this investigation, an attempt has been made to study the influence of welding consumables on the factors that influence cold cracking of armour grade quenched and tempered （Q＆.T） steel welds. Flux cored arc welding （FCAW） process were used making welds using austenitic stainless steel （ASS） and low hydrogen ferritic steel （LHF） consumables. The diffusible hydrogen levels in the weld metal of the ASS and LHF consumables were determined by mercury method. Residual stresses were evaluated using X-ray stress analyzer and implant test was carried out to study the cold cracking of the welds. Results indicate that ASS welds offer a greater resistance to cold cracking of armour grade Q＆T steel welds.展开更多
Quenched and Tempered(Q&T) steels are widely used in the construction of military vehicles due to its high strength to weight ratio and high hardness. These steels are prone to hydrogen induced cracking(HIC) in th...Quenched and Tempered(Q&T) steels are widely used in the construction of military vehicles due to its high strength to weight ratio and high hardness. These steels are prone to hydrogen induced cracking(HIC) in the heat affected zone(HAZ) after welding. The use of austenitic stainless steel(ASS) consumables to weld the above steel was the only available remedy because of higher solubility for hydrogen in austenitic phase. The use of stainless steel consumables for a non-stainless steel base metal is not economical. Hence, alternate consumables for welding Q&T steels and their vulnerability to HIC need to be explored. Recent studies proved that low hydrogen ferritic steel(LHF) consumables can be used to weld Q&T steels, which can give very low hydrogen levels in the weld deposits. The use of ASS and LHF consumables will lead to distinct microstructures in their respective welds. This microstructural heterogeneity will have a drastic influence in the fatigue crack growth resistance of armour grade Q&T steel welds. Hence, in this investigation an attempt has been made to study the influence of welding consumables and welding processes on fatigue crack growth behaviour of armour grade Q&T Steel joints. Shielded metal arc welding(SMAW) and Flux cored arc welding(FCAW) were used for fabrication of joints using ASS and LHF consumables. The joints fabricated by SMAW process using LHF consumable exhibited superior fatigue crack growth resistance than all other joints.展开更多
Compared to traditional welding methods, the underwater wet welding is special with many different characteristics due to the unique aqueous environment. It is conducted completely under water by divers and unique wel...Compared to traditional welding methods, the underwater wet welding is special with many different characteristics due to the unique aqueous environment. It is conducted completely under water by divers and unique welding technology is required in the special operation environment. The operating levels of the divers are the key factor to acquire high quality welded joints. In this paper, an underwater wet welding experimental and divers training system is developed to serve divers training and conducting welding experiments. The system consists of life support system, signals real-time monitoring system and communicating system, etc. An underwater butt welding experiment based on welding electrodes is conducted, and the system works well. It proves that the system can guarantee divers welding safely and successfully and high quality weld seam is expected to be acquired.展开更多
Austenitic stainless steel(ASS) and High nickel steel(HNS) welding consumables are being used for welding Q&T steels, as they have higher solubility for hydrogen in austenitic phase, to avoid hydrogen induced crac...Austenitic stainless steel(ASS) and High nickel steel(HNS) welding consumables are being used for welding Q&T steels, as they have higher solubility for hydrogen in austenitic phase, to avoid hydrogen induced cracking(HIC) but they are very expensive. In recent years, the developments of low hydrogen ferritic steel(LHF) consumables that contain no hygroscopic compounds are utilized for welding Q&T steels. Heat affected zone(HAZ) softening is another critical issue during welding of armour grade Q&T steels and it depends on the welding process employed and the weld thermal cycle. In this investigation an attempt has been made to study the influence of welding consumables and welding processes on metallurgical characteristics of armour grade Q&T steel joints by various metallurgical characterization procedures. Shielded metal arc welding(SMAW) and flux cored arc welding(FCAW) processes were used for making welds using ASS, LHF and HNS welding consumables. The joints fabricated by using LHF consumables offered lower degree of HAZ softening and there is no evidence of HIC in the joints fabricated using LHF consumables.展开更多
To study the influence laws of welding parameters on weld porosity, underwater wet flux-cored arc welding （ FCAW） duplex stainless steel S32101 was carried out in a hyperbaric chamber, and the second-order multiple ...To study the influence laws of welding parameters on weld porosity, underwater wet flux-cored arc welding （ FCAW） duplex stainless steel S32101 was carried out in a hyperbaric chamber, and the second-order multiple regression equation was established. The interactive effects of welding parameters on the porosity were analyzed by the three dimensional response surfaces and the contour plots. The results present that the interaction effect between water depth and voltage on the porosity is the most significant. Theoretically, a non-pores weld bead can be gained by reasonably matching these parameters with water depth less than 10 m. Always, the weld porosity reaches its peak value with a 7 mm/s welding speed.展开更多
文摘Five experimental self-shielded flux cored wires are fabricated withdifferent amount of Fe_2O_3 in the flux. The effect of Fe_2O_3 on welding technology and mechanicalproperties of weld metals deposited by these wires are studied. The results show that with theincrease of Fe_2O_3 in the mix, the melting point of the pretreated mix is increased. LiBaF_3 andBaFe_(12)O_(19), which are very low in inherent moisture, are formed after the pretreatment. Themechanical properties are evaluated to the weld metals. The low temperature notch toughness of theweld metals is increased linearly with the Fe_2O_3 content in the flux due to the balance betweenFe_2O_3 and residual Al in the weld metal. The optimum Fe_2O_3 content in flux is 2.5 percent approx3.5 percent.
文摘The variation in arc characteristics and behavior of metal transfer with the change in pulse parameters has been studied by high speed video camera during pulse current flux-cored arc weld deposition.A comparative study of similar nature has also been carried out during flux-cored arc weld deposition in globular and spray transfer modes.The effect of pulse parameters has been studied by considering their mean current and arc voltage.The arc characteristics studied by its root diameter,projected diameter and length,and the behavior of metal transfer noted by the metal transfer model and the droplet diameter have been found to vary significantly with the pulse parameters.The observation may help in understanding the arc characteristics with respect to the variation in pulse parameters which may be beneficial in using pulse current FCAW to produce desired weld quality.
文摘In this work, we utilized high-speed video photography to investigate the arc characteristics, metal transfer behavior, and welding spatter of the pulse-current flux-cored arc welding(P-FCAW) process in the horizontal position. The results indicate the presence of a stable ‘‘flux pole'' during both the pulse-on and pulse-off periods when the mean current ranged from 140 to 170 A. The existence of this ‘‘flux pole'' was beneficial for droplet transfer in the‘‘axial droplet transfer'' mode. With respect to welding spatter, with an increase in the welding current, we observed three kinds of spatter—explosive spatter,rebounded droplet spatter, and scattering spatter. With an increase in the pulse current from 310.6 to 345.6 A, the deflection of the arc reduced from 30.4° to 16.6°, which positively influenced the arc rigidity, particularly in the horizontal position.
基金New Delhi for funding this project work(Project No.MAA/03/41)
文摘Quenched and Tempered （Q＆T） steels are widely used in the construction of military vehicles due to its high strength to weight ratio and high hardness. These steels are prone to hydrogen induced cracking （HIC） and softening in the heat affected zone （HAZ） after welding. The use of austenitic stainless steel （ASS） consumables to weld the above steel was the only available remedy to avoid HIC because of higher solubility for hydrogen in austenitic phase. Recent studies revealed that low hydrogen ferritic （LHF） steel consumables can also be used to weld Q＆T steels, which can give very low hydrogen levels in the weld deposits and required resistance against cold cracking. Hence, in this investigation an attempt has been made to study the performance of armour grade Q＆T steel joints fabricated by flux cored arc welding with LHF steel consumables. Two different consumables namely （i） austenitic stainless steel and （ii） low hydrogen ferritic steel have been used to fabricate the joints by flux cored arc welding （FCAW） process. The joints fabricated by LHF consumable exhibited superior transverse tensile properties due to the presence of ferrite microstructure in weld metal. The joints fabricated by ASS consumable showed higher impact toughness due to the presence of austenitic phase in weld metal microstructure. The HAZ softening in coarse grain heat affected zone （CGHAZ） is less in the joints fabricated using LHF consumable due to the lower heat input involved during fabrication compared to the joints fabricated using ASS consumables.
文摘The formation mechanism of inclusion in welds with different aluminum contents was determined based on thermodynamic equilibrium in self-shielded flux cored arc welds.Inclusions in welds were systematically studied by optical microscopy,scanning microscopy and image analyzer.The results show that the average size and the contamination rate of inclusions in low-aluminum weld are lower than those in high-aluminum weld.Highly faceted AlN inclusions with big size in the high-aluminum weld are more than those in low-aluminum weld.As a result,the low temperature impact toughness of low-aluminum weld is higher than that of high-aluminum weld.Finally,the thermodynamic analysis indicates that thermodynamic result agrees with the experimental data.
基金Armament Research Board (ARMREB),New Delhi for funding this projectwork (Project No MAA/03/41)
文摘In this investigation, an attempt has been made to study the influence of welding consumables on the factors that influence cold cracking of armour grade quenched and tempered （Q＆.T） steel welds. Flux cored arc welding （FCAW） process were used making welds using austenitic stainless steel （ASS） and low hydrogen ferritic steel （LHF） consumables. The diffusible hydrogen levels in the weld metal of the ASS and LHF consumables were determined by mercury method. Residual stresses were evaluated using X-ray stress analyzer and implant test was carried out to study the cold cracking of the welds. Results indicate that ASS welds offer a greater resistance to cold cracking of armour grade Q＆T steel welds.
基金New Delhi for funding this project work(Project No MAA/03/41)
文摘Quenched and Tempered(Q&T) steels are widely used in the construction of military vehicles due to its high strength to weight ratio and high hardness. These steels are prone to hydrogen induced cracking(HIC) in the heat affected zone(HAZ) after welding. The use of austenitic stainless steel(ASS) consumables to weld the above steel was the only available remedy because of higher solubility for hydrogen in austenitic phase. The use of stainless steel consumables for a non-stainless steel base metal is not economical. Hence, alternate consumables for welding Q&T steels and their vulnerability to HIC need to be explored. Recent studies proved that low hydrogen ferritic steel(LHF) consumables can be used to weld Q&T steels, which can give very low hydrogen levels in the weld deposits. The use of ASS and LHF consumables will lead to distinct microstructures in their respective welds. This microstructural heterogeneity will have a drastic influence in the fatigue crack growth resistance of armour grade Q&T steel welds. Hence, in this investigation an attempt has been made to study the influence of welding consumables and welding processes on fatigue crack growth behaviour of armour grade Q&T Steel joints. Shielded metal arc welding(SMAW) and Flux cored arc welding(FCAW) were used for fabrication of joints using ASS and LHF consumables. The joints fabricated by SMAW process using LHF consumable exhibited superior fatigue crack growth resistance than all other joints.
基金This research is supported by the National Natural Science Foundation of China （No. 51105237 and No. 51105103）.
文摘Compared to traditional welding methods, the underwater wet welding is special with many different characteristics due to the unique aqueous environment. It is conducted completely under water by divers and unique welding technology is required in the special operation environment. The operating levels of the divers are the key factor to acquire high quality welded joints. In this paper, an underwater wet welding experimental and divers training system is developed to serve divers training and conducting welding experiments. The system consists of life support system, signals real-time monitoring system and communicating system, etc. An underwater butt welding experiment based on welding electrodes is conducted, and the system works well. It proves that the system can guarantee divers welding safely and successfully and high quality weld seam is expected to be acquired.
基金Project (09003) supported by the Open-Fund Research of State Key Laboratory of Advanced Welding and Joining,Harbin Institute of Technology,ChinaProject (JD0805) supported by the Science and Technology Innovation Team,Jiangsu University,China
基金Armament Research Board (ARMREB), New Delhi for funding this project work (Project no. MAA/03/ 41)
文摘Austenitic stainless steel(ASS) and High nickel steel(HNS) welding consumables are being used for welding Q&T steels, as they have higher solubility for hydrogen in austenitic phase, to avoid hydrogen induced cracking(HIC) but they are very expensive. In recent years, the developments of low hydrogen ferritic steel(LHF) consumables that contain no hygroscopic compounds are utilized for welding Q&T steels. Heat affected zone(HAZ) softening is another critical issue during welding of armour grade Q&T steels and it depends on the welding process employed and the weld thermal cycle. In this investigation an attempt has been made to study the influence of welding consumables and welding processes on metallurgical characteristics of armour grade Q&T steel joints by various metallurgical characterization procedures. Shielded metal arc welding(SMAW) and flux cored arc welding(FCAW) processes were used for making welds using ASS, LHF and HNS welding consumables. The joints fabricated by using LHF consumables offered lower degree of HAZ softening and there is no evidence of HIC in the joints fabricated using LHF consumables.
基金the National Natural Science Foundation of China(Grant No.51374111&51175185)Science and Technology Plan Project of Guangdong Province(Grant No.2015B050502005)for financial support
文摘To study the influence laws of welding parameters on weld porosity, underwater wet flux-cored arc welding （ FCAW） duplex stainless steel S32101 was carried out in a hyperbaric chamber, and the second-order multiple regression equation was established. The interactive effects of welding parameters on the porosity were analyzed by the three dimensional response surfaces and the contour plots. The results present that the interaction effect between water depth and voltage on the porosity is the most significant. Theoretically, a non-pores weld bead can be gained by reasonably matching these parameters with water depth less than 10 m. Always, the weld porosity reaches its peak value with a 7 mm/s welding speed.