In this paper, a high calcium high sulfate ash as the main material, adding fly ash, lime, cement, gypsum and some modifiers to prepare autoclaved aerated concrete. The products complies with the technical requirement...In this paper, a high calcium high sulfate ash as the main material, adding fly ash, lime, cement, gypsum and some modifiers to prepare autoclaved aerated concrete. The products complies with the technical requirements of GB/T11968-2006. This paper also studies the influence of the physical methods and water ratio on autoclaved aerated concrete by high calcium high sulfate ash aerated concrete. The best ratio of water and Grinding time were found in practice study.展开更多
The associated MgO in limestone is believed to affect the volume stability of cementitious materials at room tem-perature,which limits the utilization of low grade limestone.In this study,MgO was used as an alkali act...The associated MgO in limestone is believed to affect the volume stability of cementitious materials at room tem-perature,which limits the utilization of low grade limestone.In this study,MgO was used as an alkali activator instead of partial CaO to prepare the aerated concrete under hydrother mal conditions.The expansion process was studied to evaluate the influence of the raw materials on the gas forming stability of the slurry.The pore structure(porosity,pore size and its distribution)was analyzed by the image method.The physic mechanical properties(density,strength,thermal properties)of concrete with the addition of MgO were comprehensively investigated.Besides,the mineral compositions and morphology of the hydration products were analyzed to demonstrate the infuence mechanism of MgO on the mechanical properties.Experimental results show that the final expansion rate of the slurry decreases with MgO content.A reasonable MgO content,ie,MgO/(MgO+CaO)<20%,con-tributes to improve the compressive strength,attributing to an increased reaction rate to C-S-H gel and tobermor-ite.The addition of MgO causes the thermal conductivity and specific heat to increase.The pore structure is mainly related to the amount of air entraining agent.This study has a significance for the further utilization of magnesium-rich carbonates in the autoclaved building products.展开更多
In active response to the national requirements of promoting green building materials and developing prefabricated buildings,it is necessary to continuously optimize and reasonably employ relevant technologies.Autocla...In active response to the national requirements of promoting green building materials and developing prefabricated buildings,it is necessary to continuously optimize and reasonably employ relevant technologies.Autoclaved aerated concrete block prefabricated multi-storey building technology is a new technology,which will not only effectively realize green environmental protection in construction engineering,but also promote the further development of prefabricated buildings.Therefore,this paper analyzes the autoclaved aerated concrete block prefabricated multi-storey building technology for future references.展开更多
文摘In this paper, a high calcium high sulfate ash as the main material, adding fly ash, lime, cement, gypsum and some modifiers to prepare autoclaved aerated concrete. The products complies with the technical requirements of GB/T11968-2006. This paper also studies the influence of the physical methods and water ratio on autoclaved aerated concrete by high calcium high sulfate ash aerated concrete. The best ratio of water and Grinding time were found in practice study.
基金This work is financially supported by National Natural Science Foundation of China(52002245)Natural Science Foundation of Guangdong(Nos.2019A1515012172,2021A1515010671)+3 种基金Key Platform and Major Scientific Research Project of Guangdong(No.2018KQNCX232)Science and Technology Plan Project of Shaoguan(Nos.2019sn057,210726194533404)Scientific Research Projects of Shaoguan University(SY2020KJ12,SY2020KJ02,408-99000623,408-230083990402)Innovation and Entrepreneurship Program for College Students(S202110576030).
文摘The associated MgO in limestone is believed to affect the volume stability of cementitious materials at room tem-perature,which limits the utilization of low grade limestone.In this study,MgO was used as an alkali activator instead of partial CaO to prepare the aerated concrete under hydrother mal conditions.The expansion process was studied to evaluate the influence of the raw materials on the gas forming stability of the slurry.The pore structure(porosity,pore size and its distribution)was analyzed by the image method.The physic mechanical properties(density,strength,thermal properties)of concrete with the addition of MgO were comprehensively investigated.Besides,the mineral compositions and morphology of the hydration products were analyzed to demonstrate the infuence mechanism of MgO on the mechanical properties.Experimental results show that the final expansion rate of the slurry decreases with MgO content.A reasonable MgO content,ie,MgO/(MgO+CaO)<20%,con-tributes to improve the compressive strength,attributing to an increased reaction rate to C-S-H gel and tobermor-ite.The addition of MgO causes the thermal conductivity and specific heat to increase.The pore structure is mainly related to the amount of air entraining agent.This study has a significance for the further utilization of magnesium-rich carbonates in the autoclaved building products.
文摘In active response to the national requirements of promoting green building materials and developing prefabricated buildings,it is necessary to continuously optimize and reasonably employ relevant technologies.Autoclaved aerated concrete block prefabricated multi-storey building technology is a new technology,which will not only effectively realize green environmental protection in construction engineering,but also promote the further development of prefabricated buildings.Therefore,this paper analyzes the autoclaved aerated concrete block prefabricated multi-storey building technology for future references.