In this article,NiCr coatings with chromium content of 13%,27%and 41%were prepared by arc spraying.They were exposed in molten salts(NaCl-Na_(2)SO_(4))at 800℃for 200 hours.The effect of chromium content on the hot co...In this article,NiCr coatings with chromium content of 13%,27%and 41%were prepared by arc spraying.They were exposed in molten salts(NaCl-Na_(2)SO_(4))at 800℃for 200 hours.The effect of chromium content on the hot corrosion behavior of the coatings was in-vestigated.X-ray diffraction(XRD)and scanning electron microscope with energy dispersion spectrum(SEM-EDS)were used to analyze the phase compositions,morphologies and chemical compositions of the coatings.The results show that NiCr13 coating exhibited the worst hot corrosion resistance due to the low chromium content,which resulted in NiO being the major reaction product.It should be noted that the hot corrosion resistance of NiCr27 coating was better than that of NiCr41 coating.The basic fluxing of Cr_(2)O_(3) lowered its protection during the hot corrosion process and led to the formation of porous Cr_(2)O_(3) on the NiCr41 coating.The molten salts accelerated the oxidation reac-tion resulting in thicker and porous oxide scales formed on the surfaces of coatings.展开更多
In high speed continuous casting of peritectic steel slabs, mold fluxes with high basicity are required for less surface defect product. However, the basicity of remaining liquid slag film tends to decrease in casting...In high speed continuous casting of peritectic steel slabs, mold fluxes with high basicity are required for less surface defect product. However, the basicity of remaining liquid slag film tends to decrease in casting process because of the crystallization of 3CaO ·2SiO2 · CaF2. Thus, a way is put forward to improve mold fluxesr properties by raising the original basicity. In order to confirm the possibility of this method, the effect of rising original basicity on the properties of mold fluxes is discussed. Properties of high fluorine based mold fluxes with different basicities and contents of CaF2 , Na2 O, and MgO were measured, respectively. Then, properties of higher basicity mold fluxes were discussed and compared with traditional ones. The results show that increasing the basicity index can improve the melting and flow property of mold fluxes. With the increasing basicity, crystallization rate of mold fluxes increases obviously and crystallization temperature tends to decrease when the basicity exceeds 1.35. The method presen- ted before is proved as a potential way to resolve the contradiction between horizontal heat transfer controlling and solidified shell lubricating for peritectic steel slab casting. But further study on improving the flow property of liquid slag is needed. This work can be used to guide mold fluxes design for high speed continuous casting of peritectic steel slabs.展开更多
基金supported by Corporate Talent Fund Program of Zhengzhou Research Institute of Mechanical Engineering Co.,Ltd.(No.201SJ2023013)the Faculty of Materials and Manufacturing,Beijing University of Technology.
文摘In this article,NiCr coatings with chromium content of 13%,27%and 41%were prepared by arc spraying.They were exposed in molten salts(NaCl-Na_(2)SO_(4))at 800℃for 200 hours.The effect of chromium content on the hot corrosion behavior of the coatings was in-vestigated.X-ray diffraction(XRD)and scanning electron microscope with energy dispersion spectrum(SEM-EDS)were used to analyze the phase compositions,morphologies and chemical compositions of the coatings.The results show that NiCr13 coating exhibited the worst hot corrosion resistance due to the low chromium content,which resulted in NiO being the major reaction product.It should be noted that the hot corrosion resistance of NiCr27 coating was better than that of NiCr41 coating.The basic fluxing of Cr_(2)O_(3) lowered its protection during the hot corrosion process and led to the formation of porous Cr_(2)O_(3) on the NiCr41 coating.The molten salts accelerated the oxidation reac-tion resulting in thicker and porous oxide scales formed on the surfaces of coatings.
基金Item Sponsored by National Natural Science Foundation of China(50904083)
文摘In high speed continuous casting of peritectic steel slabs, mold fluxes with high basicity are required for less surface defect product. However, the basicity of remaining liquid slag film tends to decrease in casting process because of the crystallization of 3CaO ·2SiO2 · CaF2. Thus, a way is put forward to improve mold fluxesr properties by raising the original basicity. In order to confirm the possibility of this method, the effect of rising original basicity on the properties of mold fluxes is discussed. Properties of high fluorine based mold fluxes with different basicities and contents of CaF2 , Na2 O, and MgO were measured, respectively. Then, properties of higher basicity mold fluxes were discussed and compared with traditional ones. The results show that increasing the basicity index can improve the melting and flow property of mold fluxes. With the increasing basicity, crystallization rate of mold fluxes increases obviously and crystallization temperature tends to decrease when the basicity exceeds 1.35. The method presen- ted before is proved as a potential way to resolve the contradiction between horizontal heat transfer controlling and solidified shell lubricating for peritectic steel slab casting. But further study on improving the flow property of liquid slag is needed. This work can be used to guide mold fluxes design for high speed continuous casting of peritectic steel slabs.