Thaumasite form of sulfate attack（TSA）is a major concern in evaluating durability of concrete structures subjected to sulfate and carbonate ions.By means of Fourier transform infrared spectroscopy （FT-IR）,X-ray di...Thaumasite form of sulfate attack（TSA）is a major concern in evaluating durability of concrete structures subjected to sulfate and carbonate ions.By means of Fourier transform infrared spectroscopy （FT-IR）,X-ray diffraction（XRD）,scanning electron microscopy（SEM）,and energy dispersive spectrum（EDS） as well as Raman spectra of erosion substances,effect of fly ash on TSA resistance of Portland cement-based material were investigated.Immersed in magnesium sulfate solution with 33 800 ppm mass concentration of SO 4 2-at 5±2℃for 15 weeks,ratio of compressive strength loss decreased as binder replacement ratio of fly ash increased.Furthermore,when binder replacement of fly ash was 60%,compressive strength increased.When thaumasite came into being in samples with 0,15%binder replacement ratio of fly ash,ettringite and gypsum appeared in those with 30%,45%,60%binder replacement ratio of fly ash.Results mentioned above showed that fly ash can restrain formation of thaumasite and improve TSA resistance of Portland cement-based material sufficiently.展开更多
基金Supported by the Scientific Research Foundation for the Talents of Hohai University(No.20090603)the Fundamental Research Funds for the Central Universities(No.2010B25514)the National Natural Science Foundation of China(No.50979032)
文摘Thaumasite form of sulfate attack（TSA）is a major concern in evaluating durability of concrete structures subjected to sulfate and carbonate ions.By means of Fourier transform infrared spectroscopy （FT-IR）,X-ray diffraction（XRD）,scanning electron microscopy（SEM）,and energy dispersive spectrum（EDS） as well as Raman spectra of erosion substances,effect of fly ash on TSA resistance of Portland cement-based material were investigated.Immersed in magnesium sulfate solution with 33 800 ppm mass concentration of SO 4 2-at 5±2℃for 15 weeks,ratio of compressive strength loss decreased as binder replacement ratio of fly ash increased.Furthermore,when binder replacement of fly ash was 60%,compressive strength increased.When thaumasite came into being in samples with 0,15%binder replacement ratio of fly ash,ettringite and gypsum appeared in those with 30%,45%,60%binder replacement ratio of fly ash.Results mentioned above showed that fly ash can restrain formation of thaumasite and improve TSA resistance of Portland cement-based material sufficiently.