Fluxing agents of zinc borate, antimony oxide, galss frit A and glass frit B, with different melting or softening point temperatures, were added into MgO-Al_2O_3-SiO_2/boron phenol formaldehyde resin（MAS/BPF） compos...Fluxing agents of zinc borate, antimony oxide, galss frit A and glass frit B, with different melting or softening point temperatures, were added into MgO-Al_2O_3-SiO_2/boron phenol formaldehyde resin（MAS/BPF） composites to lower the formation temperature of eutectic liquid phase and promote the ceramification of ceramifiable composites. The effects of fluxing agents on the thermogravimetric properties, phase evolution, and microstructure evolution of MAS/BPF composites were characterized by TG-DSC, XRD and SEM analyses. The results reveal that the addition of a fluxing agent highly reduces the decomposition rate of MAS/BPF composites. Fluxing agents lower the formation temperatures of liquid phases of ceramifiable MAS/BPF composites obviously, and then promote the ceramification and densification process. The final residues of composites are ceramic surrounded by large amount of glass phases.展开更多
Monoclinic SrAl_(2)Si_(2)O_(8) ceramics for Sr immobilization were prepared by a liquid-phase sintering method.The sintering temperature,mineral phase composition,microstructure,flexural strength,bulk density,and Sr i...Monoclinic SrAl_(2)Si_(2)O_(8) ceramics for Sr immobilization were prepared by a liquid-phase sintering method.The sintering temperature,mineral phase composition,microstructure,flexural strength,bulk density,and Sr ion leaching characteristics of the SrAl_(2)Si_(2)O_(8) ceramics were investigated.A crystalline monoclinic SrAl_(2)Si_(2)O_(8) phase formed through liquid-phase sintering at 1223 K.The introduction of four flux agents(B_(2)O_(3),CaO·2B_(2)O_(3),SrO·2B_(2)O_(3),and BaO·2B_(2)O_(3))to the SrAl_(2)Si_(2)O_(8) ceramics not only reduced the densification temperature and decreased the volatilization of Sr during high-temperature sintering but also impacted the mechanical properties of the ceramics.Product consistency tests showed that the leaching concentration of Sr ions in the sample with flux agent B_(2)O_(3) was the lowest,whereas that of Sr ions in the sample with flux agent BaO·2B_(2)O_(3) was the highest.These results show that the leaching concentration of Sr ions depends largely on the amorphous phase in the ceramics.Meanwhile,the formation of mineral analog ceramics containing Sr is an important factor to improve Sr immobilization.展开更多
Sr3SiO5:Eu2+ yellow phosphors for white LEDs were synthesized by high temperature solid state reaction method under a reductive atmosphere. The crystalline phases were examined with X-ray diffraction (XRD). Luminescen...Sr3SiO5:Eu2+ yellow phosphors for white LEDs were synthesized by high temperature solid state reaction method under a reductive atmosphere. The crystalline phases were examined with X-ray diffraction (XRD). Luminescence properties were studied, and effects of various fluxing agents BaCl2, MgF2, CaF2 and BaF2 on the emission spectra were also studied. The optimal Eu2+ concentration and flux were determined. Sr3SiO5: Eu2+ was obtained by firing the sample on optimal composition and fabrication process. The sa...展开更多
文摘Fluxing agents of zinc borate, antimony oxide, galss frit A and glass frit B, with different melting or softening point temperatures, were added into MgO-Al_2O_3-SiO_2/boron phenol formaldehyde resin（MAS/BPF） composites to lower the formation temperature of eutectic liquid phase and promote the ceramification of ceramifiable composites. The effects of fluxing agents on the thermogravimetric properties, phase evolution, and microstructure evolution of MAS/BPF composites were characterized by TG-DSC, XRD and SEM analyses. The results reveal that the addition of a fluxing agent highly reduces the decomposition rate of MAS/BPF composites. Fluxing agents lower the formation temperatures of liquid phases of ceramifiable MAS/BPF composites obviously, and then promote the ceramification and densification process. The final residues of composites are ceramic surrounded by large amount of glass phases.
基金This work was financially supported by the National Natural Science Foundation of China(No.11605116).
文摘Monoclinic SrAl_(2)Si_(2)O_(8) ceramics for Sr immobilization were prepared by a liquid-phase sintering method.The sintering temperature,mineral phase composition,microstructure,flexural strength,bulk density,and Sr ion leaching characteristics of the SrAl_(2)Si_(2)O_(8) ceramics were investigated.A crystalline monoclinic SrAl_(2)Si_(2)O_(8) phase formed through liquid-phase sintering at 1223 K.The introduction of four flux agents(B_(2)O_(3),CaO·2B_(2)O_(3),SrO·2B_(2)O_(3),and BaO·2B_(2)O_(3))to the SrAl_(2)Si_(2)O_(8) ceramics not only reduced the densification temperature and decreased the volatilization of Sr during high-temperature sintering but also impacted the mechanical properties of the ceramics.Product consistency tests showed that the leaching concentration of Sr ions in the sample with flux agent B_(2)O_(3) was the lowest,whereas that of Sr ions in the sample with flux agent BaO·2B_(2)O_(3) was the highest.These results show that the leaching concentration of Sr ions depends largely on the amorphous phase in the ceramics.Meanwhile,the formation of mineral analog ceramics containing Sr is an important factor to improve Sr immobilization.
基金Project Supported by the Jilin Province Science and Technology Development Projects (20090348 and 20080511)
文摘Sr3SiO5:Eu2+ yellow phosphors for white LEDs were synthesized by high temperature solid state reaction method under a reductive atmosphere. The crystalline phases were examined with X-ray diffraction (XRD). Luminescence properties were studied, and effects of various fluxing agents BaCl2, MgF2, CaF2 and BaF2 on the emission spectra were also studied. The optimal Eu2+ concentration and flux were determined. Sr3SiO5: Eu2+ was obtained by firing the sample on optimal composition and fabrication process. The sa...