The effects of process parameters on the depth-to-width ratio (D/W) of flux-cored wire underwater wet welding with a certain type of homemade .flux-cored wire are studied. It is found that the welding .speed, wire f...The effects of process parameters on the depth-to-width ratio (D/W) of flux-cored wire underwater wet welding with a certain type of homemade .flux-cored wire are studied. It is found that the welding .speed, wire feeding speed and torch oscillating amplitude hare significant effects on the dopth-to-width ratio (D/W) of welds. The D/W ratio of welds increases significantly with the increase of welding speed without the oscillating of welding torch. It increased (from 0. 14 to 0. 26 ) with the increase of wire feeding speed while the torch oscillating. And it decreased linearly with the increase of torch oscillating amplitude. However, the influelwe of oscillating speed, wire extension and welding voltage on the D/W ratio of welds was not obvious.展开更多
Metal transfer behavior of six kinds of self shielded flux cored wire(SSFCW) is studied using the apparatus of SSFCW high speed photography self made. Six kinds of metal transfer modes of SSFCW were obtained throu...Metal transfer behavior of six kinds of self shielded flux cored wire(SSFCW) is studied using the apparatus of SSFCW high speed photography self made. Six kinds of metal transfer modes of SSFCW were obtained through observation for high speed photograph film and analysis. It is believed that the research is of magnificent for improving operative performance and mechanical properties of SSFCW and dynamics characteristic of welding power.展开更多
The effect of graphene oxide(GO)and reduced graphene oxide(RGO)nanosheets on the microstructure and mechanical properties of welded joints of mild steel was evaluated by flux-cored arc welding.GO was synthesized by th...The effect of graphene oxide(GO)and reduced graphene oxide(RGO)nanosheets on the microstructure and mechanical properties of welded joints of mild steel was evaluated by flux-cored arc welding.GO was synthesized by the Hummer’s method and was reduced under hydrothermal conditions at a pressure of 1.1 MPa at 180°C for 12 h.1,3,and 10 mg/mL paste fillers were used in GO and RGO,and applied to the weld notch.The results clearly showed that by increasing the concentration of RGO up to 10 mg/mL,the tensile strength and hardness of the weld metal were improved by approximately 20.5%and 38.4%,respectively,because the coarse grains were changed into fine domains.The domain of the nanosheets cluster was 19.85×10^?9 m.Specifically,the RGO nanosheets contributed to modifying the mechanical properties of the welded steel,likely due to dislocation pinning.展开更多
The variation in arc characteristics and behavior of metal transfer with the change in pulse parameters has been studied by high speed video camera during pulse current flux-cored arc weld deposition.A comparative stu...The variation in arc characteristics and behavior of metal transfer with the change in pulse parameters has been studied by high speed video camera during pulse current flux-cored arc weld deposition.A comparative study of similar nature has also been carried out during flux-cored arc weld deposition in globular and spray transfer modes.The effect of pulse parameters has been studied by considering their mean current and arc voltage.The arc characteristics studied by its root diameter,projected diameter and length,and the behavior of metal transfer noted by the metal transfer model and the droplet diameter have been found to vary significantly with the pulse parameters.The observation may help in understanding the arc characteristics with respect to the variation in pulse parameters which may be beneficial in using pulse current FCAW to produce desired weld quality.展开更多
In this work, we utilized high-speed video photography to investigate the arc characteristics, metal transfer behavior, and welding spatter of the pulse-current flux-cored arc welding(P-FCAW) process in the horizontal...In this work, we utilized high-speed video photography to investigate the arc characteristics, metal transfer behavior, and welding spatter of the pulse-current flux-cored arc welding(P-FCAW) process in the horizontal position. The results indicate the presence of a stable ‘‘flux pole'' during both the pulse-on and pulse-off periods when the mean current ranged from 140 to 170 A. The existence of this ‘‘flux pole'' was beneficial for droplet transfer in the‘‘axial droplet transfer'' mode. With respect to welding spatter, with an increase in the welding current, we observed three kinds of spatter—explosive spatter,rebounded droplet spatter, and scattering spatter. With an increase in the pulse current from 310.6 to 345.6 A, the deflection of the arc reduced from 30.4° to 16.6°, which positively influenced the arc rigidity, particularly in the horizontal position.展开更多
The effects of alloying elements in welding wires and submerged arc welding process on the microstructures and low-temperature impact toughness of weld metals have been investigated. The results indicate that the opti...The effects of alloying elements in welding wires and submerged arc welding process on the microstructures and low-temperature impact toughness of weld metals have been investigated. The results indicate that the optimal contents of alloying elements in welding wires can improve the low-temperature impact toughness of weld metals because the proeutectoid ferrite and bainite formations can be suppressed, and the fraction of acicular ferrite increases. However, the contents of alloying elements need to vary along with the welding heat input. With the increase in welding heat input, the contents of alloying elements in welding wires need to be increased accordingly. The microstructures mainly consisting of acicular ferrite can be obtained in weld metals after four-wire submerged arc welding using the wires with a low carbon content and appropriate contents of Mn, Mo, Ti-B, Cu, Ni, and RE, resulting in the high low-temperature impact toughness of weld metals.展开更多
The weld appearance, deposition rate, welding efficiency, stability of arc, laser keyhole characteristic, and weld property were studied by using a novel laser-MIG hybrid welding process with filling wire of aluminum ...The weld appearance, deposition rate, welding efficiency, stability of arc, laser keyhole characteristic, and weld property were studied by using a novel laser-MIG hybrid welding process with filling wire of aluminum alloy. The results were also compared with those by conventional laser-MIG hybrid welding process. It was found that with the suitable process parameters this novel welding process for aluminum alloy was stable and final weld bead had fine appearance. Compared to conventional laser-MIG hybrid welding process, during this novel welding process the stability of arc, the laser keyhole characteristic and the weld property were similar, while the keyhole cycle frequency and keyhole opening area had differences of 1.23% and 15.34%, respectively, and the welding efficiency increased by about 31% without increasing heat input.展开更多
Laser welding with filler wire of AZ31 magnesium alloys is investigated using a CO2 laser experimental system. The effect of three different filler wires on the joint properties is researched. The results show that th...Laser welding with filler wire of AZ31 magnesium alloys is investigated using a CO2 laser experimental system. The effect of three different filler wires on the joint properties is researched. The results show that the weld appearance can be effectively improved when using laser welding with filler wire. The microhardness and tensile strength of joints are almost the same us those of the base metal when ER AZ31 or ER AZ61 wire is adopted. However, when the filler wire of ER 5356 aluminum alloy is used, the mechanical properties of flints become worse. For ER AZ31 and ER AZ61 filler wires, the microstructure of weld zone slws small dendrite grains. In comparison, for ER 5356 filler wire, the weld shows a structure of snowy dendrites and many intermetallic compounds and eutectic phases distribute in the dendrites. These intermetallic constituents with low melting point increase the tendency of hot crack and result in fiagile joint properties. Therefore, ER AZ31 and ER AZ61 wire are more suitable filler material than ER 5356 for CO2 laser welding of AZ31 magnesium alloys.展开更多
Weldability test was carried out on the newly developed fine grain, low sulphur, high strength and high toughness pipeline steel of X80 and its matching SAW wire. Test of maximum hardness in welding heat-affected zone...Weldability test was carried out on the newly developed fine grain, low sulphur, high strength and high toughness pipeline steel of X80 and its matching SAW wire. Test of maximum hardness in welding heat-affected zone and test of Y groove cracking show that X80 steel features low hardenability and good cracking resistance. The submerged arc welding joint made with the newly developed low carbon and multi-alloyed SAW wire of WGX2 exhibits a little higher strength than the base metal, qualified bending performance, under maximum limitation hardness and good impact toughness, which can completely meet the technical requirement of X80 steel. Despite somewhat coarsening the grain size in welding heat-affected zone is still much finer than that of traditional steels, and the microstructure in weld metal is almost full acicular ferrite. The results show that X80 steel and WGX2 wire are of great weldability.展开更多
The arc characteristics of submerged arc welding (SAW) with stainless steel wire were studied by using Analysator Hannover (AH). The tests were carded out under the same preset arc voltage combined with different ...The arc characteristics of submerged arc welding (SAW) with stainless steel wire were studied by using Analysator Hannover (AH). The tests were carded out under the same preset arc voltage combined with different welding currents. By comparing the probability density distribution (PDD) curves of arc voltage and welding current, the changes were analyzed, the metal transfer mode in SAW was deduced, and the characteristics of a stable arc were summarized. The analysis results show that, with an increase of welding parameters, the short-circuiting peak in the PDD curves of arc voltage decreases gradually until it disappears, and the dominant metal transfer mode changes from flux-wall guided transfer to projected transfer and then to streaming transfer. Moreover, when the PDD curves of arc voltage are both unimodal and generally symmetrical, the greater the peak probability and the smaller the peak span, the more stable the arc becomes.展开更多
The metal transfer mode of electron beam welding (EBW) with filler wire was studied experimentally. The spatial position between the electron beam and the filler wire was defined. Basing on the charge coupled device...The metal transfer mode of electron beam welding (EBW) with filler wire was studied experimentally. The spatial position between the electron beam and the filler wire was defined. Basing on the charge coupled device (CCD) visual sensing system, the metal transfer mode of filler wire was investigated. The results showed that there were five transfer modes during EBW process due to different wire feed rates and spatial positions between beam and filler wire, such as short-circuiting mode, molten metal bridge mode, small droplet mode, big droplet mode and mixed mode. By comparing the weld appearance of different transfer modes, the molten metal bridge transfer was proved to be the best transfer mode.展开更多
7 xxx welding wire was self-made by spray forming ingots drawn to series welding wires products,and then TIG butt welding test is used for 5 mm thick 7075 high-strength aluminium alloy.After welding,the stress relief+...7 xxx welding wire was self-made by spray forming ingots drawn to series welding wires products,and then TIG butt welding test is used for 5 mm thick 7075 high-strength aluminium alloy.After welding,the stress relief+solid-solution aging heat treatment(T6)were performed to joints,and the mechanical properties and microstructure of the joints before and after heat treatment were comparative analyzed.The results show that the properties of the heat-affected zone(HAZ)of the joint before heat treatment decreas,and the joint is softened.The welded joints tensile strength is 271.8 MPa,the elongation is 5.6%,and the average hardness of the weld is 118.4 HV.The second phase particles such asη(Mg Zn2),S(Al2 Cu Mg),Al13 Fe4 are distributed in a network layer,with no apparent element segregation.After heat treatment,the structure of each area of the joint is coarsened,and a small amount of Fe-containing impurity phases are distributed.Theηand S phases are dissolved in the matrix.The hardness of each area of the joint is increased to 155 HV,and the softening zone is disappeared,this leads the joint elongation close to 16.9%.The tensile strength is increased to 511.8 MPa,reaching 94%of the base metal tensile strength.展开更多
With preheating wire by resistance heat, laser hot wire welding improves process stability and wire deposition efficiency, which gives broad potential applications in sugracing and narrow gap welding. It is a critical...With preheating wire by resistance heat, laser hot wire welding improves process stability and wire deposition efficiency, which gives broad potential applications in sugracing and narrow gap welding. It is a critical issue to control the temperature of preheated wire in this process. The temperature which is so high that the wire fuses outside molten pool or so low that the wire cannot melt timely in the molten pool, results in poor wire transfer stability and bad weld formation. This paper is purposed to calculate the wire temperature for the prediction of wire transfer behavior under various welding parameters. A heat conduction model is set up. Heat sources of the wire include resistance heat and reflected laser, and the heat source of molten pool is laser. The calculated temperature of wire part outside the molten pool is verified by infrared ratio temperature measurement. The calculated temperature of wire part in the molten pool is verified by measurement of the molten pool size. Analyzing the wire temperature and welding process observed by the high speed video imaging, the temperature criteria of wire transfer behaviors are obtained. Thus, numerical simulation of the wire temperature can be used to predict wire transfer behaviors in laser hot wire welding.展开更多
According to the study of the microstructure and properties of X100 pipeline steel, the welding consumable-wire based on Mn-Ni-Mo-B-Ti alloy system was successfully designed and developed. The yield strength of the de...According to the study of the microstructure and properties of X100 pipeline steel, the welding consumable-wire based on Mn-Ni-Mo-B-Ti alloy system was successfully designed and developed. The yield strength of the deposited metal of the developed welding wire was 695 MPa, the tensile strength was 810 MPa, and Charpy impact energy was 92 J at negative 20 ℃ when matching with BSG-SJ101H1 sintered flux. The results of the weldability test for X100 pipeline steel which adopting this developed wire showed that the tensile strength of the weld was 827 MPa, 185 J of Charpy impact energy( -10 ℃ ) , 97% of section of shear and the weld had good strength and toughness matching when the welding speed got to 1.7 m/min. The microstructure and fracture appearance of the weld were analyzed by using metallographic microscope, scanning electron microscope (SEM) and laser confocal microscope, the results indicated that the microstructure was mainly granular bainite in the weld metal, and the fracture was dimple with 200 - 300 μm depth presenting a typical ductile fracture characteristics. The test of welding wire with different content of Ni and Cr element indicated that Ni was better than Cr in improving the strength and toughness of weld metal.展开更多
The welding wire feed mechanism is an important component of welding equipment, both reliability and stabilization are the premise that the welding quality can be ensured. The PID is currently adapted to control the w...The welding wire feed mechanism is an important component of welding equipment, both reliability and stabilization are the premise that the welding quality can be ensured. The PID is currently adapted to control the welding wire feed mechanism, although the fuzzy PID has advantage of fast response and adaptation, the precision of fuzzy PID is lower. Accordingly, the fuzzy self-adaptive PID controller was proposed through changing fuzzy input variables and output variables based on variable universe, simple furwtion is adopted as scaling factor, the fuzzy PID controller parameters are adjusted to improve the precision and adjustment range. Simulation results show that control effects of fuzzy self-adaptive PID adopted by the welding wire feed mechanism have good adaptive ability and robustness based on variable universe, the welding experiments indicate that the welding quality met the requirements actually.展开更多
CO2 laser welding aluminum alloy with filler wire was studied. The results indicate that the problems in CO2 laser welding of Al alloy, such as bad appearance of weld, easily excessive penetration and low strength, ca...CO2 laser welding aluminum alloy with filler wire was studied. The results indicate that the problems in CO2 laser welding of Al alloy, such as bad appearance of weld, easily excessive penetration and low strength, can be improved effectively by using laser welding with filler wire, and the maximum tensile strength of weld can reach 94% for the base metal. It also can be found that, the linear energy have great influence on the microstructure and mechanical properties of the joint. As the heat input increases, the cellular fir-tree crystals in the weld zone become sparse and the form of tensile fracture transforms from gliding fracture to brittle fracture.展开更多
Traditional welding methods are limited in low heat input to workpiece and high welding wire melting rate. Twin-wire indirect arc(TWIA) welding is a new welding method characterized by high melting rate and low heat...Traditional welding methods are limited in low heat input to workpiece and high welding wire melting rate. Twin-wire indirect arc(TWIA) welding is a new welding method characterized by high melting rate and low heat input. This method uses two wires one connected to the negative electrode and another to the positive electrode of a direct-current(DC) power source. The workpiece is an independent, non-connected unit. A three dimensional finite element model of TWIA is devised. Electric and magnetic fields are calculated and their influence upon TWIA behavior and the welding process is discussed. The results show that with a 100 A welding current, the maximum temperature reached is 17 758 K, arc voltage is 14.646 V while maximum current density was 61 A/mm2 with a maximum Lorene force of 84.5 ~tN. The above mentioned arc parameters near the cathode and anode regions are far higher than those in the arc column region. The Lorene force is the key reason for plasma velocity direction deviated and charged particles flowed in the channel formed by the cathode, anode and upper part of arc column regions. This led to most of the energy being supplied to the polar and upper part of arc column regions. The interaction between electric and magnetic fields is a major determinant in shaping TWIA as well as heat input on the workpiece. This is a first study of electromagnetic characteristics and their influences in the TWIA welding process, and it is significant in both a theoretical and practical sense.展开更多
In this study,the welding thermal cycle curve exhibited two temperature peaks in high heat-input twin-wire separate-pool submerged-arc welding and coarse-grained heat affected zone existed in the welded joint. The inc...In this study,the welding thermal cycle curve exhibited two temperature peaks in high heat-input twin-wire separate-pool submerged-arc welding and coarse-grained heat affected zone existed in the welded joint. The inclusions of primary weld metal and coarse-grained heat affected zone of Ce-added SAW should be Al_2O_3,MnO,SiO_2,TiO,Ce_2S_3,CeS,Ce_2O_2S and Ce_2O_3. Under the effect of welding thermal cycle,oxy-sulfides inclusions of Ce,the diameter of which was less than 2. 0 μm,slightly grew larger,but the composition and type of the inclusions didn't change. The microstructure of the large heat input weld metal had acicular ferrite that Ce oxide sulphide particles induced nucleation and proeutectoid ferrite. In the coarse-grained heat affected zone of weld metal,home-position precipitation of acicular ferrite and sympathetic acicular ferrite were both observed. It was supposed that previous crystal cells of acicular ferrite in austenite grain promoted home-position precipitation of acicular ferrite. Meanwhile,sympathetic acicular ferrite tended to nucleate at the primary acicular ferrite grain boundaries,where high dislocation density was located,and grew inside the neighboring carbon-depleted austenitic regions. The granular bainite nucleated in the austenitic zone with high carbon content close to acicular ferrite and sympathetic acicular ferrite.展开更多
In the three-wire welding system, a welding process consists of the operations of four devices, namely three welding machines and one bogie. The operations need to be synchronized by a numerical coordinate controller ...In the three-wire welding system, a welding process consists of the operations of four devices, namely three welding machines and one bogie. The operations need to be synchronized by a numerical coordinate controller ( NCC ). In this paper, we will discuss a tnsk-job-procedure cubic program structure. Under this structure, the devices are synchronized and isolated at the same time. This cubic program structure can also be used as a reference for other multi-device or multi-unit manufacturing processes.展开更多
The temperature fields in laser + GMAW-P hybrid welding for different laser-wire distances in quasi-steady state were calculated using an developed combined heat source model, and the influence of laser-wire distance...The temperature fields in laser + GMAW-P hybrid welding for different laser-wire distances in quasi-steady state were calculated using an developed combined heat source model, and the influence of laser-wire distance on them was analyzed. The results show tbat, at a low level of arc power, the temperature profiles caused by laser and arc energy respecively cannot couple well when the laser-wire distance reaches 4 mm, a trend of separation between them beginning to take place. In the case of high arc power, both the critical laser-wire distance and HAZ width increase.展开更多
文摘The effects of process parameters on the depth-to-width ratio (D/W) of flux-cored wire underwater wet welding with a certain type of homemade .flux-cored wire are studied. It is found that the welding .speed, wire feeding speed and torch oscillating amplitude hare significant effects on the dopth-to-width ratio (D/W) of welds. The D/W ratio of welds increases significantly with the increase of welding speed without the oscillating of welding torch. It increased (from 0. 14 to 0. 26 ) with the increase of wire feeding speed while the torch oscillating. And it decreased linearly with the increase of torch oscillating amplitude. However, the influelwe of oscillating speed, wire extension and welding voltage on the D/W ratio of welds was not obvious.
文摘Metal transfer behavior of six kinds of self shielded flux cored wire(SSFCW) is studied using the apparatus of SSFCW high speed photography self made. Six kinds of metal transfer modes of SSFCW were obtained through observation for high speed photograph film and analysis. It is believed that the research is of magnificent for improving operative performance and mechanical properties of SSFCW and dynamics characteristic of welding power.
基金the Sustainable Nano Surfaces of the East(Payanano.com)Company in Islamic Republic of Iran.
文摘The effect of graphene oxide(GO)and reduced graphene oxide(RGO)nanosheets on the microstructure and mechanical properties of welded joints of mild steel was evaluated by flux-cored arc welding.GO was synthesized by the Hummer’s method and was reduced under hydrothermal conditions at a pressure of 1.1 MPa at 180°C for 12 h.1,3,and 10 mg/mL paste fillers were used in GO and RGO,and applied to the weld notch.The results clearly showed that by increasing the concentration of RGO up to 10 mg/mL,the tensile strength and hardness of the weld metal were improved by approximately 20.5%and 38.4%,respectively,because the coarse grains were changed into fine domains.The domain of the nanosheets cluster was 19.85×10^?9 m.Specifically,the RGO nanosheets contributed to modifying the mechanical properties of the welded steel,likely due to dislocation pinning.
文摘The variation in arc characteristics and behavior of metal transfer with the change in pulse parameters has been studied by high speed video camera during pulse current flux-cored arc weld deposition.A comparative study of similar nature has also been carried out during flux-cored arc weld deposition in globular and spray transfer modes.The effect of pulse parameters has been studied by considering their mean current and arc voltage.The arc characteristics studied by its root diameter,projected diameter and length,and the behavior of metal transfer noted by the metal transfer model and the droplet diameter have been found to vary significantly with the pulse parameters.The observation may help in understanding the arc characteristics with respect to the variation in pulse parameters which may be beneficial in using pulse current FCAW to produce desired weld quality.
文摘In this work, we utilized high-speed video photography to investigate the arc characteristics, metal transfer behavior, and welding spatter of the pulse-current flux-cored arc welding(P-FCAW) process in the horizontal position. The results indicate the presence of a stable ‘‘flux pole'' during both the pulse-on and pulse-off periods when the mean current ranged from 140 to 170 A. The existence of this ‘‘flux pole'' was beneficial for droplet transfer in the‘‘axial droplet transfer'' mode. With respect to welding spatter, with an increase in the welding current, we observed three kinds of spatter—explosive spatter,rebounded droplet spatter, and scattering spatter. With an increase in the pulse current from 310.6 to 345.6 A, the deflection of the arc reduced from 30.4° to 16.6°, which positively influenced the arc rigidity, particularly in the horizontal position.
基金supported by the Research and Development Project of Science and Technology of Hebei Province, China (No.03212211D and No.002121186D)
文摘The effects of alloying elements in welding wires and submerged arc welding process on the microstructures and low-temperature impact toughness of weld metals have been investigated. The results indicate that the optimal contents of alloying elements in welding wires can improve the low-temperature impact toughness of weld metals because the proeutectoid ferrite and bainite formations can be suppressed, and the fraction of acicular ferrite increases. However, the contents of alloying elements need to vary along with the welding heat input. With the increase in welding heat input, the contents of alloying elements in welding wires need to be increased accordingly. The microstructures mainly consisting of acicular ferrite can be obtained in weld metals after four-wire submerged arc welding using the wires with a low carbon content and appropriate contents of Mn, Mo, Ti-B, Cu, Ni, and RE, resulting in the high low-temperature impact toughness of weld metals.
基金supported by the Key Science and Technology of Jilin Province(Grant No.20140204070GX)
文摘The weld appearance, deposition rate, welding efficiency, stability of arc, laser keyhole characteristic, and weld property were studied by using a novel laser-MIG hybrid welding process with filling wire of aluminum alloy. The results were also compared with those by conventional laser-MIG hybrid welding process. It was found that with the suitable process parameters this novel welding process for aluminum alloy was stable and final weld bead had fine appearance. Compared to conventional laser-MIG hybrid welding process, during this novel welding process the stability of arc, the laser keyhole characteristic and the weld property were similar, while the keyhole cycle frequency and keyhole opening area had differences of 1.23% and 15.34%, respectively, and the welding efficiency increased by about 31% without increasing heat input.
文摘Laser welding with filler wire of AZ31 magnesium alloys is investigated using a CO2 laser experimental system. The effect of three different filler wires on the joint properties is researched. The results show that the weld appearance can be effectively improved when using laser welding with filler wire. The microhardness and tensile strength of joints are almost the same us those of the base metal when ER AZ31 or ER AZ61 wire is adopted. However, when the filler wire of ER 5356 aluminum alloy is used, the mechanical properties of flints become worse. For ER AZ31 and ER AZ61 filler wires, the microstructure of weld zone slws small dendrite grains. In comparison, for ER 5356 filler wire, the weld shows a structure of snowy dendrites and many intermetallic compounds and eutectic phases distribute in the dendrites. These intermetallic constituents with low melting point increase the tendency of hot crack and result in fiagile joint properties. Therefore, ER AZ31 and ER AZ61 wire are more suitable filler material than ER 5356 for CO2 laser welding of AZ31 magnesium alloys.
文摘Weldability test was carried out on the newly developed fine grain, low sulphur, high strength and high toughness pipeline steel of X80 and its matching SAW wire. Test of maximum hardness in welding heat-affected zone and test of Y groove cracking show that X80 steel features low hardenability and good cracking resistance. The submerged arc welding joint made with the newly developed low carbon and multi-alloyed SAW wire of WGX2 exhibits a little higher strength than the base metal, qualified bending performance, under maximum limitation hardness and good impact toughness, which can completely meet the technical requirement of X80 steel. Despite somewhat coarsening the grain size in welding heat-affected zone is still much finer than that of traditional steels, and the microstructure in weld metal is almost full acicular ferrite. The results show that X80 steel and WGX2 wire are of great weldability.
基金financially supported by the Shanxi Provincial Key Programs for Science and Technology Development (No. 20100321084)Taiyuan Special Foundation for Excellent Talents (No. 20111075)
文摘The arc characteristics of submerged arc welding (SAW) with stainless steel wire were studied by using Analysator Hannover (AH). The tests were carded out under the same preset arc voltage combined with different welding currents. By comparing the probability density distribution (PDD) curves of arc voltage and welding current, the changes were analyzed, the metal transfer mode in SAW was deduced, and the characteristics of a stable arc were summarized. The analysis results show that, with an increase of welding parameters, the short-circuiting peak in the PDD curves of arc voltage decreases gradually until it disappears, and the dominant metal transfer mode changes from flux-wall guided transfer to projected transfer and then to streaming transfer. Moreover, when the PDD curves of arc voltage are both unimodal and generally symmetrical, the greater the peak probability and the smaller the peak span, the more stable the arc becomes.
文摘The metal transfer mode of electron beam welding (EBW) with filler wire was studied experimentally. The spatial position between the electron beam and the filler wire was defined. Basing on the charge coupled device (CCD) visual sensing system, the metal transfer mode of filler wire was investigated. The results showed that there were five transfer modes during EBW process due to different wire feed rates and spatial positions between beam and filler wire, such as short-circuiting mode, molten metal bridge mode, small droplet mode, big droplet mode and mixed mode. By comparing the weld appearance of different transfer modes, the molten metal bridge transfer was proved to be the best transfer mode.
文摘7 xxx welding wire was self-made by spray forming ingots drawn to series welding wires products,and then TIG butt welding test is used for 5 mm thick 7075 high-strength aluminium alloy.After welding,the stress relief+solid-solution aging heat treatment(T6)were performed to joints,and the mechanical properties and microstructure of the joints before and after heat treatment were comparative analyzed.The results show that the properties of the heat-affected zone(HAZ)of the joint before heat treatment decreas,and the joint is softened.The welded joints tensile strength is 271.8 MPa,the elongation is 5.6%,and the average hardness of the weld is 118.4 HV.The second phase particles such asη(Mg Zn2),S(Al2 Cu Mg),Al13 Fe4 are distributed in a network layer,with no apparent element segregation.After heat treatment,the structure of each area of the joint is coarsened,and a small amount of Fe-containing impurity phases are distributed.Theηand S phases are dissolved in the matrix.The hardness of each area of the joint is increased to 155 HV,and the softening zone is disappeared,this leads the joint elongation close to 16.9%.The tensile strength is increased to 511.8 MPa,reaching 94%of the base metal tensile strength.
基金This work was supported by the National Natural Science Foundation of China (Grant No. 51005125 ) and National Basic Research Program of China (Grant No. 2011CB013404).
文摘With preheating wire by resistance heat, laser hot wire welding improves process stability and wire deposition efficiency, which gives broad potential applications in sugracing and narrow gap welding. It is a critical issue to control the temperature of preheated wire in this process. The temperature which is so high that the wire fuses outside molten pool or so low that the wire cannot melt timely in the molten pool, results in poor wire transfer stability and bad weld formation. This paper is purposed to calculate the wire temperature for the prediction of wire transfer behavior under various welding parameters. A heat conduction model is set up. Heat sources of the wire include resistance heat and reflected laser, and the heat source of molten pool is laser. The calculated temperature of wire part outside the molten pool is verified by infrared ratio temperature measurement. The calculated temperature of wire part in the molten pool is verified by measurement of the molten pool size. Analyzing the wire temperature and welding process observed by the high speed video imaging, the temperature criteria of wire transfer behaviors are obtained. Thus, numerical simulation of the wire temperature can be used to predict wire transfer behaviors in laser hot wire welding.
文摘According to the study of the microstructure and properties of X100 pipeline steel, the welding consumable-wire based on Mn-Ni-Mo-B-Ti alloy system was successfully designed and developed. The yield strength of the deposited metal of the developed welding wire was 695 MPa, the tensile strength was 810 MPa, and Charpy impact energy was 92 J at negative 20 ℃ when matching with BSG-SJ101H1 sintered flux. The results of the weldability test for X100 pipeline steel which adopting this developed wire showed that the tensile strength of the weld was 827 MPa, 185 J of Charpy impact energy( -10 ℃ ) , 97% of section of shear and the weld had good strength and toughness matching when the welding speed got to 1.7 m/min. The microstructure and fracture appearance of the weld were analyzed by using metallographic microscope, scanning electron microscope (SEM) and laser confocal microscope, the results indicated that the microstructure was mainly granular bainite in the weld metal, and the fracture was dimple with 200 - 300 μm depth presenting a typical ductile fracture characteristics. The test of welding wire with different content of Ni and Cr element indicated that Ni was better than Cr in improving the strength and toughness of weld metal.
文摘The welding wire feed mechanism is an important component of welding equipment, both reliability and stabilization are the premise that the welding quality can be ensured. The PID is currently adapted to control the welding wire feed mechanism, although the fuzzy PID has advantage of fast response and adaptation, the precision of fuzzy PID is lower. Accordingly, the fuzzy self-adaptive PID controller was proposed through changing fuzzy input variables and output variables based on variable universe, simple furwtion is adopted as scaling factor, the fuzzy PID controller parameters are adjusted to improve the precision and adjustment range. Simulation results show that control effects of fuzzy self-adaptive PID adopted by the welding wire feed mechanism have good adaptive ability and robustness based on variable universe, the welding experiments indicate that the welding quality met the requirements actually.
文摘CO2 laser welding aluminum alloy with filler wire was studied. The results indicate that the problems in CO2 laser welding of Al alloy, such as bad appearance of weld, easily excessive penetration and low strength, can be improved effectively by using laser welding with filler wire, and the maximum tensile strength of weld can reach 94% for the base metal. It also can be found that, the linear energy have great influence on the microstructure and mechanical properties of the joint. As the heat input increases, the cellular fir-tree crystals in the weld zone become sparse and the form of tensile fracture transforms from gliding fracture to brittle fracture.
基金Supported by National Natural Science Foundation of China(Grant No.51171093)
文摘Traditional welding methods are limited in low heat input to workpiece and high welding wire melting rate. Twin-wire indirect arc(TWIA) welding is a new welding method characterized by high melting rate and low heat input. This method uses two wires one connected to the negative electrode and another to the positive electrode of a direct-current(DC) power source. The workpiece is an independent, non-connected unit. A three dimensional finite element model of TWIA is devised. Electric and magnetic fields are calculated and their influence upon TWIA behavior and the welding process is discussed. The results show that with a 100 A welding current, the maximum temperature reached is 17 758 K, arc voltage is 14.646 V while maximum current density was 61 A/mm2 with a maximum Lorene force of 84.5 ~tN. The above mentioned arc parameters near the cathode and anode regions are far higher than those in the arc column region. The Lorene force is the key reason for plasma velocity direction deviated and charged particles flowed in the channel formed by the cathode, anode and upper part of arc column regions. This led to most of the energy being supplied to the polar and upper part of arc column regions. The interaction between electric and magnetic fields is a major determinant in shaping TWIA as well as heat input on the workpiece. This is a first study of electromagnetic characteristics and their influences in the TWIA welding process, and it is significant in both a theoretical and practical sense.
基金supported by the National Natural Science Foundation of China,the Baoshan Iron&Steel Co.,Ltd(No.U1260103)
文摘In this study,the welding thermal cycle curve exhibited two temperature peaks in high heat-input twin-wire separate-pool submerged-arc welding and coarse-grained heat affected zone existed in the welded joint. The inclusions of primary weld metal and coarse-grained heat affected zone of Ce-added SAW should be Al_2O_3,MnO,SiO_2,TiO,Ce_2S_3,CeS,Ce_2O_2S and Ce_2O_3. Under the effect of welding thermal cycle,oxy-sulfides inclusions of Ce,the diameter of which was less than 2. 0 μm,slightly grew larger,but the composition and type of the inclusions didn't change. The microstructure of the large heat input weld metal had acicular ferrite that Ce oxide sulphide particles induced nucleation and proeutectoid ferrite. In the coarse-grained heat affected zone of weld metal,home-position precipitation of acicular ferrite and sympathetic acicular ferrite were both observed. It was supposed that previous crystal cells of acicular ferrite in austenite grain promoted home-position precipitation of acicular ferrite. Meanwhile,sympathetic acicular ferrite tended to nucleate at the primary acicular ferrite grain boundaries,where high dislocation density was located,and grew inside the neighboring carbon-depleted austenitic regions. The granular bainite nucleated in the austenitic zone with high carbon content close to acicular ferrite and sympathetic acicular ferrite.
基金This work was supported by the Natural Science Fund of China,grant number 50375054.
文摘In the three-wire welding system, a welding process consists of the operations of four devices, namely three welding machines and one bogie. The operations need to be synchronized by a numerical coordinate controller ( NCC ). In this paper, we will discuss a tnsk-job-procedure cubic program structure. Under this structure, the devices are synchronized and isolated at the same time. This cubic program structure can also be used as a reference for other multi-device or multi-unit manufacturing processes.
文摘The temperature fields in laser + GMAW-P hybrid welding for different laser-wire distances in quasi-steady state were calculated using an developed combined heat source model, and the influence of laser-wire distance on them was analyzed. The results show tbat, at a low level of arc power, the temperature profiles caused by laser and arc energy respecively cannot couple well when the laser-wire distance reaches 4 mm, a trend of separation between them beginning to take place. In the case of high arc power, both the critical laser-wire distance and HAZ width increase.